| Type: | Stainless Steel Bars |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | 310 310S S31008 |
| Certification: | ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS |
| Shape: | Round |
| Technique: | Hot Rolled |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys is a renowned manufacturer of premium-quality SS 310/310S Round Bars, celebrated for their remarkable attributes. Stainless Steel 310/310S Round Bars boast an austenitic composition based on chromium and nickel. These round bars exhibit outstanding properties such as durability, flexibility, workability, machinability, weldability, ductility, fabricability, exceptional strength, and hardness. They are indispensable in industrial chemistry and nut manufacturing, prized for their anti-corrosion characteristics. Capable of withstanding extreme temperatures, these rods maintain stability even at annealing temperatures without deformation. We offer Stainless Steel Round Bars to our esteemed clients at competitive market prices. Customization in finishes, lengths, and shapes is available to cater to specific requirements. Our circular bars are ideal for a wide range of industrial applications.
For comprehensive information on stainless steel rods, please contact Daxun.
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our forming capabilities include cutting-edge radial forging machines, advanced heat treatment and melting furnaces, and rolling mills for manufacturing titanium rods. Additionally, we employ a unique hydroforming process for part fabrication.
Our stainless steel rod heat treatment process utilizes advanced furnace equipment to ensure the material's stability and high performance.
9799d8a7
Our stainless steel products boast full certification and traceability, ensuring the pinnacle of quality and reliability. We proudly supply top-tier stainless steel to leading industries such as aerospace, industrial, medical, marine, and military sectors, meeting their stringent standards.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and pipes exhibit outstanding resistance to both corrosion and heat, even in the most challenging environments.
Daxun Alloys' stainless steel round bars are highly versatile, finding use in various sectors from construction to automotive. Offering a range of grades and sizes, we provide advanced cutting services to precisely meet your needs.
Our premium stainless steel round bars are available in an extensive array of sizes to suit all your project needs. Choose the specific grade of steel, and we'll deliver bars in lengths spanning from 500mm to an impressive 6 meters, and diameters ranging from a delicate 3mm to a robust 500mm. Whether you need metric or imperial measurements, we've got you covered with utmost precision.
Need a custom size? No problem at all! We offer unlimited free cuts to length, ensuring the perfect fit for your unique specifications. Utilizing advanced bandsaw technology, we guarantee exceptional accuracy and repeatability with every cut. Simply specify your requirements when placing your order, and we'll handle the rest with precision and care.
Can you manufacture SS grinding bars and rods?
Absolutely, we specialize in crafting SS grinding bars and rods with exceptional precision in dimension, roundness, and straightness. These are superior to standard stainless steel polished bars, though they come at a higher processing cost.
Q1: What products can you offer?
A: We offer a broad range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series,
400 series, and duplex stainless steels such as 2205, 2304, 2101, 2507, etc. We also provide high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce products according to my own drawings?
Yes, we can customize products to match your drawings, ensuring they meet your exact specifications and satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We are committed to stringent quality control measures from the very start to the final stages of production.
Q4. Can I request changes in packaging and transportation?
Yes, we can modify the packaging and transportation methods according to your requests.
However, you will need to cover any additional costs and differences incurred during this period.
Q5. How does your factory ensure quality control?
Quality is paramount. We consistently prioritize quality control throughout the entire manufacturing process.
Q6. What is the delivery time?
A: The delivery time is typically 7-20 working days after payment confirmation.
If your order is urgent, we will expedite the production process to meet your timeline.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T in advance and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) steel?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Let us know your specific use, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I get a sample?
A: We offer FREE samples for your evaluation. For small pieces, we may cover the courier cost, depending on the circumstances.
Q10: Which countries have you exported to?
A: We have successfully exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}