| Product Parameters: Stainless Steel rod |
| Material |
904L 1.4539 N08904 Super Austenite Round Bar |
| Specifications |
ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions |
EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars |
Outside Diameter in the range of 4mm to 500mm |
| Bright Bars |
Outside Diameter in the range of 4mm to 100mm |
| Hex Bars |
18mm - 57mm (11/16″ to 2-3/4″) |
| Finish |
Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length |
1 to 6 Meters, Custom Cut Lengths |
| Form |
Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability |
Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate |
Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. |
| Under Third Party Inspection |
| Testing & Inspection |
Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Hot Rolled Stainless Steel Rod
Our stainless steel rods and bars undergo a meticulous heating and rolling process through multiple passes in a rolling mill. They come in a wide range of specifications, ensuring that their performance consistently meets and exceeds industry standards.
Cold Drawn Bright Stainless Steel Rods
Crafted under cold working conditions, our cold-drawn stainless steel rods boast an exceptionally smooth surface. They can also be polished and ground to perfection, offering unparalleled quality.
Forged Stainless Steel Rod and Bar
Our forged stainless steel rods undergo multiple forging processes to enhance their mechanical properties and significantly increase their strength, making them ideal for demanding applications.
General Properties
Our extensive network of service centers ensures a ready supply of stainless steel bar products, available in standard sizes and alloys. We also cater to custom sizing needs. If your order quantity is below the factory minimum, our stocking program ensures prompt and fast turnaround. Daxun Alloys offers stainless steel round bars ranging from 1/16" to 26" in diameter, available in nearly every stainless steel grade including 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.
Additional Services
Our inventory predominantly features our exclusive processed bar grade: stainless steel round bars. These bars are melted to consistent standards, enhancing machinability and lowering the overall cost per part. Our advanced stainless steel bar processing machinery allows Daxun Alloys to precisely meet customer specifications.
1. Heat Treatments: Daxun can perform specialized heat treatments on our stainless steel bars, tailored to the specific chemistry of the metal being treated. 2. Positive Material Identification (PMI): We offer in-house PMI testing, and in certain cases, collaborate with independent labs to ensure material integrity. 3. Ultrasonic Testing (UT): Utilizing high-frequency sound energy, our UT capabilities enable precise inspection and measurement of stainless steel bars, aiding in defect detection and dimensional accuracy.
For more information on stainless steel rods, please contact Daxun
904L Stainless Steel Rod Chemical Composition
| Element |
% Present (in product form) |
| Carbon (C) |
0.02 |
| Silicon (Si) |
0.7 |
| Manganese (Mn) |
2 |
| Phosphorous (P) |
0.03 |
| Sulfur (S) |
0.01 |
| Chromium (Cr) |
19.00 - 21.00 |
| Nickel (Ni) |
24.00 - 26.00 |
| Nitrogen (N) |
0.15 |
| Molybdenum (Mo) |
4.00 - 5.00 |
| Copper (Cu) |
1.20 - 2.00 |
| Iron (Fe) |
Balance |
904L Stainless Steel Rod Mechanical Properties
| Product Form |
|
|
|
| |
C |
H |
P |
L |
L |
TW/TS |
| Thickness (mm) Max. |
8 |
13.5 |
75 |
160 |
2502) |
60 |
| Yield Strength |
Rp0.2N/mm2 |
2403) |
2203) |
2203) |
2304) |
2305) |
2306) |
| Rp1.0N/mm2 |
2703) |
2603) |
2603) |
2603) |
2603) |
2503) |
| Tensile Strength |
RmN/mm2 |
530 - 7303) |
530 - 7303) |
520 - 7203) |
530 - 7304) |
530 - 7305) |
520 - 7206) |
| Elongation min. in % |
Jmin(Longitudinal) |
- |
100 |
100 |
100 |
- |
120 |
| Jmin(Transverse) |
- |
60 |
60 |
- |
60 |
90 |
904L Stainless Steel Rod Physical Properties
| Density at 20°C kg/m3 |
8 |
| Thermal Conductivity W/m K at |
20°C |
12 |
| Modulus of Elasticity kN/mm2 at |
20°C |
195 |
| 200°C |
182 |
| 400°C |
166 |
| 500°C |
158 |
| Specific Thermal Capacity at 20°C J/kg K |
450 |
| Electrical Resistivity at 20°C mm2/m |
1 |
Daxun's Stainless Steel Rods Manufacturing Capabilities
Our forming capabilities are second to none, featuring advanced radial forging machines, state-of-the-art heat treatment furnaces, cutting-edge melting furnaces, and high-performance rolling mills for titanium rod manufacturing. We also employ a unique hydroforming process for producing complex parts.
Daxun's Heat Treatment Furnace
Our advanced heat treatment furnace equipment ensures that our stainless steel rods achieve maximum stability and performance, meeting the highest industry standards.
Daxun's Smelting Ability
Daxun Stainless Steel leverages the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These technologies significantly reduce impurities during the smelting process, enhancing the performance of our finished stainless steel rods.
Discover unmatched reliability with Jiangsu Daxun Alloy Co., Ltd., your premier supplier of 904L Stainless Steel Rods. Experience the perfect blend of quality and trust with our exceptional range of stainless steel products.
Our stainless steel offerings are not only fully certified but also traceable, ensuring you receive nothing short of the best. We proudly supply top-tier stainless steel to a diverse range of leading industries, including aerospace, industrial, medical, marine, and military sectors.
Mechanical Properties of Various Grades of Stainless Steel Bars
| |
Tensile Strength |
Yield Strength |
|
|
|
|
|
|
| Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
Grain Size Req. |
Max. Hardness |
Modulus of Elasticity (x106 psi) |
| 304 |
S30400 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
| 304L |
S30403 |
A270 A312 |
70,000 |
485 |
70 |
25,000 |
170 |
25 |
35 |
- |
90 Rb |
28 |
| 304LN |
S30453 |
A249, A688 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
| 304H |
A30409 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
7 or coarser |
90 Rb |
28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. |
| Grade |
Tensile Str |
Yield Str |
Elong |
Hardness |
| (MPa) min |
0.2% Proof |
(% in 50mm) min |
| |
(MPa) min |
|
Rockwell B (HR B) max |
Brinell (HB) max |
| 316 |
515 |
205 |
40 |
95 |
217 |
| 316L |
485 |
170 |
40 |
95 |
217 |
| 316H |
515 |
205 |
40 |
95 |
217 |
| |
Tensile Strength |
Yield Strength |
|
|
|
| Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
| 321 |
S32100 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
| 321H |
S32109 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
| Grade |
Density |
Melting Point |
Tensile Strength |
Yield Strength (0.2%Offset) |
Elongation |
| 310S |
7.9 g/cm3 |
1402 °C (2555 °F) |
Psi - 75000 , MPa - 515 |
Psi - 30000 , MPa - 205 |
40% |
| Grade |
Tensile Strength |
Yield Strength |
Elongation |
Hardness |
| (MPa) min |
0.2% Proof |
(% in 50mm) min |
| |
(MPa) min |
|
Rockwell C (HR C) |
Brinell (HB) |
| UNS S31803 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
| UNS S32205 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
| Grade |
Property |
Value |
2507/
S32750 |
Density (g/cm3) |
7.8 |
| 0.2% Offset Yield Strength |
80 ksi |
| Ultimate Tensile Strength |
116 ksi |
| 0.1% Offset Yield Strength 0.2% |
91 ksi |
| Elongation in 2 inches, % |
15% |
| Hardness Rockwell C |
32 |
| Impact Energy |
74 ft.-lbs |
| Density |
0.28 lb per inch3 |
| Modulus of elasticity |
28 x 10(6) psi |
| Coefficient of thermal expansion |
7.2 x 10(-6) per of at 68 to 212 of |
| Thermal conductivity |
8.7 Btu/hr ftoF |
| Heat capacity |
0.12 Btu/ lb oF |
| Electrical resistivity |
31.5 x10(-6) ohm-inch |
For comprehensive details and inquiries about our stainless steel rods, please reach out to Jiangsu Daxun Alloy Co., Ltd. We are here to provide the information you need.