| Customization: | Available |
|---|---|
| Type: | Titanium Sheets |
| Application: | Industrial |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a premier global producer and supplier of top-grade Grade 1 titanium plates, known for their exceptional quality and performance.
Pure Grade 1 titanium plate boasts exceptional ductility and cold formability, ideal for deep drawing processes. Renowned for its outstanding general and seawater corrosion resistance, as well as its resilience against oxidizing, neutral, and mildly reducing media, including chlorides, Grade 1 titanium offers remarkable low density (approximately half that of nickel-based alloys), high strength-to-weight ratio, and superior corrosion resistance. These properties make it an excellent choice for challenging chemical environments. Commercially pure Grade 1 titanium is the softest and most ductile grade, offering excellent cold formability, superb corrosion resistance, and excellent weldability, along with good impact hardness.
As leading ASTM B265 Titanium Gr 1 Plate Producers, we specialize in Titanium Gr 1 Sheets, Finished Plates, Grade 1 Coil Suppliers, Pure Titanium Hot Rolled Plates, Cold Rolled Plates, ASTM B265 Gr 1 Sheets, Patterned Plates, Perforated Plates, and more. Based in China, we are renowned manufacturers of Titanium Grade 1 Sheets and Plates.
We ensure rapid and efficient delivery of Grade 1 titanium plate products to our customers. This speed is backed by robust support systems encompassing production capacity, information flow, logistics, and capital flow. For instance, Daxun's order data integrates seamlessly into our logistics system in real-time, enabling immediate action. Our processing center, strategically located near highways, rivers, and seas, ensures efficient scheduling, quick response, and effective storage and transportation linkages, guaranteeing timely completion of delivery tasks.
Grade 1 titanium plate is characterized by its low density and high ductility, making it ideal for weight-sensitive industries and deep drawing applications. Key industries utilizing titanium alloys include medical, chemical equipment, and aerospace sectors. Its strength and corrosion resistance make Grade 1 titanium perfect for marine, chemical processing, and desalination applications. Typical uses encompass oil and gas components, reaction and pressure vessels, piping systems, power generation, heat exchangers, linings, flue gas desulfurization systems, and numerous other industrial components. Common standards include ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, and AMS4972.
For Grade 1 Titanium Plates, the cold rolled thickness ranges from 0.3 mm to 6.0 mm, while hot rolled thickness spans 4.76 mm to 155 mm. These plates, produced via longitudinal and transverse rolling, can be supplied in hot rolled or heat-treated conditions. Creep flattening is available as a heat treatment to address internal stresses and specific flatness requirements. Additionally, plates can be supplied as cut blanks - complex shapes derived from a parent plate. Further processing can be tailored to customer requirements, utilizing either mechanical or chemical methods.
About the chemical composition of (Ti 6AL-4V) Grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of Grade 2 titanium sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of Grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is a renowned metal expert specializing in both small and large titanium plate projects. As a cornerstone and long-term ally for your business, DAXUN is committed to delivering top-tier titanium plates and comprehensive technical assistance. Beyond being a mere supplier of industrial pure titanium and titanium alloy plates, DAXUN positions itself as a strategic partner, dedicated to overcoming any challenges and fulfilling your specific needs, ensuring the successful realization of your project goals.
DAXUN's service center in China boasts an extensive inventory of titanium plate products, enabling swift order processing. With foundational processing capabilities, precision water jet cutting, and efficient plate nesting services, we offer significant value-added benefits to our customers, optimizing their time and reducing costs.
Our unwavering investment in state-of-the-art production facilities and strategic capacity agreements with our partners ensure that DAXUN remains a leader in titanium plate quality, both now and in the future.
Reach out to DAXUN today for the most up-to-date titanium plate prices and detailed technical information.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a renowned manufacturer and supplier of Ti-6Al-4V Grade 5 TC4 UNS R56400 alloy titanium plates in China, dedicated to producing world-class, high-performance titanium alloy plates. We offer rapid worldwide delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. Our inventory includes Grade 5 (UNS R56400) titanium plates with thicknesses ranging from 0.5mm to 300mm. Plates from 0.5mm to 6.0mm are cold rolled, from 6.0mm to 50mm are hot rolled, and those above 50mm are forged. Grade 5 titanium plates (Ti-6Al-4V) are the industry standard due to their high strength, excellent ductility, and superior corrosion and high-temperature resistance, making them ideal for both general and military applications. They comply with standards including ASTM, ASME, AMS, GB, GJB, MIL, JIS, and EN.
Ti-6Al-4V Grade 5 titanium plates are primarily used in aerospace, military, power generation, vehicle armor, rocket precision guidance, and marine industries.
Grade 1
Today, DAXUN Alloys stands as a leading global producer and supplier of high-quality Grade 1 titanium plates.
Pure Grade 1 titanium plates exhibit excellent ductility and cold formability, suitable for deep drawing processes. Known for their outstanding general and seawater corrosion resistance, these plates withstand oxidizing, neutral, and mildly reducing environments, including chlorides. Titanium's low density, about half that of nickel-based alloys, combined with a high strength-to-weight ratio and corrosion resistance, makes it perfect for various harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile, with excellent cold formability, superior corrosion resistance, excellent weldability, and good impact hardness.
Producers of ASTM B265 Titanium Grade 1 Plates, Titanium Grade 1 Sheets, and Finished Plates. Suppliers of Titanium Grade 1 Coils, Pure Titanium Hot Rolled Plates, Cold Rolled Plates, and Patterned Plates. Dealers of Titanium Grade 1 Perforated Plates and manufacturers of Titanium Grade 1 Sheets and Plates in China.
Grade 2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the standard bearer of the commercially pure titanium family, offering a superior balance of high strength, ductility, and excellent corrosion resistance, suitable for numerous industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate that balances strength and ductility perfectly. It exhibits good impact strength, is easily weldable, and offers excellent corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, it performs exceptionally well in seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an ideal material for various applications. Grade 2 Titanium Plate effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, it is the preferred alloy for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is your expert in both small and large titanium plate projects. As your reference point and long-term partner, DAXUN is ready to provide you with titanium plates and technical assistance to meet any challenges. Consider DAXUN not only as your supplier of industrial pure titanium and titanium alloy plates but also as your strategic partner, helping you achieve your project goals effortlessly.
At Jiangsu Daxun Alloy Co., Ltd., our premier service center in China boasts an impressive inventory of titanium plate products, ensuring rapid order fulfillment. Leveraging basic processing techniques, advanced water jet cutting, and meticulous plate nesting, we deliver unparalleled added value, thus saving our customers both precious time and significant costs.
Jiangsu Daxun Alloy Co., Ltd. stands at the pinnacle of titanium plate quality, thanks to our unwavering commitment to continuous investment in state-of-the-art production facilities. Our strategic capacity agreements with esteemed partners further solidify our position, ensuring that we remain industry leaders now and in the future.
Reach out to Jiangsu Daxun Alloy Co., Ltd. today to secure the most competitive titanium plate prices and access comprehensive technical information tailored to your needs.
Q1: What products can you offer?
A: Our offerings include a variety of high-quality steel types such as 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, we provide 300 and 400 series steel, as well as duplex stainless steels like 2205, 2304, 2101, and 2507. We also specialize in high-nickel alloys, including 904L, 800H, and 600H.
Q2: Can you produce the products according to my own drawings?
A: Absolutely, we can manufacture products precisely according to your drawings to ensure maximum satisfaction.
Q3: How does your factory ensure quality control?
A: Quality is our top priority. We meticulously manage quality control from the beginning to the end of the production process to guarantee superior products.
Q4: Can I request to change the form of packaging and transportation?
A: Yes, we can accommodate changes in packaging and transportation to meet your specific requests.
However, please note that any additional costs incurred during this period will be your responsibility.
Q5: How does your factory ensure quality control?
A: Quality is our top priority. We meticulously manage quality control from the beginning to the end of the production process to guarantee superior products.
Q6: How long is the delivery time?
A: Our standard delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we expedite production to meet your deadlines.
Q7: What are your payment terms?
A: 100% T/T in advance or Western Union for small orders.
B: 30% T/T deposit with the remaining 70% balance due before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) products?
A: Yes, we can produce DDQ materials suitable for stainless steel pots, sinks, bowls, etc. Simply inform us of your specific application, and we will tailor the mechanical properties to meet your requirements.
Q9: How can I get a sample?
A: We offer FREE samples for your evaluation. If you require a small piece, we may cover courier costs depending on the circumstances.
Q10: Which countries have you exported to?
A: We have successfully exported our stainless steel materials to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
){kind=link}