Type: | Titanium Pipes |
---|---|
Application: | Industrial, Medical |
Technique: | Hot Rolled |
Grade: | Gr1 Gr2 Gr5 Gr7 Gr9 Gr12 6al-4V 3al-2.5V |
Shape: | Round |
Standards: | Astmb861 B862 B338 ASME Sb861 Sb862 Sb338 |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Gr1 Gr2 Gr5 Gr7 Gr9 Gr12 6al-4V 3al-2.5V Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Grades | Commercially pure titanium Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
Titanium welded pipe - φ1.0mm to φ1219mm | |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
Titanium pipe Form TA2 | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
Marking Gr1 Gr2 Gr5 Gr7 Gr9 Gr12 6al-4V 3al-2.5V | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
Gr1 Gr2 Gr5 Gr7 Gr9 Gr12 6al-4V 3al-2.5V Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
Gr1 Gr2 Gr5 6AL-4V 3AL-2.5V Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Titanium Welded Tube: Diameter ranges from 6.0mm to 1219mm, wall thickness ranges from 0.3mm to 30mm (depending on diameter), length up to 25000mm, made from Gr1 titanium tube. Welded tubes are made from flat rolled billets (tube blanks) on electric tube welding machines using automatic tungsten inert gas (argon) welding, and heat treated on the mill line. Mechanical tests, geometric measurements, 100% ultrasonic and eddy current testing, pneumatic or hydrostatic testing are performed before the finished titanium welded tubes are packaged according to customer specifications. Manufacturing technology as well as inspection and testing equipment ensure that thin wall welded tubes meet ASTM B 338 and ASME SB 338 specifications.
Titanium Pipes and Tubing are extensively applied in extremely corrosive conditions in the below Industries:
Daxun performs several quality assurance tests, these tests include flattening test, flaring test, ultrasonic flaw detection test, pitting and resistance test, mechanical test, hardness test, material positive identification, expansion test, etc. All these tests ensure that the Grade 1 Titanium Welded Pipe and Grade 1 Titanium Seamless Pipe materials are suitable for the required application. During the production process, we measure the diameter, thickness and surface of the products. Our standard delivery time is 5-7 days and the delivery time for special size products is 15-20 days.
About the chemical composition of(Ti 6AL-4V) grade 5 titanium tube
Chemical Composition: | |||
Symbol | Element | Min % | Max % |
Al | Aluminum | 5.50% | 6.75% |
V | Vanadium | 3.50% | 4.50% |
Fe | Iron | 0.30% | |
O | Oxygen | 0.20% | |
C | Carbon | 0.08% | |
N | Nitrogen | 0.05% | |
H | Hydrogen | 0.01% | |
Y | Yttrium | 0.01% | |
Other, each | 0.10% | ||
Other, total | 0.40% | ||
Ti | Titanium | Remainder |
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % |
About the chemical composition of grade 2 titanium tube
Element | Weight % |
C | ≤0.08 |
O | ≤0.25 |
N | ≤0.03 |
H | ≤0.015 |
Fe | ≤0.30 |
*OEE | ≤0.10 |
*OET | ≤0.40 |
Ti | Remaining |
About the mechanical properties of grade 2 titanium tube
Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
psi | MPa | ksi | psi | MPa | ksi | % | |||||||
Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
50,000 |
Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
Fe | 0.2 | ||
O | 0.18 | ||
C | 0.08 | ||
N | 0.03 | ||
H | 0.015 | ||
Ti | Balance |
Density | |
lb/in3 | g/cm3 |
0.163 | 4.51 |
Tensile Strength | |
ksi | MPa |
35 min | 240 min |
Yield Strength | |
ksi | MPa |
20 min | 138 min |
Hardness | |
70 HRC max | |
Elongation | |
24% min |
Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
---|---|---|---|
Al | 2.5 | 3.5 | |
V | 2.0 | 3.0 | |
Fe | 0.25 | ||
O | 0.15 | ||
C | 0.08 | ||
N | 0.03 | ||
H | 0.015 | ||
Ti | Balance |
CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.50 g/cc | 0.163 lb/in³ | |
a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
Mechanical Properties | Metric | English | Comments |
Hardness, Brinell | 120 | 120 | annealed |
Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
Hardness, Rockwell B | 70 | 70 | annealed |
Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
Elongation at Break | 24% | 24% | |
25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
Reduction of Area | 35% | 35% | |
Tensile Modulus | 103 GPa | 14900 ksi | |
Compressive Modulus | 110 GPa | 16000 ksi | |
Poissons Ratio | 0.37 | 0.37 | |
Shear Modulus | 45.0 GPa | 6530 ksi | |
Charpy Impact | 310 J | 229 ft-lb | V-notch |
Impact Test | 136 J | 100 ft-lb | Impact Strength |
Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
0.8 | 0.8 | Ti sliding on Ti; 40 m/min |
CP GR2 Titanium tube PHYSICAL PROPERTIES | |
Density | Magnetic Permeability |
0.163 lbs/in-3 | Nonmagnetic |
4.51 g/cm-3 | Electrical Resistivity |
Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
1680°F | 0.53 µΩ/m |
915°C | Elastic Modulus |
Thermal Conductivity | 15.2-17.4 Msi |
12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % | |
Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
Compressive Yield Strength | 970 MPa | 141000 psi | |
Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
Poisson's Ratio | 0.342 | 0.342 | |
Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
Shear Modulus | 44 GPa | 6380 ksi | |
Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
Electrical Properties | |||
Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
Thermal Properties | |||
CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
Solidus | 1604 °C | 2920 °F | |
Liquidus | 1660 °C | 3020 °F | |
Beta Transus | 980 °C | 1800 °F |
This is the most often used titanium tube for industrial applications, providing a superb balance of moderate strength and reasonable ductility. It offers excellent corrosion resistance in both highly oxidising and slightly reducing conditions (including chlorides). It provides good corrosion protection in the chemical and offshore industries, as well as aircraft manufacture, where strength and ease of forming are required. It's also utilised in heat exchangers, hypochlorite systems, fire water systems, ballast water systems, industrial and aerospace components, CPI equipment, and pipes.
Q1: What products can you offer?
A: We can offer you general steel types like 310S, 316L,304.304L.201,904L, 316H, 316,316L 300and
400 series, and duplex stainless steel like 2205, 2304,2101,2507,etc. 904L, 800H, 600H high-nickel alloy.
Q2. Can you produce the products according to my own drawings?
Yes, we can produce the products according to your drawings that will be most satisfy you.
Q3. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q4. Can I request to change the form of packaging and transportation?
Yes, We can change the form of the packaging and transportation according to your request,
but you have to bear their own costs incurred during this period and the spreads.
Q5. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q6. How long is the delivery time?
A: 7~20 working days after confirming the payment.
If the order is urgent, we will push our workshop finish in advance.
Q7. What is your Payment?
A: 100% T/T advance, Western Union (For Small Order)
B: 30% T/T and balance 70% before the shipment
C: 100% Irrevocable LC at sight (For Big Order)
Q8: Can you make DDQ ( Deep Drawing Quality)?
A: Yes, we can. Our material can be used for stainless steel pots, stainless steel sinks, stainless steel bowls etc. U can tell us your usage, and we will adjust the mechanical propertise to meet your requirement.
Q9: How to get a sample?
A: FREE samples are available for your checking and testing.If you require for a small piece,we can afford courier cost,it depends.
Q10:Which country have you exported to?
A:Until now,we have exported stainless steel material to following countries: Vietnam,Thailand,Turkey,Russia,Maroc,Korea,India,Pakistan,UAE,Ukraine and so on.
Q11: How to visit your company?
A:By flight to Guangzhou Baiyun International airport,then we will pick you up.
Suppliers with verified business licenses