| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition of 201 Stainless Steel Rods
Chemical Composition (wt%) Limits as per ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties of 201 Stainless Steel Rods
Mechanical property requirements for annealed products as defined in ASTM A240 and ASME SA240
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
Mechanical property requirements for cold worked flat rolled products as specified in 201 Stainless Steel Rod - Elevate your projects with the superior craftsmanship of our 201 stainless steel rod.
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Physical Properties
Physical Properties for Type 201 Stainless Steel Rod - Discover the exceptional physical attributes of our Type 201 stainless steel rod, ensuring durability and reliability.
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Forming Capabilities - Our state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills enable the precise manufacturing of titanium rods. Additionally, our unique hydroforming process is ideal for creating intricate parts.
Stainless Steel Rod Heat Treatment - Utilizing cutting-edge heat treatment furnace equipment, we ensure the stability and high performance of our stainless steel rods.
Daxun Stainless Steel employs the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace to meticulously reduce impurities during the smelting process, thus enhancing the performance of the finished stainless steel rods.
Our state-of-the-art stainless steel products come with complete certification and traceability. We pride ourselves on delivering top-tier stainless steel materials to a variety of prestigious industries, including aerospace, industrial sectors, medical fields, marine endeavors, and military applications.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you provide SS grinding bars and rods?
Yes, we specialize in SS grinding bars and rods noted for their precise dimensions, exceptional roundness, and straightness. These attributes surpass those of standard polished stainless steel bars, although they do come with a higher processing cost.
Q1: What products can you offer?
A: We offer a comprehensive range of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. The 300 series is also available.
Additionally, we provide the 400 series and duplex stainless steels such as 2205, 2304, 2101, and 2507. High-nickel alloys like 904L, 800H, and 600H are also part of our offerings.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products tailored to your drawings, ensuring they satisfy your specifications fully.
Q3. How does your factory manage quality control?
Quality is our top priority. We consistently prioritize quality control from the initial stages through to the final product.
Q4. Can I request to change the packaging and transportation method?
Yes, we can modify the packaging and transportation methods according to your preferences.
However, any additional costs incurred during this period and differences in price will be your responsibility.
Q5. How does your factory manage quality control?
Quality is our top priority. We consistently prioritize quality control from the initial stages through to the final product.
Q6. How long is the delivery time?
A: The delivery time is typically 7~20 working days after payment confirmation.
For urgent orders, we expedite the process to complete them as soon as possible.
Q7. What are your payment terms?
A: We accept 100% T/T advance, Western Union (for small orders).
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Provide us with the intended use, and we'll adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: Free samples are available for your inspection and testing. If a small piece is needed, we may cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many other countries.
){kind=link}