| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Explore our extensive range of stainless steel products: ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, Stainless Steel 410 Rod. We proudly offer SS 410 Round Bar, SS DIN 1.4006 Round Bar, Stainless Steel 410 Bright Bar, 410 SS Polished Bar, and more. As leading manufacturers and suppliers in China, we ensure top-quality materials for your needs.
For further details on our stainless steel rods, please reach out to Daxun.
410 Stainless Steel Rod Chemical Composition
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our forming capabilities are second to none, featuring state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rod manufacturing. Additionally, we utilize a unique hydroforming process for manufacturing complex parts.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods, meeting the highest industry standards.
Utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun Stainless Steel minimizes impurities during the smelting process, significantly enhancing the performance of our finished stainless steel rods.
Our stainless steel products are fully certified and traceable, adhering to the highest standards of quality. We proudly supply top-grade stainless steel to a diverse array of leading industries, such as aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
Please refer to specific product pages for unique sizes and feel free to contact us for a quote on any custom size orders.
410 Stainless steel round bars are extensively utilized across various industries, from construction to automotive parts. Due to their vast range of applications, Daxun Alloys provides stainless steel round bars in multiple grades and sizes. Our advanced cutting service ensures we meet your precise needs every time.
Can you do SS grinding bar & rod?
Yes, we can produce SS grinding bars & rods with precise dimensions, exceptional roundness, and straightness. These outperform regular polished stainless steel bars, though they do come with higher processing costs.
Q1: What products can you offer?
A: We provide a wide range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and the 300 series.
Additionally, we offer 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Absolutely, we can manufacture products that align perfectly with your drawings to ensure maximum satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We rigorously monitor and control quality from start to finish.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation methods as per your requests.
However, you will need to cover any additional costs and related expenses incurred during this period.
Q5. How does your factory handle quality control?
Quality is our top priority. We rigorously monitor and control quality from start to finish.
Q6. How long is the delivery time?
A: The delivery time is typically 7 to 20 working days after payment confirmation.
If your order is urgent, we will expedite the process in our workshop.
Q7. What are your payment terms?
A: 100% T/T payment in advance, or Western Union for smaller orders.
B: 30% T/T in advance and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for larger orders.
Q8: Can you produce DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, etc. Inform us of your specific usage, and we will tailor the mechanical properties to meet your needs.
Q9: How can I get a sample?
A: FREE samples are available for your inspection and testing. We can cover the courier cost for small samples, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}