| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | GR1 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a premier global producer and trusted supplier of superior Grade 1 titanium plates.
Our Pure Grade 1 titanium plate is celebrated for its outstanding ductility and cold formability, making it perfect for deep drawing applications. Renowned for its excellent resistance to general and seawater corrosion, as well as its resilience against oxidizing, neutral, and mildly reducing media, including chlorides, Grade 1 titanium is an exceptional choice. Its low density (about half that of nickel-based alloys), high strength-to-weight ratio, and superior corrosion resistance make it ideal for demanding chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile, boasting impressive cold formability, corrosion resistance, weldability, and impact hardness.
Producers of ASTM B265 Titanium Gr 1 Plates, Titanium Gr 1 Sheets, and Finished Plates. Suppliers of Titanium Gr 1 Coils, Hot Rolled Plates, and Cold Rolled Plates. Dealers of ASTM B265 Titanium Grade 1 Sheets, Patterned Plates, and Perforated Plates. Leading Manufacturers of Titanium Grade 1 Sheets and Plates in China.
We ensure prompt and efficient delivery of Grade 1 titanium plate products, supported by an integrated system encompassing production capacity, information flow, logistics, and capital flow. Our order data is instantly pushed to the logistics system, allowing for seamless data integration. Strategically located processing centers near highways and waterways facilitate efficient scheduling, swift responses, and smooth storage and transportation. This comprehensive approach guarantees timely completion of tasks.
Grade 1 titanium plate, known for its lower density and superior ductility, is ideal for industries requiring weight sensitivity and deep drawing processes. Key sectors include medical, chemical equipment, aerospace, marine, chemical processing, and desalination. Typical applications encompass oil and gas components, reaction and pressure vessels, piping systems, power generation, heat exchangers, linings, flue gas desulfurization systems, and various industrial components. Common standards adhered to include ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, and AMS4972.
Our cold-rolled Grade 1 Titanium Plates range from 0.3 mm to 6.0 mm in thickness and are available in hot rolled or heat-treated conditions. Hot-rolled thicknesses range from 4.76 mm to 155 mm and are produced by longitudinal and transverse rolling. Plates can be supplied as cut blanks, meeting complex shape requirements through mechanical or chemical processing based on customer needs. If needed, creep flattening can be applied as a heat treatment to relieve internal stresses and meet specific flatness criteria.
Chemical Composition of Ti 6AL-4V Grade 5 Titanium Sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
Chemical Composition of Grade 2 Titanium Sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Mechanical Properties of Grade 2 Titanium Sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN, the unparalleled metal expert, specializes in both small and large-scale titanium plate projects. As your quintessential reference point and reliable long-term partner, DAXUN is here to supply your business with high-quality titanium plates and comprehensive technical assistance. Think of DAXUN not merely as your provider of industrial pure titanium and titanium alloy plates but as a strategic ally committed to helping you overcome any challenge and fulfill any requirement, ultimately enabling the successful achievement of your project ambitions.
Our state-of-the-art DAXUN service center in China boasts a full inventory of titanium plate products, ensuring rapid order processing. Alongside basic processing services, we offer advanced water jet cutting and plate nesting solutions, adding immense value for our customers by significantly saving both time and costs.
DAXUN's unwavering commitment to continuous investment in production facilities and capacity agreements with our esteemed partners guarantees our position at the pinnacle of titanium plate quality, now and in the future.
Reach out to DAXUN today to access the most competitive titanium plate prices and cutting-edge technical information.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a premier manufacturer and supplier of Ti-6Al-4V Grade 5 TC4 UNS R56400 Alloy Titanium Plates from China! We aspire to produce the world's highest-performance titanium alloy plates, ensuring rapid worldwide delivery. Our ASTM B265 Grade 2 and Grade 5 Titanium Plates range from 0.5mm to 300mm in thickness (cold rolled for 0.5mm-6.0mm, hot rolled for 6.0-50mm, and forged for 50mm and above). Grade 5 titanium plate (Ti-6Al-4V) is renowned for its superior strength, ductility, excellent corrosion and high-temperature resistance, making it the material of choice for various general and military industries. Compliant with: ASTM, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
Ti-6Al-4V Grade 5 titanium plates are extensively used in aerospace, military, power industries, vehicle armor, rocket precision guidance parts, and marine applications.
Grade 1
Today, DAXUN Alloys stands as a leading global producer and supplier of premium Grade 1 titanium plates.
Pure Grade 1 titanium plate boasts exceptional ductility and cold formability, making it perfect for deep drawing. Known for its outstanding general and seawater corrosion resistance, Grade 1 titanium also resists oxidizing, neutral, and mildly reducing media, including chlorides. Its low density, roughly half that of nickel-based alloys, coupled with a high strength-to-weight ratio and corrosion resistance, makes it ideal for severe chemical environments. Commercially pure Grade 1 titanium is the softest and most ductile, providing excellent cold formability, corrosion resistance, and weldability, along with good impact hardness.
Producers and suppliers of ASTM B265 Titanium Gr 1 Plates, Titanium Gr 1 Sheets, and Titanium Gr 1 Finished Plates. We offer Titanium Gr 1 Coils, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, and Perforated Plates. Available in China, our Titanium Gr 1 products meet the highest standards for quality and performance.
Grade 2
DAXUN manufactures and stocks commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses from 0.5mm to 120mm. Known as the 'workhorse' of commercially pure titanium, Grade 2 titanium plate excels in strength, ductility, and corrosion resistance for various industrial applications.
Grade 2 Titanium Plate is a versatile, commercially pure titanium plate offering an ideal mix of strength and ductility. It has excellent impact strength, weldability, and corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, and wet ***. Additionally, it resists seawater and salt solutions.
With low density, high strength-to-weight ratio, and corrosion resistance, titanium is perfect for a vast array of applications. Grade 2 Titanium Plate withstands stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. Melting at 1660°C, it's the preferred alloy for industrial applications demanding both good ductility and corrosion resistance.
DAXUN is your expert partner for small and large titanium plate projects. As your reliable reference and long-term ally, DAXUN provides not only industrial pure and titanium alloy plates but also comprehensive technical support. Consider DAXUN a strategic partner dedicated to conquering your challenges and fulfilling your project goals with top-notch titanium solutions.
At DAXUN's premier service center in China, we maintain an extensive stock of titanium plate products ready for swift order fulfillment. Our value-added services, including essential processing, precision water jet cutting, and efficient plate nesting, empower our customers to save both time and costs, ensuring they receive the highest quality products with unparalleled convenience.
With ongoing investments in our cutting-edge production facilities and strategic capacity agreements with our trusted partners, DAXUN solidifies its position as a leader in titanium plate quality. Our commitment ensures that we continue to set industry standards, both today and in the future.
Reach out to DAXUN today to secure the most competitive titanium plate prices and access comprehensive technical information. Our dedicated team is ready to assist you with all your titanium needs.
Q1: What products can you offer?
A: We offer a comprehensive range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and the 300 series.
Additionally, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Yes, we can manufacture products based on your drawings to ensure complete satisfaction.
Q3. How does your factory manage quality control?
A: Quality is our top priority. We place immense importance on quality control from start to finish.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can alter the packaging and transportation forms according to your request.
However, you will need to cover any additional costs and differences incurred during this period.
Q5. How does your factory manage quality control?
A: Quality is our top priority. We place immense importance on quality control from start to finish.
Q6. How long is the delivery time?
A: Our delivery time is typically 7-20 working days after payment confirmation.
If the order is urgent, we can expedite the process in our workshop.
Q7. What payment methods do you accept?
A: We accept 100% T/T advance and Western Union (for small orders).
B: We also accept 30% T/T upfront and the remaining 70% before shipment.
C: For large orders, we accept 100% Irrevocable LC at sight.
Q8: Can you produce DDQ (Deep Drawing Quality)?
A: Yes, we specialize in DDQ materials for stainless steel pots, sinks, bowls, etc. Inform us of your usage, and we'll tailor the mechanical properties accordingly.
Q9: How can I get a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we may cover the courier costs depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}