| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 2507 S32750 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
ASTM A276 Super Duplex Steel S32750 Round Bar. We are a premier Super Duplex Steel Bar Supplier, offering Super Duplex Steel UNS S32760 Bright Bar, Super Duplex Steel 2507 Bar, Super Duplex Steel UNS S32950 Flat Bar, and Austenitic Super Duplex Steel S32760 Round Bar. Our range includes Hot Rolled Super Duplex Steel S32760 Round Bar and expertly crafted Super Duplex Steel S32760 products. We are a proud manufacturer of Super Duplex Steel UNS S32750 in China.
For more information on stainless steel rods, please contact Daxun.
2507 Stainless Steel Rod Chemical Composition
| Grade | Super Duplex 2507 |
| UNS Designation | S32750 |
| Carbon (C) Max. | 0.03 |
| Manganese (Mn) Max. | 1.2 |
| Phosphorous (P) Max. | 0.035 |
| *** (S) Max. | 0.02 |
| Silicon (Si) Max. | 0.8 |
| Chromium (Cr) | 24.0-26.0 |
| Nickel (Ni) | 6.0-8.0 |
| Molybdenum (Mo) | 3.0-5.0 |
| Nitrogen (N) | 0.24-0.32 |
| Iron (Fe) | Bal. |
| Copper (Cu) | 0.5 |
| Other Elements | - |
| Physical Properties of Super Duplex 2507 Alloys in the Annealed Condition at -20°F to +100°F | ||||||||||||||
| Tensile Strength | Yield Strength | |||||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
| Super Duplex 2507 | S32950 | A789, A790 | 100,000 | 690 | 100 | 70,000 | 485 | 70 | 20 | - | 30.5 Rc | - | - | - |
| Super Duplex 2507 | S32750 | A789, A790 | 116,000 | 800 | 116 | 80,000 | 550 | 80 | 15 | - | 32 Rc | 27.5 | 7.2 | 98 |
| Density, lb/in3 | 0.28 |
| Modulus of Elasticity, psi | 29.0x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 7.5 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 8 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microhm-in | 31.5 |
Our forming capabilities include cutting-edge radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rod manufacturing. Additionally, we employ a unique hydroforming process for part production.
Our advanced heat treatment furnace ensures the stability and high performance of our stainless steel rods through precise temperature control and treatment processes.
Daxun Stainless Steel utilizes the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These technologies minimize impurities during smelting, significantly enhancing the performance and quality of our finished stainless steel rods.
Our stainless steel products come with full certification and traceability. We proudly supply top-quality stainless steel to premier sectors such as aerospace, industrial, medical, marine, and military industries.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you manufacture stainless steel grinding bars and rods?
Absolutely, we specialize in stainless steel grinding bars and rods that boast precise dimensions, exceptional roundness, and straightness. These offer superior performance compared to stainless steel polished bars, though the processing costs are higher.
Q1: What types of products can you supply?
A: We offer a broad array of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300,
400 series, and duplex stainless steels such as 2205, 2304, 2101, 2507, etc. Additionally, we have high-nickel alloys like 904L, 800H, and 600H.
Q2: Can you manufacture products based on my custom drawings?
Yes, we are fully capable of producing products according to your custom drawings, ensuring your utmost satisfaction.
Q3: What measures does your factory take for quality control?
Quality is our top priority. We maintain rigorous quality control from the beginning of the process to the end.
Q4: Can I request changes to the packaging and transportation method?
Yes, we can adapt the packaging and transportation methods to meet your specific requests.
However, you will need to cover any additional costs incurred during this period, including any price differences.
Q5: How does your factory ensure quality control?
Ensuring quality is our foremost priority. We strictly control quality from the start of the process to the finish.
Q6: What is your delivery time frame?
A: Our delivery window is typically 7 to 20 working days post-payment confirmation.
If the order is urgent, we will expedite production in our workshop to meet the deadline.
Q7: What are your payment terms?
A: 100% T/T in advance, Western Union (for small orders).
B: 30% T/T upfront, with the remaining 70% due before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you provide Deep Drawing Quality (DDQ) material?
A: Yes, we can. Our materials are suitable for making stainless steel pots, sinks, bowls, and more. Tell us your specific needs, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: We provide FREE samples for your inspection and testing. If a small piece is required, we may cover the courier costs, depending on the circumstances.
Q10: Which countries have you exported to?
A: We have exported our stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}