| Customization: | Available |
|---|---|
| Type: | Titanium Bars |
| Application: | Industrial, Medical, Chemical Industry, Aviation |
|
Still deciding? Get samples of US$ 1/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Material | Titanium rod and bar Grade 5 Ti6Al4V |
| Standard | ASTM B348, ASTM SB348, AMS 4921, AMS 4902 |
| Dimensions | EN, ASTM, JIS, ASME, BS, AISI |
| Diameter Range | 0.125″ - 14″ (3.175mm - 355.6mm), custom |
| Length Range | Up to 240″ (6096mm), custom |
| Finish | Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black |
| Surface Finish | Cold drawn, Centerless Ground, Polished, Or Rough Turned, Black, NO.4 Finish, BA Finish, Matt Finish, etc. |
| Condition | Hardened & tempered, annealed |
| Tolerance | Diameter tolerance: +/- 0.005″ (0.127mm), length tolerance: +/- 0.125″ (3.175mm) |
| Form | Titanium square bars, titanium ingots, titanium round bars, rectangular titanium bars, triangular titanium bars, forged titanium bars, titanium hexagonal bars, etc. |
Grade 5 Titanium Alloy Rod (Titanium Aluminum Vanadium Alloy) is the most widely used α-β Titanium Alloy, accounting for 50% of global titanium alloy consumption. This grade is fully heat treatable and operable at temperatures up to 400°C. With a low density of 4.43 kg/dm³, it offers exceptional corrosion resistance and superior mechanical strength. It boasts high tensile strength at room temperature and excellent creep resistance up to 300°C, along with strong *** and fatigue resistance. The age-hardening quality makes 6AL-4V Titanium Alloy Rods ideal for fasteners and components in demanding environments. Their high machinability and weldability support a broad range of industrial applications.
DAXUN® Ti Grade 5 is a Titanium Alloy Bar (6AL-4V) Featuring:
Daxun manufactures high-performance titanium bars and can accommodate custom agreements:
Daxun conducts rigorous quality assurance tests, including mechanical tests (area tensile), chemical analysis, PMI testing, micro and macro assessments, intergranular corrosion testing, ultrasonic flaw detection, pitting and resistance tests, hardness measurements, expansion tests, and surface inspection. These tests ensure that Grade 2 Titanium Rods and Grade 2 Titanium Round Bars meet application requirements. Diameters, thicknesses, and surfaces are measured throughout the production process.
The Chemical Composition of (Ti 6AL-4V) Grade 5 Titanium Rods
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
The Chemical Composition of Grade 2 Titanium Rods
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
The Mechanical Properties of Grade 2 Titanium Rods
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
Daxun Alloys boasts an extensive inventory of Grade 1, Grade 2, and Grade 5 Titanium Rods, available in a variety of diameters to suit your project needs-from general industrial applications to demanding military aerospace requirements. Our Titanium Alloy Rods span sizes from 1mm to 300mm in diameter, with custom orders welcomed for larger dimensions. All Titanium Rods adhere to the highest standards, certified to ASTM B348 and ASTM B381. Contact Daxun for premium quality pure titanium and titanium alloy rods. Our expert team is ready to assist with any inquiries and provide quotations tailored to your specifications.
Daxun operates a fully integrated technology cycle, from raw material processing to the production of finished products with advanced mechanical processing. Our bar products are stocked across an extensive service center network, ensuring swift, off-the-shelf delivery of standard sizes and alloys. We also specialize in manufacturing custom sizes and offer stocking programs designed for rapid turnaround, catering to just-in-time requirements for orders below the mill minimum. For efficient and reliable titanium solutions, trust Daxun's expertise.
| CP GR1 Titanium rods PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium rods PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium rods PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
Daxun Jiangsu Daxun Alloy Co., Ltd. produces highly competitive, high-precision Grade 1 titanium bars in our state-of-the-art production facilities in China. With an excellent surface finish, precise tolerance, straightness, and superior material quality, we provide you with technological leadership and consistent production processes. These advantages apply across a wide range of diameters and materials. Additionally, our comprehensive stocking program at our service center ensures just-in-time delivery.
We produce bars according to your specific requirements.
With excellent surface and straightness, perfect roundness, and the tightest diameter tolerances (according to ISO 286-2 up to h5). Available in straightened, ground, polished conditions.
Sawing
Band saws (up to Ø510 mm)
Bench band saws (up to 6,000 x 3,000 x 400 mm)
High-performance sawing machines for precise cuts
Single or double-sided
Chamfer 90° (45°)
Point 60° (30°)
Flat end
Centered
ASTM American Society for Testing and Materials Standards
AMS American Aerospace Materials Standards
NACE American Association of Corrosion Engineers International Standards
ASME American Society of Mechanical Engineers Standards
GB Chinese National Standards
GJB Chinese National Military Standards
ISO International Standards
DIN German Standards
EN European Standards
API American Petroleum Institute Standards
Non-destructive testing > 100% testing
Testing Methods
Eddy current testing/eddy current *** testing
Defect-free surface (level 4)
Flat bottom hole diameter 0.7 mm and 0.4 mm
Blind area can be cut off according to fixed length >Test to the end of the bar
Full diameter ultrasonic testing
When placing purchase orders, please specify the quantity, grade, type or category, API5L reference, thickness, width, length, and any other requirements pertaining to chemical composition, mechanical properties, heat treatment, additional testing, manufacturing process, surface coating, or end finish. Reach out to Daxun for prompt email responses.
Grade 5 Titanium Rod
Daxun boasts a cutting-edge production facility in China, producing highly competitive and precise Grade 5 titanium bars. Our products excel in surface quality, tolerance, straightness, and material integrity, ensuring technological leadership and consistent production. Our extensive stock program offers just-in-time delivery across a broad range of diameters and materials.
AMS 4928 - Bars, Forgings, and Forging Stock (Annealed)
AMS 4965 - Bars, Forgings (Solution treated and aged)
AMS 4967 - Bars, Forgings (Annealed, Heat Treatable)
In the solution treated and aged condition, quick quenching of small sections results in optimal properties. Larger sections or delayed quenching may result in suboptimal properties.
In the annealed condition, the typical hardness is Rockwell C 30-34, while in the solution and aged condition, it ranges from Rockwell C 35-39.
Our Ti-6Al-4V, Grade 5 alloy bar is precision-engineered to be machined using austenitic stainless-steel methods. It requires slow machining speeds, high feeds, and rigid tools, complemented by generous use of non-chlorinated cutting fluids for unparalleled efficiency.
The Ti-6Al-4V, Grade 5 alloy rod is highly weldable, whether in the annealed state or in the solution and partially aged condition. Aging is seamlessly achieved during post-weld heat treatment. To avoid contamination from oxygen, nitrogen, and hydrogen, fusion welding should be done in an inert gas-filled chamber or with inert gas shielding. Spot, seam, and flash welding can be executed without a protective atmosphere.
When working with the Ti-6Al-4V, Grade 5 titanium alloy rod, caution is essential to prevent contamination. Improper pickling can lead to hydrogen contamination, while forging, heat treating, and brazing may introduce oxygen, nitrogen, and carbon. Such contaminants can reduce ductility and adversely impact notch sensitivity and forming characteristics.
We craft bars tailored precisely to your specifications.
Experience unparalleled surface quality and straightness, with perfect roundness and the tightest diameter tolerances (per ISO 286-2 up to h5). Available in straightened, ground, and polished conditions.
Sawing
Band saws (up to Ø510 mm)
Bench band saws (up to 6,000 x 3,000 x 400 mm)
High-performance sawing machines for precise cuts
Single or double-sided
Chamfer 90° (45°)
Point 60° (30°)
Flat end
Centered
ASTM - American Society for Testing and Materials Standards
AMS - American Aerospace Materials Standards
NACE: Rigorous Standards by the American Association of Corrosion Engineers International
ASME: Premier Standards by the American Society of Mechanical Engineers
GB: Comprehensive Chinese National Standards
GJB: Specialized Chinese National Military Standards
ISO: Widely Accepted International Standards
DIN: Renowned German Standards
EN: Essential European Standards
API: Trusted American Petroleum Institute Standards
Non-Destructive Testing: Ensuring Over 100% Thorough Examination
Various Testing Methods
Eddy Current Testing: Precision in Eddy Current *** Detection
Surface Quality: Guaranteed Defect-Free (Level 4)
Precision Testing: Flat Bottom Hole Diameters at 0.7 mm and 0.4 mm
Cutting Edge Analysis: Blind Areas Can Be Cut Off According to Fixed Length > Comprehensive Testing to the End of the Bar
Ultrasonic Testing: Full Diameter Examination
To place orders, include quantity, grade, type or category, API5L reference, thickness, width, length, and any relevant attachments or specific requirements related to chemical composition, mechanical properties, heat treatment, additional testing, manufacturing process, surface coating, or end finish. Contact Daxun now for prompt email responses.
Titanium should not be used with strong reducing acids, fluoride solutions, pure oxygen, or anhydrous ***.
Table 1 details the general corrosion rates for Grade 2 Titanium across various media. Commercially Pure (CP) Titanium demonstrates excellent corrosion resistance in numerous environments, including:
CP Titanium offers superior resistance to crevice corrosion in salt solutions compared to stainless steels. It maintains resilience up to 80°C (176°F) regardless of pH, even under super chlorinated conditions.
Grade 2 Titanium boasts exceptional resistance to stress corrosion (SCC) cracking in hot chloride solutions and remains immune to SCC in seawater.
Titanium excels in erosion resistance within flowing environments.
Remarkably resilient, the material withstands seawater velocities of up to 130 ft/sec (40 m/sec) with negligible impact. Even abrasive particles like sand only minimally affect its corrosion resistance.
Titanium remains largely unaffected by hydrogen absorption when exposed to seawater, even at elevated temperatures. Hydrogen absorption is typically a concern only under the following stringent conditions:
Titanium alloys exhibit exceptional immunity to all forms of microbiologically influenced corrosion. Although biofouling can occur due to titanium's non-toxicity towards marine organisms, this can be effectively minimized through chlorination or by increasing the water velocity in heat exchangers.
Unlike many materials, titanium's fatigue performance remains steady in seawater. Both fatigue endurance limits and fatigue *** growth rates show no variance whether tested in air or seawater.
In the galvanic series, titanium is positioned near the noble end, close to stainless steels, and typically acts as the cathode when paired with other metals. Consequently, titanium is not impacted by galvanic corrosion but can accelerate corrosion in the other metal. Coupling titanium with more noble metals, like graphite, only strengthens titanium's passivity.
Grade 2 Titanium Rod maintains its fatigue properties even in seawater. Fatigue endurance limits and fatigue *** growth rates are consistent whether tested in air or seawater.
CP2 Grade Titanium Rod is highly weldable with appropriate precautions. Due to titanium's reactive nature, an inert gas shield must protect both the OD and ID of the rod. The material should be devoid of any grease or oil contamination.
Typically, Grade 2 Titanium Rod is welded using manual or automatic TIG welding, with or without filler wire. To minimize the heat-affected zone, low heat input is recommended. Post-weld heat treatment is generally unnecessary.
| Working material: | 3.7035 / UNS R50400 |
| Diameter: | 3 - 400 mm |
| Lengths: | 2.000 - 4.000 mm |
| Versions: | Rolled, forged, annealed |
| Surfaces: | Turned, peeled, polished |
| Standards: | ASTM B 348, ASME SB 348, DIN 17862, ASTM F 67, NACE MR 0175, ISO 1515156-3, ISO 5832-2 |
In need of round rod material made from Grade 2 Titanium Alloy Rod-3,7035? At Daxun, we offer customized titanium rods tailored to your project's requirements, backed by our experienced team.
Our Grade 2 Titanium bars are available in diameters ranging from 2.0 mm to 400 mm. Note that execution and tolerances may vary; small diameters will be delivered centerless ground with h7 tolerances, while larger diameters will have h9 or h11 tolerances.
When placing a purchase order, please include the quantity, grade, type or category, API5L reference, thickness, width, length, and any specific attachments or additional requirements. These may relate to chemical composition, mechanical properties, heat treatment, additional testing, manufacturing process, surface coating, or end finish. Reach out to Jiangsu Daxun Alloy Co., Ltd. today, and we will respond to your email promptly.
Q1: What products can you offer?
A: We offer a wide array of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300 series. Additionally, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, and 2507. High-nickel alloys like 904L, 800H, and 600H are also available.
Q2. Can you produce the products according to my own drawings?
A: Absolutely, we can manufacture products precisely according to your drawings, ensuring they meet your utmost satisfaction.
Q3. How does your factory ensure quality control?
A: Quality is our top priority. We consistently emphasize meticulous quality control from the initial stages to the final product.
Q4. Can I request a different form of packaging and transportation?
A: Yes, we can alter the packaging and transportation form according to your preferences.
Please note, you will need to cover any additional costs incurred during this process.
Q5. How does your factory ensure quality control?
A: Quality is our top priority. We consistently emphasize meticulous quality control from the initial stages to the final product.
Q6. How long is the delivery time?
A: Delivery takes 7 to 20 working days after payment confirmation.
For urgent orders, we strive to expedite the process to meet your needs.
Q7. What are your payment options?
A: We offer several payment options: 100% T/T advance, Western Union for small orders,
30% T/T with the remaining 70% paid before shipment,
and 100% Irrevocable LC at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Inform us of your specific usage, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I get a sample?
A: We provide FREE samples for your evaluation. For small pieces, we may cover the courier costs, depending on the case.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
){kind=link}