Basic Info.
Material
TC4 Titanium Alloy
Surface Treatment
Spray Coating
Standards
Astmb861 B862 B338 ASME Sb861 Sb862 Sb338
Titanium Plate Grade
Grade 5 Uns R50600
Application
Industrial, Medical
Grade
Gr5 Grade5 6-4 Ti6al4V
Transport Package
Wooden Box
Specification
φ 6.35mm-φ 1219mm
Product Description
Product Parameters
| Ti-6Al-4V Grade 5 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 5 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 5-Ti-6Al4V- TC4- USN 56400 |
| Grade 5 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 5 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ6.0mm to φ1219mm |
| Grade 5 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 5 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form Ti-6Al-4V | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TC4 1.37165 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 5 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 5 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 5 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 5 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 5 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 5 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 5 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 5 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 5 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Detailed Photos
Applications and standards
Grade 5 titanium tubes are widely used in the following industries under extreme corrosive conditions:
- Chemical processing parts, military industry, aerospace, chemical energy, marine engineering, oil and gas industry, rockets and missiles, military armor, ships and vessels, industrial machinery, power industry, paper and pulp industry, pharmaceutical and food processing equipment, etc.
- Specifications: ASTM B861, B862, B338 / ASME SB861, SB862, SB338
- Standards: ASTM, GB, GJB, ASME and API
Quality, delivery, inspection
Daxun performs several quality assurance tests, these tests include flattening test, flaring test, ultrasonic flaw detection test, pitting and resistance test, mechanical test, hardness test, material positive identification, expansion test, etc. All these tests ensure that the Grade 1 Titanium Welded Pipe and Grade 1 Titanium Seamless Pipe materials are suitable for the required application. During the production process, we measure the diameter, thickness and surface of the products. Our standard delivery time is 5-7 days and the delivery time for special size products is 15-20 days.
- Our delivery time is strictly in accordance with the contract.
- Support customer third-party agencies to go to the factory for inspection
- Support free samples for customer testing
- Support on-site or video factory inspection
Grade 5 Titanium Tube Features
Ti-6Al4V Grade 5 Titanium Alloy Tube is the most commercially available of all Titanium alloys. It combines high strength and toughness. Grade 5 Titanium alloy has good welding and processing characteristics:
- High Strength Titanium Alloy
- Heat Treatable
- Good Ductility
- Good Machinability
- Good Weldability
We stock and sell Grade 5 Titanium Alloy Seamless Tubes, Forged Seamless Tubes, Welded Tubes, etc.
Daxun Alloy, as a leading titanium alloy tube manufacturer and supplier in China, provides high-quality Grade 5 titanium pipes to the world and has been well received by many projects.
Ti 6Al-4V (Grade 5 Titanium) is the most widely used of all titanium alloy tubes, accounting for more than 50% of the total titanium usage. It is usually used in the annealed state and has an operating temperature of up to 400°C (750°F). Ti 6Al/4V is welded with matching or ELI filler wire. Ti 6Al/4V has significantly higher strength than commercial pure titanium tubes, while having better stiffness and thermal properties (excluding thermal conductivity), and the thermal conductivity of Grade 5 titanium tube is about 60% lower than CP titanium. Among its many advantages, it can be heat treated. Thus, more ideal strength and performance are obtained. The advantages of using Grade 5 titanium seamless tubes include not only strong formability and low density, but also excellent corrosion resistance.
This grade is a perfect combination of strength, corrosion resistance, weldability and machinability. Therefore, it is widely used, such as in military aircraft or aviation industry, rocket parts, precision-guided components, armor parts, ship equipment, military vacuum equipment and other parts. The close version of 6-4, 6-4ELI, is also used in surgical implants. Typically, it is used in applications up to 400°C to improve ductility and toughness in cold working conditions. It also has excellent specific strength. It is usually provided in the annealed state and is easy to heat treat to increase strength for a variety of applications. As a general-purpose titanium alloy, Ti 6Al-4V titanium seamless tube has a wide range of ideal properties at temperatures around -210°C - 400°C. Grade 5 titanium alloy tube is the most commercialized of all titanium alloys. It combines high strength and toughness. Grade 5 titanium alloy tube has good welding and processing characteristics.
Titanium Alloy Grade 5 Seamless Pipe, Titanium Gr 5 High Pressure Pipe, ASTM B338 Titanium Alloy Gr 5 Seamless Pipe, Titanium Gr 5 Thick Wall Pipe. China Titanium Grade 5 ERW Pipe Supplier. Titanium Alloy Gr 5 Pipe, Titanium Gr 5 Electropolished Pipe, Anti-corrosion Titanium Pipe, Titanium Tube, ASTM B338 Titanium Grade 5 Welded Pipe, ASTM B861 / ASME SB861 Titanium Grade 5 Seamless Pipe China Titanium Gr-5 Seamless Pipe Manufacturer. Ti-6al-4v Pipe Dealer, ASTM B338 Titanium Grade 5 Pipe, Titanium Gr 5 Bright Annealed Pipe, Ti-6al-4v Pipe, Gr 5 Pipe, Titanium Gr 5 Pipe, Titanium WERKSTOFF NR 3.7165 Pipe
Packaging & Shipping
Company Profile
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
These tubes are supplied in the form of hot-rolled or hot-extruded, straightened, machined inside and outside diameters, and surface polished. Titanium tubes are available in heat-treated or non-heat-treated forms. Our company has 100% ultrasonic flaw detection capabilities.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: OD 19mm to 325mm, wall thickness 9mm to 30mm, length up to 5000mm (to be agreed on a case-by-case basis between the manufacturer and the customer); - Hot-extruded Titanium Tubes: OD 50mm to 160mm, wall thickness 7mm to 35mm, length up to 3000 (to be agreed on a case-by-case basis between the manufacturer and the customer).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are supplied in the form of heat-treated, surface-etched, hydrostatically tested, or ultrasonically tested, depending on the requirements of the manufacturing specifications. Tubes Supplied:- OD 6mm to 89mm, wall thickness 0.5mm to 11mm, length up to 6000mm (to be agreed on a case-by-case basis between the manufacturer and the customer).
Titanium Welded Pipes
DaXun manufactures and supplies titanium pipes with diameters from 100 mm. 12.7 to 38.1 mm (0.47 in to 1.5 in), wall thickness from 0.4 to 1.65 mm (0.016 in to 0.065 in, depending on diameter), lengths up to 25000 mm, electrical Gr1, Gr2 and Gr12 titanium alloy pipes for engineering and chemical industries. Titanium welded pipes are made from flat rolled raw material (kelp) by automatic tungsten inert gas (argon) welding on electric pipe welders and heat treated on the mill line. Finished titanium welded pipes undergo mechanical testing, geometrical measurements, 100% ultrasonic and eddy current testing, pneumatic or hydrostatic testing; pipes are packed as per customer specifications. Manufacturing processes and inspection test equipment ensure thin wall welded pipes comply with ASTM B 338, ASME SB 338 standards.
| CP GR1 Titanium tube PHYSICAL PROPERTIES |
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | |
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | |
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset |
| | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | |
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | |
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | |
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| | 0.8 | 0.8 | Ti sliding on Ti; 40 m/min |
| CP GR2 Titanium tube PHYSICAL PROPERTIES |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES |
| Physical Properties | Metric | English | Comments |
| | | | |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties |
| | | | |
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties |
| | | | |
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties |
| | | | |
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
Certifications
Ti-6Al-4V- Grade 5 Titanium tube
- Titanium Alloy-(UNS R56400)
INTRODUCTION
- DAXUN Ti-6Al-4V, Grade 5 Alloy Tube (UNS R56400) is the most popular titanium alloy. It is a duplex alpha+beta titanium alloy that uses aluminium as an alpha stabiliser and vanadium as a beta stabiliser. This high-strength alloy can be employed at cryogenic temperatures of around 800°F (427°C). ATI Ti-6Al-4V, Grade 5 alloy is used in annealing, solution treatment, and ageing. Compressor blades, discs, and rings for jet engines; fuselage and space capsule components; pressure containers; rocket engine cases; helicopter rotor hubs; fasteners; and crucial forgings with a high strength-to-weight ratio.
- The alloy is initially melted using vacuum arc (VAR), electron beam (EB) or plasma arc hearth melting (PAM). Remelting is achieved in one or two vacuum arc steps.
SPECIFICATIONS
•ASTE B338 - Tubes Titanium tubes standard heat treatable
• AMS 4928 - Forgings and forging stock (annealed)
• AMS 4965 - Forgings (solution treated and aged)
• AMS 4967 - Forgings (annealed, heat treatable)
PHYSICAL PROPERTIES
- Melting Range: 2,800-3,000°F (1,538 - 1,649°C)
- Density: 0.160 lbs/cu. in.; 4.47 gm/cc
- Beta Transus Temperature: 1830°F (± 25°); 999°C (± 14°)
HEAT TREATMENT
- Annealing at 1,700-1,900°F (927 - 1,038°C) is done where high hardness, tensile and fatigue strength are desired.
- DAXUN 6-4™, Grade 5 Alloy can be heat treated in several ways.
- 1. Anneal: 1,275 -1,400°F; (691 - 760°C), ½ to 2 hours, air or furnace cool
- 2. Stress Relief Anneal: 1,000 -1,200°F; (538 - 649°C), 1 to 8 hours, air or furnace cool
- 3. Solution Heat Treatment: 1,675 -1,750°F; (913 - 954°C), 1 hour, water quench
- 4. Aging Treatment: 975 -1,025°F; (524 - 552°C), 4 to 8 hours - air cool
- The very best of properties In the solution treated and aged condition, small cross sections are obtained that are rapidly
quenched. Larger sections sizes and/or a quench delay may cause properties to be lower than the optimum values.
HARDNESS
Typical hardness in the annealed condition is Rockwell C 30-34, and about Rockwell C 35-39 in the solution and aged condition.
FORGEABILITY/ FORMABILITY
- DAXUN Ti-6Al-4V, Grade 5 alloy tubes are forged at 1,750°F (954°C), with an end forging temperature of 1,450°F (788°C). For optimal results, a reduction of at least 35% is recommended.
- DAXUN Ti-6Al-4V, Grade 5 alloy is difficult to form at room temperature, even when annealed. As a result, harsh forming operations like bending or stretching can be conducted on annealed material at temperatures as high as 1,200°F (649°C) without altering its mechanical qualities. Creep forming can be used for hot sizing or forming at temperatures ranging from 1,000 to 1,200°F (538 to 649°C).
MACHINABILITY
- DAXUN Ti-6Al-4V, Grade 5 alloy can be machined using practices for austenitic stainless steels with slow speeds, heavy feeds, rigid
tooling, and large amounts of non-chlorinated cutting fluid.
WELDABILITY
- DAXUN Ti-6Al-4V Grade 5 Alloy Titanium Tube is easily welded in the annealed or solution and partially aged form, with ageing.
- done during the post-weld heat treatment. Precautions must be made to avoid contamination by oxygen, nitrogen, and hydrogen. Fusion welding can be performed in an inert gas-filled chamber or with an inert gas tail shield applied to the molten metal and nearby hot zone. Spot welding, seam welding, and flash welding can all be performed without the use of a protective environment.
SPECIAL PRECAUTIONS
- DAXUN Ti-6Al-4V, Grade 5 alloy may be contaminated with hydrogen as a result of incorrect pickling, as well as the absorption of oxygen, nitrogen, and carbon during forging, heat treatment, brazing, and so on. This contamination may reduce ductility, compromising notch sensitivity and forming properties.
Ti-6Al-4V Titanium Pipe- Grade 5 Titanium Tube
Titanium Alloy - (UNS R56400)
Introduction
DAXUN Ti-6Al-4V Titanium Tube, Grade 5 (UNS R56400) is the most popular titanium alloy. It is a duplex alpha+beta titanium alloy using aluminum as the alpha stabilizer and vanadium as the beta stabilizer. This high-strength alloy can be used at low temperatures of about 800°F (427°C). ATI Ti-6Al-4V, Grade 5 alloy is used for annealing, solution treating, and aging. Compressor blades, disks, and rings for jet engines; fuselage and space capsule components; pressure vessels; rocket engine cases; helicopter rotor hubs; fasteners; and critical forgings with a high strength-to-weight ratio.
The alloy is initially melted using vacuum arc (VAR), electron beam (EB), or plasma arc hearth melting (PAM). Remelting is achieved in one or two vacuum arc steps.
Specifications
•ASTE B338 - Standard Heat Treatable Titanium Tube
• AMS 4928 - Forgings and Forging Stock (Annealed)
• AMS 4965 - Forgings (Solution Treated and Aged)
• AMS 4967 - Forgings (Annealed, Heat Treatable)
Physical Properties
Ti-6Al-4V Titanium Tube Melting Range: 2,800-3,000°F (1,538 - 1,649°C)
Density: 0.160 lb/in3; 4.47 g/cm3
Beta Transus Temperature: 1830°F (± 25°); 999°C (± 14°)
Heat Treatment
Annealed at 1,700-1,900°F (927 - 1,038°C) when high hardness, tensile strength, and fatigue strength are required.
DAXUN 6-4 Grade 5 Titanium Tube can be heat treated in a variety of ways.
1. Annealing: 1,275 -1,400°F; (691 - 760°C), ½ to 2 hours, air or furnace cool
2. Stress Relief Annealing: 1,000 -1,200°F; (538 - 649°C), 1 to 8 hours, air or furnace cool
3. Solution Heat Treating: 1,675 -1,750°F; (913 - 954°C), 1 hour, water quench
4. Aging: 975 -1,025°F; (524 - 552°C), 4 to 8 hours - air cool
Optimum Properties
Small cross sections with rapid quenching are obtained in the solution treated and aged condition. Larger cross-section sizes and/or delayed quenching may result in less than optimal properties.
Hardness
Typical hardness in the annealed condition is Rockwell C 30-34 and approximately Rockwell C 35-39 in the solution and aged condition.
Forgeability/Formability
DAXUN Ti-6Al-4V Titanium Tube, Grade 5 Titanium Tube is forged at 1,750°F (954°C) with a final forging temperature of 1,450°F (788°C). A reduction of at least 35% is recommended for best results.
DAXUN Ti-6Al-4V Titanium Tube, Grade 5 Titanium Tube is difficult to form at room temperature, even when annealed. Therefore, severe forming operations such as bending or stretching can be performed on the annealed material at temperatures up to 1,200°F (649°C) without changing its mechanical properties. Creep forming can be used for hot sizing or forming at temperatures ranging from 1,000 to 1,200°F (538 to 649°C).
Machinability
DAXUN Ti-6Al-4V Titanium Tube, Grade 5 Titanium Tube can be machined using machining methods for austenitic stainless steels, with slow speeds, high feeds, good tool rigidity, and the use of large amounts of non-chlorinated cutting fluids.
Weldability
DAXUN Ti-6Al-4V Titanium Tube Grade 5 Titanium Tube is readily weldable in the annealed or solution and partially aged conditions, with aging
accomplished during post-weld heat treatment. Precautions must be taken to avoid contamination with oxygen, nitrogen, and hydrogen. Fusion welding may be performed in an inert gas-filled chamber or with the use of an inert gas tail shield over the molten metal and nearby hot zones. Spot welding, seam welding, and flash welding may all be performed without the use of a protective atmosphere.
Special Considerations
DAXUN Ti-6Al-4V Titanium Tube, Grade 5 Titanium Tube may be contaminated with hydrogen from improper pickling and from the absorption of oxygen, nitrogen, and carbon during forging, heat treating, brazing, etc. This contamination may reduce ductility and impair notch sensitivity and formability.
FAQ
Q1: What products can you offer?
A: We can offer you general steel types like 310S, 316L,304.304L.201,904L, 316H, 316,316L 300and
400 series, and duplex stainless steel like 2205, 2304,2101,2507,etc. 904L, 800H, 600H high-nickel alloy.
Q2. Can you produce the products according to my own drawings?
Yes, we can produce the products according to your drawings that will be most satisfy you.
Q3. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q4. Can I request to change the form of packaging and transportation?
Yes, We can change the form of the packaging and transportation according to your request,
but you have to bear their own costs incurred during this period and the spreads.
Q5. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q6. How long is the delivery time?
A: 7~20 working days after confirming the payment.
If the order is urgent, we will push our workshop finish in advance.
Q7. What is your Payment?
A: 100% T/T advance, Western Union (For Small Order)
B: 30% T/T and balance 70% before the shipment
C: 100% Irrevocable LC at sight (For Big Order)
Q8: Can you make DDQ ( Deep Drawing Quality)?
A: Yes, we can. Our material can be used for stainless steel pots, stainless steel sinks, stainless steel bowls etc. U can tell us your usage, and we will adjust the mechanical propertise to meet your requirement.
Q9: How to get a sample?
A: FREE samples are available for your checking and testing.If you require for a small piece,we can afford courier cost,it depends.
Q10:Which country have you exported to?
A:Until now,we have exported stainless steel material to following countries: Vietnam,Thailand,Turkey,Russia,Maroc,Korea,India,Pakistan,UAE,Ukraine and so on.
Q11: How to visit your company?
A:By flight to Guangzhou Baiyun International airport,then we will pick you up.
Address:
B108, No. 32-1, Chengnan Road, Xinwu District, Wuxi, Jiangsu, China
Business Type:
Manufacturer/Factory, Trading Company
Business Range:
Metallurgy, Mineral & Energy
Management System Certification:
ISO 9001, ISO 9000, ISO 14001, ISO 14000, ISO 20000, OHSAS/ OHSMS 18001, IATF16949, HSE, ISO 14064, QC 080000, GMP, BSCI, BRC, SA 8000, QHSE, HACCP, ISO 13485, EICC, ANSI/ESD, SEDEX, ISO 22000, AIB, WRAP, GAP, ASME, ISO 29001, HQE, IFS
Company Introduction:
Founded in 2003, Daxun Alloy is a leading global metal material manufacturer. Headquartered in Wuxi, China, the company has multiple production bases and sales offices around the world. Daxun Alloy focuses on the development, production and sales of various stainless steels, titanium alloys, high-temperature alloys, etc. For general industry, construction, aerospace, energy, chemical industry, medical and other fields.
China, Daxun Metal Group is a global vertically integrated metal material manufacturer and stockist. Daxun can provide finished products and customized full-process services and professional technical services. Currently, the group has 600 employees and covers a total area of 130, 000 square meters. Daxun has a standing inventory of 50, 000 tons of stainless steel, 5, 000 tons of nickel-based alloys, and 2, 000 tons of pure titanium and titanium alloys. The main product forms are metal plates, metal coils, metal pipes, and metal bars. The metal materials produced by Daxun are market leaders for marine, energy, military, general industrial and aerospace applications. In addition, the company also produces seamless pipes, plates, forgings and other metal materials for power generation and oil and gas applications; Commercial and military alloy products; And metal alloys and other metal products for the forging industry.