| Product Parameters: Stainless Steel rod | |
| Material | 2507 S32750 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
ASTM A276 Super Duplex Steel S32750 Round Bar, Super Duplex Steel Bar Supplier, Super Duplex Steel UNS S32760 Bright Bar, Super Duplex Steel 2507 Bar, Super Duplex Steel UNS S32950 Flat Bar, Austenitic Super Duplex Steel S32760 Round Bar, Hot Rolled Super Duplex Steel S32760 Round Bar, Super Duplex Steel S32760 Round Bar, Super Duplex Steel UNS S32750 Manufacturer from China.
For more information on stainless steel rods, please contact Daxun
2507 Stainless Steel Rod Chemical Composition
| Grade | Super Duplex 2507 |
| UNS Designation | S32750 |
| Carbon (C) Max. | 0.03 |
| Manganese (Mn) Max. | 1.2 |
| Phosphorous (P) Max. | 0.035 |
| *** (S) Max. | 0.02 |
| Silicon (Si) Max. | 0.8 |
| Chromium (Cr) | 24.0-26.0 |
| Nickel (Ni) | 6.0-8.0 |
| Molybdenum (Mo) | 3.0-5.0 |
| Nitrogen (N) | 0.24-0.32 |
| Iron (Fe) | Bal. |
| Copper (Cu) | 0.5 |
| Other Elements | - |
| Physical Properties of Super Duplex 2507 Alloys in the Annealed Condition at -20°F to +100°F | ||||||||||||||
| Tensile Strength | Yield Strength | |||||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
| Super Duplex 2507 | S32950 | A789, A790 | 100,000 | 690 | 100 | 70,000 | 485 | 70 | 20 | - | 30.5 Rc | - | - | - |
| Super Duplex 2507 | S32750 | A789, A790 | 116,000 | 800 | 116 | 80,000 | 550 | 80 | 15 | - | 32 Rc | 27.5 | 7.2 | 98 |
| Density, lb/in3 | 0.28 |
| Modulus of Elasticity, psi | 29.0x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 7.5 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 8 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microhm-in | 31.5 |
Our forming capabilities are supported by state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for the production of titanium rods. We also employ a unique hydroforming process for manufacturing parts.
We utilize advanced heat treatment furnace equipment for our stainless steel rod heat treatments, ensuring material stability and high performance.
Daxun Stainless Steel employs the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace to minimize impurities during the smelting process, thereby enhancing the performance of our finished stainless steel rods.
Our stainless steel products are fully certified and traceable. We supply the highest quality stainless steel to leading industries including aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you produce stainless steel grinding bars and rods?
Yes, we specialize in manufacturing SS grinding bars and rods that boast exceptional precision in dimension, roundness, and straightness. These attributes surpass those of standard polished stainless steel bars; however, please note that the processing costs are correspondingly higher.
Q1: What products can you offer?
A: We supply a broad range of steel types, including but not limited to 310S, 316L, 304, 304L, 201, 904L, 316H, and 316.
Additionally, we offer the 400 series, duplex stainless steel such as 2205, 2304, 2101, and 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you manufacture products according to my drawings?
Yes, we are fully capable of producing products based on your specific drawings to ensure they meet your utmost satisfaction.
Q3. How does your factory manage quality control?
Quality is our top priority. We maintain rigorous quality control procedures at every stage of production, from start to finish.
Q4. Can I request changes to the packaging and transportation methods?
Yes, we can accommodate changes to the form of packaging and transportation according to your specifications.
Please note, however, that any additional costs incurred during this process, including price differences, will be your responsibility.
Q5. How does your factory manage quality control?
Quality is our top priority. We maintain rigorous quality control procedures at every stage of production, from start to finish.
Q6. What is the typical delivery time?
A: Our standard delivery time is 7 to 20 working days following payment confirmation.
For urgent orders, we will expedite processing to meet your deadlines.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and 70% balance before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Do you offer Deep Drawing Quality (DDQ) materials?
A: Absolutely. Our DDQ materials are ideal for producing stainless steel pots, sinks, bowls, etc. Simply inform us of your specific application, and we will fine-tune the mechanical properties to match your requirements.
Q9: How can I obtain a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we may even cover the courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many others.
){kind=link}