| Product Parameters: Stainless Steel rod | |
| Material | 2507 S32750 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Our extensive product range includes ASTM A276 Super Duplex Steel S32750 Round Bar, Super Duplex Steel Bar Supplier, Super Duplex Steel UNS S32760 Bright Bar, Super Duplex Steel 2507 Bar, Super Duplex Steel UNS S32950 Flat Bar, Austenitic Super Duplex Steel S32760 Round Bar, Hot Rolled Super Duplex Steel S32760 Round Bar, and many more. We are a leading manufacturer of Super Duplex Steel UNS S32750 in China.
For more detailed information on our stainless steel rods, please contact Jiangsu Daxun Alloy Co., Ltd.
2507 Stainless Steel Rod Chemical Composition
| Grade | Super Duplex 2507 |
| UNS Designation | S32750 |
| Carbon (C) Max. | 0.03 |
| Manganese (Mn) Max. | 1.2 |
| Phosphorous (P) Max. | 0.035 |
| *** (S) Max. | 0.02 |
| Silicon (Si) Max. | 0.8 |
| Chromium (Cr) | 24.0-26.0 |
| Nickel (Ni) | 6.0-8.0 |
| Molybdenum (Mo) | 3.0-5.0 |
| Nitrogen (N) | 0.24-0.32 |
| Iron (Fe) | Bal. |
| Copper (Cu) | 0.5 |
| Other Elements | - |
| Physical Properties of Super Duplex 2507 Alloys in the Annealed Condition at -20°F to +100°F | ||||||||||||||
| Tensile Strength | Yield Strength | |||||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
| Super Duplex 2507 | S32950 | A789, A790 | 100,000 | 690 | 100 | 70,000 | 485 | 70 | 20 | - | 30.5 Rc | - | - | - |
| Super Duplex 2507 | S32750 | A789, A790 | 116,000 | 800 | 116 | 80,000 | 550 | 80 | 15 | - | 32 Rc | 27.5 | 7.2 | 98 |
| Density, lb/in3 | 0.28 |
| Modulus of Elasticity, psi | 29.0x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 7.5 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 8 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microhm-in | 31.5 |
Our state-of-the-art forming capabilities include radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rods, enhanced by our unique hydroforming process for part manufacturing.
Our advanced heat treatment furnace equipment ensures the superior stability and performance of our stainless steel rods.
Utilizing the latest vacuum induction furnace, vacuum consumable furnace, and electroslag furnace technology, we minimize impurities during the smelting process, thereby enhancing the performance of our finished stainless steel rods.
Our stainless steel products are not only fully certified but also traceable. We are dedicated to supplying the highest quality stainless steel to prestigious industries such as aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you provide SS grinding bar & rod?
Absolutely! We offer SS grinding bars and rods characterized by precise dimensions, impeccable roundness, and exceptional straightness. Though superior to stainless steel polished bars, please note that these come with a higher processing cost.
Q1: What products can you offer?
A: We offer a wide range of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, 300 series,
400 series, and duplex stainless steels like 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my drawings?
Yes, we can manufacture products based on your drawings to ensure they meet your highest satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We place great emphasis on rigorous quality control from the beginning to the end of the production process.
Q4. Can I request changes in packaging and transportation?
Yes, we can modify the packaging and transportation forms according to your specific requests.
However, please note that you would need to bear any additional costs incurred during this period.
Q5. How does your factory handle quality control?
Quality is our top priority. We place great emphasis on rigorous quality control from the beginning to the end of the production process.
Q6. What is your delivery time?
A: Typically, it takes about 7 to 20 working days after payment confirmation.
If the order is urgent, we will expedite the workshop processes to meet your timeline.
Q7. What are your payment terms?
A: 100% T/T in advance or Western Union for small orders.
B: 30% T/T in advance and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you provide DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for making stainless steel pots, sinks, bowls, etc. Just let us know your application, and we'll adjust the mechanical properties to fit your requirements.
Q9: How can I get a sample?
A: We offer FREE samples for your inspection and testing. For small pieces, we may cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: So far, we have exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}