| Type: | Stainless Steel Bars |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | 410 |
| Certification: | ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS |
| Shape: | Round |
| Technique: | Hot Rolled |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Discover ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, Stainless Steel 410 Rod: A Comprehensive Range of Stainless Steel 410 Round Bars, SS 410 Round Bars, SS DIN 1.4006 Round Bars by Leading Manufacturers. Purchase Premium Stainless Steel 410 Bright Bars, 410 SS Polished Bars, SS 410 Rods from Top Suppliers and China's AISI SS 410 Round Bar Producers.
For Further Details on Stainless Steel Rods, Reach Out to Daxun
Chemical Composition of 410 Stainless Steel Rod
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our Forming Capabilities Feature State-of-the-Art Radial Forging Machines, Advanced Heat Treatment Furnaces, Melting Furnaces, and Rolling Mills for Titanium Rod Manufacturing. Additionally, our unique hydroforming process is ideal for part fabrication.
Our Advanced Heat Treatment Furnace Equipment Ensures the Stability and High Performance of Stainless Steel Rods.
Utilizing the World's Most Advanced Vacuum Induction Furnace, Vacuum Consumable Furnace, and Electroslag Furnace, Daxun Stainless Steel Minimizes Impurities During Smelting, Enhancing the Performance of Finished Stainless Steel Rods.
Our premium stainless steel products are not only fully certified but also meticulously traceable. We pride ourselves on delivering the highest quality stainless steel to preeminent industries, including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
For specific product dimensions, please visit our product pages. Contact us for custom size orders or quotes.
410 Stainless steel round bars are highly versatile, serving numerous sectors from construction to automotive parts. Given their wide range of applications, Jiangsu Daxun Alloy Co., Ltd. provides these bars in various grades and sizes. Our advanced, complimentary cutting service ensures precise customization to meet your specific requirements.
Can you manufacture stainless steel grinding bars and rods?
Yes, we specialize in producing stainless steel grinding bars and rods that boast precise dimensions, superior roundness, and straightness. While they surpass the quality of regular stainless steel polished bars, please note that the processing costs are higher.
Q1: What products can you offer?
A: We offer a wide variety of steel types such as 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series.
We also provide 400 series stainless steel and duplex stainless steel like 2205, 2304, 2101, 2507, and more. Additionally, we supply high-nickel alloys such as 904L, 800H, and 600H.
Q2: Can you produce products according to my own drawings?
Yes, we can manufacture products according to your specific drawings to ensure they meet your exact requirements.
Q3: How does your factory maintain quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures from start to finish.
Q4: Can I request changes to the packaging and transportation form?
Yes, we can modify the packaging and transportation methods according to your requests.
However, any additional costs and differences incurred during this period will be your responsibility.
Q5: How does your factory ensure quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures from start to finish.
Q6: What is your delivery time?
A: Our delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite the process to ensure timely delivery.
Q7: What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and 70% balance before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, our material is suitable for deep drawing applications like stainless steel pots, sinks, and bowls. Please inform us of your specific usage, and we will adjust the mechanical properties accordingly.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation and testing. For small pieces, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Suppliers with verified business licenses
Audited Supplier 