| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
At DAXUN, we specialize in producing and stocking commercially pure titanium plates Gr1, Gr2, Gr3, and Gr4 (UNS), with varying thicknesses from 0.5 mm to 120 mm. Known as the 'workhorses' of the titanium family, these grades combine high strength, excellent ductility, and superior corrosion resistance, making them indispensable for myriad industrial applications.
Gr1, Gr2, Gr3, and Gr4 titanium plates are celebrated for their commercial purity, striking a superb balance between strength and ductility. With outstanding impact strength and weldability, these plates excel in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. They also showcase exceptional resistance to seawater and salt solutions.
Gr5 Ti-6Al-4V titanium alloy plate is a high-performance titanium alloy, comprising 90% titanium, 6% aluminum, and 4% vanadium. This α-β type alloy, where aluminum stabilizes the α phase and vanadium the β phase, is renowned for its excellent comprehensive performance and processability. TC4 titanium alloy exhibits superior room and high-temperature strength, exceptional creep resistance, thermal stability, high fatigue performance, *** growth resistance in seawater, and commendable fracture toughness and hot salt stress corrosion resistance. Furthermore, Gr5 Ti-6Al-4V titanium alloy plate offers excellent process plasticity and superplasticity, making it suitable for various processing, welding, and machining methods.
About the chemical composition of (Ti-6Al-4V) Grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of Grade 2 titaniumsheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of Grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
1. Cold-Rolled Titanium Plate: Crafted with precision through a meticulous plate-rolling process, the cold-rolled titanium plate undergoes its final transformation in the cold rolling stage. Offered in both work-hardened and heat-treated conditions, these sheets can be further processed mechanically or chemically to meet specific customer requirements. 2. Hot-Rolled Titanium Plate: Created through longitudinal and transverse rolling, our hot-rolled titanium plates boast thicknesses ranging from 3.0mm to 155mm. Delivered in a heat-treated state, these sheets can undergo creep flattening to eliminate internal stress and achieve exceptional flatness. Available as cut blanks or complex shaped parts, they can be tailored to your exact specifications.3. Forged Titanium Plate: Forged on a vertical hydraulic press and then rolled, or through open die forging followed by rolling, our forged titanium plates offer unparalleled durability. Standard slab dimensions include a maximum thickness of 580 mm, a width of up to 2000 mm, and lengths reaching 6000 mm. Exact dimensions and weights are customized in agreement with the customer.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a premier manufacturer and supplier of Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate from China. Our mission is to create the world's highest-performing titanium alloy plates. We offer rapid worldwide delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. DAXUN stocks Grade 5 alloy titanium plates (UNS R56400) in thicknesses from 0.5mm to 300mm. Plates with thicknesses from 0.5mm to 6.0mm are cold rolled, those from 6.0mm to 50mm are hot rolled, and plates above 50mm are forged. Grade 5 titanium plate (Ti-6Al-4V) is renowned as the 'workhorse' of titanium alloys, offering high strength, excellent ductility, superior corrosion resistance, and high-temperature resilience, making it highly sought after by both general and military industries. Our products comply with standards including ASTE, ASME, AMS, GB, GJB, MIL, JIS, and EN.
The versatile Ti-6Al-4V Grade 5 titanium plate is extensively utilized in aerospace, military, power industry, vehicle armor, precision rocket guidance components, and marine applications.
Grade 1
Today, DAXUN Alloys proudly stands as a leading global producer and supplier of premium Grade 1 titanium plates, setting benchmarks in quality and performance.
Pure Grade 1 titanium plate is celebrated for its outstanding ductility and cold formability, making it perfect for deep drawing applications. Known for its excellent general and seawater corrosion resistance, Grade 1 titanium resists oxidizing, neutral, and mildly reducing media, including chlorides. With low density (about half that of nickel-based alloys), a high strength-to-weight ratio, and exceptional corrosion resistance, Grade 1 titanium is an optimal choice for a broad range of harsh chemical conditions. This commercially pure titanium is the softest and most ductile, boasting good cold formability, excellent corrosion resistance, superior weldability, and impressive impact hardness.
As leading producers of ASTM B265 Titanium Gr 1 Plates, we offer a range that includes Titanium Gr 1 Sheets, Finished Plates, Coils, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, Perforated Plates, and more. Our comprehensive product line ensures that we meet all your titanium needs with unmatched quality.
Grade 2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the 'workhorse' of the commercially pure titanium family, blending high strength, excellent ductility, and superior corrosion resistance for a wide range of industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate offering an excellent balance of strength and ductility. It features good impact strength, ease of welding, and significant corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, it showcases remarkable resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an exceptional material for various applications. It effectively withstands stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for numerous industrial applications that demand good ductility and corrosion resistance.
DAXUN is a metal expert dedicated to both small and large titanium plate projects. As your reference point and long-term partner, DAXUN is ready to supply your business with titanium plates and provide any necessary technical assistance. Consider DAXUN not just a supplier of industrial pure titanium and titanium alloy plates, but a strategic partner committed to helping you overcome challenges and meet your project goals.
DAXUN's premier service center in China proudly maintains an extensive stock of top-tier titanium plate products, ensuring swift and efficient order processing. By offering essential processing, precision water jet cutting, and optimized plate nesting solutions, we deliver remarkable added value to our customers, significantly reducing their time and costs.
By committing to continuous investment in our state-of-the-art production facilities and securing robust capacity agreements with our esteemed partners, DAXUN guarantees exceptional titanium plate quality, leading the industry now and well into the future.
Reach out to DAXUN today to discover the most competitive pricing and detailed technical information on our superior titanium plates.
Q1: What products can you offer?
A: We offer a comprehensive range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, as well as the 300 series.
Additionally, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, 2507, and more. We also specialize in high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products to your specifications, ensuring they meet your exact requirements for utmost satisfaction.
Q3. How does your factory manage quality control?
Quality is our top priority. We maintain stringent quality control measures from the initial stages to the final product to ensure excellence.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation methods according to your requests.
Please note that any additional costs and differences will be borne by you.
Q5. How does your factory handle quality control?
Quality is paramount. We emphasize rigorous quality control procedures from start to finish.
Q6. How long is the delivery time?
A: The delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we expedite the process to ensure prompt delivery.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and 70% balance before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you provide DDQ (Deep Drawing Quality) material?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Let us know your application, and we will tailor the mechanical properties to your needs.
Q9: How can I get a sample?
A: We offer FREE samples for your evaluation. For small pieces, we may cover courier costs depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange a pickup for you.
){kind=link}