| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For more information on our superior stainless steel rods, please contact Daxun.
304 Stainless Steel Rod Chemical Composition
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod Mechanical Properties
Mechanical property requirements for annealed product as specified in ASTM A240 and ASME SA240
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod Physical Properties
Physical properties for Type 304/304L stainless steel
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our capabilities include advanced radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods. We also offer a unique hydroforming process for manufacturing high-quality parts.
Our state-of-the-art heat treatment furnace ensures the stability and high performance of our stainless steel rods, providing you with materials that meet the highest industry standards.
At Daxun Stainless Steel, we harness the power of the world's foremost vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. This state-of-the-art technology allows us to significantly reduce impurities during the smelting process, thereby enhancing the performance and quality of our finished stainless steel rods. Our meticulous process ensures that every rod meets the highest standards of excellence, delivering unparalleled durability and reliability.
Our stainless steel products are fully certified and traceable. We supply only the highest quality stainless steel to leading industries including aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
DAUXN's 304/304L Stainless Steel Rods find extensive use in various residential and commercial sectors, including:
Can you do SS grinding bar & rod?
Yes, we can produce SS grinding bar & rod that boast precision in dimensions, exceptional roundness, and perfect straightness, surpassing the quality of typical stainless steel polished bars. Please note, the processing costs are higher.
Q1: What products can you offer?
A: We offer a comprehensive range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300.
We also supply 400 series and duplex stainless steels such as 2205, 2304, 2101, and 2507. Additionally, we provide high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products precisely to your drawings, ensuring they meet your utmost satisfaction.
Q3. How does your factory do regarding quality control?
Quality is our top priority. We maintain rigorous quality control measures from the start to the end of the production process.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation methods according to your specifications.
However, you will need to cover any additional costs and the price differences that arise during this process.
Q5. How does your factory do regarding quality control?
Quality is our top priority. We maintain rigorous quality control measures from the start to the end of the production process.
Q6. How long is the delivery time?
A: Delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite production to meet your deadlines.
Q7. What is your payment method?
A: 100% T/T in advance, Western Union (for small orders)
B: 30% T/T upfront, with the remaining 70% before shipment
C: 100% Irrevocable LC at sight (for large orders)
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Absolutely, we can provide DDQ material, suitable for making stainless steel pots, sinks, bowls, etc. Share your specific usage and we will tailor the mechanical properties to meet your needs.
Q9: How can I get a sample?
A: FREE samples are available for your review and testing. For small pieces, we might cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}