| Grade 2 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 2 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 2- TA2- USN 50400 |
| Grade 2 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 2 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ1.0mm to φ1219mm | |
| Grade 2 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 2 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form TA2 | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TA2 3.7035 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 2 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 2 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 2 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 2 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 2 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 2 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 2 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 2 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 2 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 2 Titanium Welded Tube: Crafted to Perfection! Diameter spans from 6.0mm to 1219mm, with wall thickness from 0.3mm to 30mm, tailored to diameter, and lengths soaring up to 25000mm. Fabricated from Gr1 titanium tube, these welded tubes originate from flat rolled billets (tube blanks) on state-of-the-art electric tube welding machines, employing automatic tungsten inert gas (argon) welding and heat treatment right on the mill line. Each tube undergoes rigorous mechanical tests, precise geometric measurements, comprehensive ultrasonic and eddy current testing, and stringent pneumatic or hydrostatic testing before being meticulously packaged to meet customer specifications. Our advanced manufacturing technology and superior inspection and testing equipment guarantee that our thin wall welded tubes exceed ASTM B 338 and ASME SB 338 standards.
Daxun's Grade 2 Titanium Tube stands out for its medium strength and superior cold forming properties. It boasts exceptional welding capabilities and remarkable resistance to both oxidation and corrosion.
Buy Grade 2 Titanium Tubes from Daxun! We offer an extensive range of sizes starting from a 1.0 mm diameter, available from stock or custom-made to your precise specifications. We can promptly supply drawn, seamless rolled, or longitudinally welded tubes for diverse applications. Our offerings of welded or seamless tubes made from Grade 2 Titanium adhere to typical heat exchanger specifications such as ASTM B 338, ASME SB 338, DIN, and VD TÜV.
Our CP Grade 2 Tubes: Lightness Meets Strength! With a density of 4.51 g/cm3, 45% lower than ferrous alloys, these medium-strength tubes feature a typical yield strength of 352 MPa. Showcasing excellent ductility, formability, and welding properties, the addition of iron and oxygen enhances their strength and formability. Comparable to Grade 1, these tubes exhibit excellent corrosion resistance in oxidizing conditions, yet they offer greater strength.
Grade 2 Titanium Tubes: The Optimal Blend of Strength and Ductility. Made from commercially pure titanium, these tubes achieve a perfect balance between strength and ductility. They are renowned for their toughness, high strength, weldability, and corrosion resistance, making them the preferred titanium alloy for piping systems, heat exchangers, reaction and pressure vessels, and flue gas desulfurization systems. Widely used across industries such as chemical and petrochemical processing, aerospace, and marine, Grade 2 titanium alloys are a versatile choice for demanding applications.
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
These premium-grade titanium tubes are meticulously manufactured through hot-rolling or hot-extrusion processes. They are professionally straightened, precisely machined both inside and out, and polished to perfection. Available in both heat-treated and non-heat-treated forms, our titanium tubes meet the highest standards of quality. Additionally, our company boasts 100% ultrasonic flaw detection capabilities, ensuring top-notch reliability and performance.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: OD 19mm to 325mm, wall thickness 9mm to 30mm, length up to 5000mm (customizable as agreed between the manufacturer and the customer); - Hot-extruded Titanium Tubes: OD 50mm to 160mm, wall thickness 7mm to 35mm, length up to 3000mm (customizable as agreed between the manufacturer and the customer).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are expertly supplied in heat-treated forms and undergo surface etching as well as rigorous hydrostatic or ultrasonic testing, per specific manufacturing requirements. These tubes are available with: - OD 6mm to 89mm, wall thickness 0.5mm to 11mm, length up to 6000mm (customizable as agreed between the manufacturer and the customer).
Titanium Welded Pipes
DaXun specializes in the production and supply of high-quality titanium pipes, featuring diameters ranging from 12.7 mm to 38.1 mm (0.47 in to 1.5 in) and wall thicknesses from 0.4 mm to 1.65 mm (0.016 in to 0.065 in, depending on diameter), with lengths reaching up to 25000 mm. These pipes are crafted from flat-rolled raw material (kelp) using advanced automatic tungsten inert gas (argon) welding on electric pipe welders and undergo heat treatment on the mill line. Rigorous mechanical testing, precise geometrical measurements, 100% ultrasonic and eddy current testing, and comprehensive pneumatic or hydrostatic testing ensure the pipes meet ASTM B 338 and ASME SB 338 standards. Tailored packing options are available to meet customer specifications. Our Gr1, Gr2, and Gr12 titanium alloy pipes are perfect for engineering and chemical industry applications.
| CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium tube PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
Grade 2 Titanium Tube stands out as the premier choice for industrial applications, striking the perfect balance between moderate strength and exceptional ductility. Renowned for its outstanding corrosion resistance, it performs superbly in both highly oxidizing and slightly reducing environments (including chlorides). This tube is indispensable in the chemical and offshore industries, aircraft manufacturing, heat exchangers, hypochlorite systems, fire water systems, ballast water systems, industrial and aerospace components, CPI equipment, and a wide range of piping applications.
Experience the unmatched versatility of the Grade 2 Titanium Tube, ASTM B338/B861/B862 Heat Exchanger Pipe, from Jiangsu Daxun Alloy Co., Ltd. This industrial marvel offers an exceptional balance of moderate strength and commendable ductility. Its superior corrosion resistance thrives in both highly oxidizing and slightly reducing environments, including chlorides. This makes it an ideal solution for diverse sectors such as chemical processing, offshore industries, aircraft manufacturing, heat exchangers, hypochlorite systems, fire water systems, ballast water systems, and CPI equipment. Its robustness and ease of forming ensure reliable performance in industrial, aerospace, and marine applications.