| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For more information on stainless steel rods, please contact Daxun.
304 Stainless Steel Rod Chemical Composition
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*.
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod Mechanical Properties
Mechanical property requirements for annealed products as specified in ASTM A240 and ASME SA240.
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod Physical Properties
Physical properties for Type 304/304L stainless steel.
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our advanced forming capabilities include state-of-the-art radial forging machines, high-efficiency heat treatment furnaces, precise melting furnaces, and sophisticated rolling mills. We also employ a unique hydroforming process for manufacturing parts, ensuring top-tier product quality.
Our stainless steel rod heat treatment utilizes cutting-edge furnace equipment to ensure the material's stability and high performance.
At Daxun Stainless Steel, we leverage the pinnacle of smelting technology, utilizing the world's foremost vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These state-of-the-art processes meticulously minimize impurities, thereby significantly enhancing the performance and quality of our finished 304 Round Rod TISCO POSCO Baosteel Hot Rolled Stainless Steel, available in 10-20mm dimensions.
Our stainless steel products are not only fully certified but also meticulously traceable. We pride ourselves on supplying the finest quality stainless steel to top-tier industries, including aerospace, industrial manufacturing, medical technology, marine applications, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
DAUXN 304/304L Stainless Steel RODS are utilized in a diverse array of residential and commercial settings, including:
Can you do SS grinding bar & rod?
Absolutely! We specialize in crafting SS grinding bars & rods with unparalleled precision in dimension, roundness, and straightness, surpassing even stainless steel polished bars. However, please note that the advanced processing incurs higher costs.
Q1: What products can you offer?
A: We proudly supply a comprehensive range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L.
In addition, we offer 400 series, duplex stainless steel such as 2205, 2304, 2101, and 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products tailored to your unique drawings, ensuring utmost satisfaction.
Q3. How does your factory manage quality control?
Quality is our highest priority. We rigorously oversee quality control from start to finish, ensuring superior standards.
Q4. Can I request to change the form of packaging and transportation?
Certainly, we can modify the packaging and transportation forms to suit your preferences.
Please be aware that you will need to cover any additional costs and price differences incurred during this period.
Q5. How does your factory manage quality control?
Quality is our highest priority. We rigorously oversee quality control from start to finish, ensuring superior standards.
Q6. What is the delivery time?
A: Typically, delivery takes 7 to 20 working days after payment confirmation.
For urgent orders, we expedite processing to meet your deadlines.
Q7. What are your payment terms?
A: For small orders, we require 100% T/T advance or Western Union.
B: For larger orders, we accept a 30% T/T advance with the remaining 70% before shipment.
C: For significant orders, we accept a 100% Irrevocable LC at sight.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we specialize in DDQ materials, perfect for stainless steel pots, sinks, bowls, and more. Share your requirements, and we'll adjust the mechanical properties to meet your needs.
Q9: How can I get a sample?
A: We offer FREE samples for your evaluation and testing. For small pieces, we might cover the courier cost, depending on the situation.
Q10: To which countries have you exported?
A: Our stainless steel materials have been exported to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more countries.