Basic Info.
Model NO.
410 stainless steel rod
Type
Stainless Steel Bars
Standard
ASTM, AISI, GB, JIS, DIN, EN
Certification
ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS
Manufacturing
Hot Rolling, Cold Rolling, Forging
Trademark
TISCO POSCO Baosteel
Transport Package
Wooden Box or Wooden Pallet
Specification
φ 3.0mm-350mm
Product Description
| Product Parameters: Stainless Steel rod |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. |
| Under Third Party Inspection |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Globally Recognized Leader in Stainless Rod and Round Bar Fabrication Services
Presenting an extensive range of high-quality products including ASTM A479 AISI 410 Stainless Steel Round Bars, ASTM A479 SS 410 Square Bars, and 410 Stainless Steel Flat Bars. We specialize in Stainless Steel 410 Rods and offer an impressive variety of SS 410 Round Bars, including SS DIN 1.4006 Round Bars. Partner with us to buy Stainless Steel 410 Bright Bars, 410 SS Polished Bars, and SS 410 Rods from leading manufacturers and suppliers in China, ensuring unmatched quality and performance.
Premium Hot Rolled Stainless Steel Rods
Our stainless steel rods and bars are meticulously heated and rolled through multiple passes in a state-of-the-art rolling mill, ensuring complete specifications and performance that meets and exceeds industry standards.
Cold Drawn Bright Stainless Steel Rods
Experience the superior quality of our Cold-Drawn Stainless Steel Rods, meticulously drawn under cold working conditions. These rods feature a smooth surface, with options for additional polishing and grinding to achieve a flawless finish.
Forged Excellence in Stainless Steel Rods and Bars
Our Forged Stainless Steel Rods undergo multiple forging processes to significantly enhance their mechanical properties and achieve superior strength, making them ideal for demanding applications.
Comprehensive Product Properties
Our expansive network of service centers ensures a ready supply of common stainless steel bar sizes and alloys for fast delivery. We also specialize in producing custom-sized stainless steel bars. For quantities below factory minimums, we offer a stocking program for quick turnarounds. Daxun Alloys stocks stainless steel round bars ranging from 1/16" to 26" in diameter, available in nearly every stainless steel grade including 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.
Specialized Additional Services
Our inventory predominantly features our unique processed bar grades. These stainless steel round bars are melted to consistent standards, enhancing machinability and lowering the overall cost of each part. Our advanced bar processing machinery ensures Daxun Alloys can meet the precise specifications of our esteemed customers.
1. Daxun offers specialized heat treatments tailored to the specific chemistry of the metal being treated. 2. Positive Material Identification (PMI): We provide thorough PMI testing, either in-house or in collaboration with an independent laboratory. 3. Ultrasonic Testing (UT): This technique employs high-frequency sound energy for inspecting and measuring stainless steel bar products, facilitating defect detection, evaluation, and dimensional measurement.
Contact Daxun for More Information on Stainless Steel Rods
Chemical Composition of 410 Stainless Steel Rods
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
Mechanical Properties of 410 Stainless Steel Rods
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
Physical Properties of 410 Stainless Steel Rods
| Density (lb./ in^2) @ RT | | 0.28 |
| Modulus of Elasticity in Tension (psi x 10^6) | | 29 |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| | 932oF | 16.6 |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| | 32 to 1,200oF | 6.5 |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Manufacturing Excellence at Daxun's Stainless Steel Rods Facility
Our forming capabilities feature cutting-edge radial forging machines, advanced heat treatment and melting furnaces, and rolling mills for top-quality titanium rod production. We also utilize a unique hydroforming process for crafting exceptional parts.
Advanced Heat Treatment Furnace at Daxun
Our stainless steel rod heat treatment employs advanced furnace equipment, guaranteeing the material's stability and high-performance attributes.
Superior Smelting Capabilities at Daxun
Daxun Stainless Steel employs the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. This sophisticated technology minimizes impurities during the smelting process, significantly enhancing the finished stainless steel rods' performance.
Allow us the honor of becoming your reliable and esteemed Stainless Steel Rod supplier.
At Jiangsu Daxun Alloy Co., Ltd., our stainless steel products come with full certification and traceability, ensuring unmatched quality. We proudly supply premium stainless steel to top-tier industries, including aerospace, industrial, medical, marine, and military sectors.
Detailed mechanical properties of a wide range of stainless steel bars.
| | Tensile Strength | Yield Strength | | | | | | |
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. |
| Grade | Tensile Str | Yield Str | Elong | Hardness |
| (MPa) min | 0.2% Proof | (% in 50mm) min |
| | (MPa) min | | Rockwell B (HR B) max | Brinell (HB) max |
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| | Tensile Strength | Yield Strength | | | |
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness |
| (MPa) min | 0.2% Proof | (% in 50mm) min |
| | (MPa) min | | Rockwell C (HR C) | Brinell (HB) |
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
2507/
S32750 | Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi |
| Ultimate Tensile Strength | 116 ksi |
| 0.1% Offset Yield Strength 0.2% | 91 ksi |
| Elongation in 2 inches, % | 15% |
| Hardness Rockwell C | 32 |
| Impact Energy | 74 ft.-lbs |
| Density | 0.28 lb per inch3 |
| Modulus of elasticity | 28 x 10(6) psi |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of |
| Thermal conductivity | 8.7 Btu/hr ftoF |
| Heat capacity | 0.12 Btu/ lb oF |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
To learn more about our exceptional stainless steel rods, please reach out to Daxun today.
- GENERAL PROPERTIES
Standard Martensitic Stainless Steel Bar 410 is an ideal choice for parts enduring extreme stress, offering outstanding corrosion resistance along with superior strength and hardness. Containing a minimum of 11.5% chromium, Alloy 410 round bar withstands corrosion in steam, various moderate chemical conditions, and mild atmospheres. This versatile grade typically comes in a hardened but machinable state, perfect for applications demanding high strength and moderate heat and corrosion resistance. Optimal corrosion resistance is achieved through polishing, tempering, and hardening. Specifications: UNS S41000
APPLICATIONS:
- Cutlery
- Steam and gas turbine blades
- Kitchen utensils
- Bolts, nuts, screws
- Pump and valve parts and shafts
- Mine ladder rugs
- Dental and surgical instruments
- Nozzles
- Hardened steel balls and seats for oil well pumps
CORROSION RESISTANCE:
- 410 Stainless Steel offers robust resistance to air corrosion, mildly corrosive environments, and drinking water. With appropriate post-use cleaning, it excels in daily activities such as sports and food preparation. It exhibits high resistance to low concentrations of moderate organic and mineral acids, ensuring durability and reliability.
Features:
- Magnetic in both annealed and hardened conditions.
- An extensive array of properties can be developed through various heating treatments.
- Exhibits remarkable corrosion resistance to acids such as sulfuric acid.
Available Stock Sizes:
Visit specific product pages for unique sizes and contact us for a quote on custom size orders.
SS 410 grade stainless steel round bars
410 Stainless steel round bars are extensively utilized across numerous sectors, from construction to automotive parts. Given their wide-ranging applications, Daxun Alloys supplies stainless steel round bars in multiple grades and sizes. Leveraging our advanced and complimentary cutting service, we cater precisely to your specific requirements each time.
Can you manufacture stainless steel grinding bars and rods?
Absolutely! We specialize in producing stainless steel grinding bars and rods that boast precise dimensions, perfect roundness, and superior straightness. These features surpass those found in polished stainless steel bars, though the processing cost is higher.
Q1: What products are available from your company?
A: We offer a wide range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L.
Additionally, we supply 400 series steel and duplex stainless steel such as 2205, 2304, 2101, 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you manufacture products according to my drawings?
Yes, we can produce products based on your drawings, ensuring they meet your highest satisfaction.
Q3. What measures does your factory take for quality control?
Quality is our top priority. We meticulously control quality from the start of production until the very end.
Q4. Can I request different packaging and transportation methods?
Yes, we can modify the packaging and transportation methods as per your request.
However, you will need to cover any additional costs and price differences incurred during these changes.
Q5. How stringent is your factory's quality control?
Quality remains our utmost priority. We maintain rigorous quality control measures from the beginning to the end of the production process.
Q6. What is the estimated delivery time?
A: Typically, delivery takes 7 to 20 working days after payment confirmation.
For urgent orders, we expedite the process to ensure early completion.
Q7. What payment methods do you accept?
A: We accept 100% T/T in advance or Western Union for small orders.
B: For larger transactions, we accept 30% T/T upfront with the balance 70% due before shipment.
C: We also accept 100% Irrevocable LC at sight for significant orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can tailor our materials for deep drawing applications like stainless steel pots, sinks, and bowls. Let us know your specific needs, and we'll adjust the mechanical properties accordingly.
Q9: How can I obtain a sample?
A: We provide FREE samples for evaluation and testing. For small sample pieces, we usually cover courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: We have exported our stainless steel materials to numerous countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Address:
B108, No. 32-1, Chengnan Road, Xinwu District, Wuxi, Jiangsu, China
Business Type:
Manufacturer/Factory, Trading Company
Business Range:
Metallurgy, Mineral & Energy
Management System Certification:
ISO 9001, ISO 9000, ISO 14001, ISO 14000, ISO 20000, OHSAS/ OHSMS 18001, IATF16949, HSE, ISO 14064, QC 080000, GMP, BSCI, BRC, SA 8000, QHSE, HACCP, ISO 13485, EICC, ANSI/ESD, SEDEX, ISO 22000, AIB, WRAP, GAP, ASME, ISO 29001, HQE, IFS
Company Introduction:
Founded in 2003, Daxun Alloy is a leading global metal material manufacturer. Headquartered in Wuxi, China, the company has multiple production bases and sales offices around the world. Daxun Alloy focuses on the development, production and sales of various stainless steels, titanium alloys, high-temperature alloys, etc. For general industry, construction, aerospace, energy, chemical industry, medical and other fields.
China, Daxun Metal Group is a global vertically integrated metal material manufacturer and stockist. Daxun can provide finished products and customized full-process services and professional technical services. Currently, the group has 600 employees and covers a total area of 130, 000 square meters. Daxun has a standing inventory of 50, 000 tons of stainless steel, 5, 000 tons of nickel-based alloys, and 2, 000 tons of pure titanium and titanium alloys. The main product forms are metal plates, metal coils, metal pipes, and metal bars. The metal materials produced by Daxun are market leaders for marine, energy, military, general industrial and aerospace applications. In addition, the company also produces seamless pipes, plates, forgings and other metal materials for power generation and oil and gas applications; Commercial and military alloy products; And metal alloys and other metal products for the forging industry.