Product Parameters: Stainless Steel rod | |
Material | 201 |
Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
Round Bars | Outside Diameter in the range of 4mm to 500mm |
Bright Bars | Outside Diameter in the range of 4mm to 100mm |
Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
Length | 1 to 6 Meters, Custom Cut Lengths |
Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
Laboratory Test Certificate from Govt. Approved Lab. | |
Under Third Party Inspection | |
Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition 201 Stainless steel rod
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*
Element | 201 |
Carbon | 0.15 |
Chromium | 16.0-18.0 |
Nickel | 3.5-5.5 |
Manganese | 5.50-7.50 |
Silicon | 1.00 |
Nitrogen | 0.25 |
Phosphorus | 0.060 |
Sulfur | 0.030 |
Mechanical Properties 201 Stainless steel rod
Mechanical property requirements for annealed product as specified in ASTM A240 and ASME SA240
Property | 201 |
Yield Strength, min. (ksi) | 45 |
Tensile Strength, min. (ksi) | 95 |
Elongation, min. (%) | 40 |
Hardness, max. (Rb) | 100 |
Mechanical property requirements for cold worked flat rolled products as specified in 201 Stainless steel rod
Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
<0.015 in. | ≥0.015 in. | |||
¼ Hard | 75 | 125 | 25 | 25 |
½ Hard | 110 | 150 | 15 | 18 |
¾ Hard | 135 | 175 | 10 | 12 |
Full Hard | 140 | 185 | 8 | 9 |
Physical Properties
Physical properties for Type 201 stainless steel rod
Property | 201 |
Density, lb/in3 | 0.283 |
Modulus of Elasticity, psi | 28.6 x 106 |
Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
Specific Heat, Btu/lb ˚F | 0.12 |
Electrical Resistivity, Microohm-in | 27.0 |
Forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces and rolling mills for manufacturing titanium rods, as well as a unique hydroforming process for manufacturing parts.
Stainless steel rod heat treatment uses advanced heat treatment furnace equipment to ensure the stability and high performance of the material.
Daxun Stainless Steel uses the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace to reduce impurities during the smelting process and improve the performance of the finished stainless steel rods.
Our stainless steel products are fully certified and traceable. We supply the highest quality stainless steel to leading industries including aerospace, industrial, medical, marine and military.
Tensile Strength | Yield Strength | |||||||||||
Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
Grade | Tensile Str | Yield Str | Elong | Hardness | |
(MPa) min | 0.2% Proof | (% in 50mm) min | |||
(MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
316 | 515 | 205 | 40 | 95 | 217 |
316L | 485 | 170 | 40 | 95 | 217 |
316H | 515 | 205 | 40 | 95 | 217 |
Tensile Strength | Yield Strength | ||||||||
Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
(MPa) min | 0.2% Proof | (% in 50mm) min | |||
(MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
Grade | Property | Value |
2507/ S32750 |
Density (g/cm3) | 7.8 |
0.2% Offset Yield Strength | 80 ksi | |
Ultimate Tensile Strength | 116 ksi | |
0.1% Offset Yield Strength 0.2% | 91 ksi | |
Elongation in 2 inches, % | 15% | |
Hardness Rockwell C | 32 | |
Impact Energy | 74 ft.-lbs | |
Density | 0.28 lb per inch3 | |
Modulus of elasticity | 28 x 10(6) psi | |
Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
Thermal conductivity | 8.7 Btu/hr ftoF | |
Heat capacity | 0.12 Btu/ lb oF | |
Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you do SS grinding bar & rod?
Yes we can do SS grinding bar & rod featuring precise dimension, roundness and straightness, superior to stainless steel polished bars, but the processing cost is also higher.
Q1: What products can you offer?
A: We can offer you general steel types like 310S, 316L,304.304L.201,904L, 316H, 316,316L 300and
400 series, and duplex stainless steel like 2205, 2304,2101,2507,etc. 904L, 800H, 600H high-nickel alloy.
Q2. Can you produce the products according to my own drawings?
Yes, we can produce the products according to your drawings that will be most satisfy you.
Q3. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q4. Can I request to change the form of packaging and transportation?
Yes, We can change the form of the packaging and transportation according to your request,
but you have to bear their own costs incurred during this period and the spreads.
Q5. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q6. How long is the delivery time?
A: 7~20 working days after confirming the payment.
If the order is urgent, we will push our workshop finish in advance.
Q7. What is your Payment?
A: 100% T/T advance, Western Union (For Small Order)
B: 30% T/T and balance 70% before the shipment
C: 100% Irrevocable LC at sight (For Big Order)
Q8: Can you make DDQ ( Deep Drawing Quality)?
A: Yes, we can. Our material can be used for stainless steel pots, stainless steel sinks, stainless steel bowls etc. U can tell us your usage, and we will adjust the mechanical propertise to meet your requirement.
Q9: How to get a sample?
A: FREE samples are available for your checking and testing.If you require for a small piece,we can afford courier cost,it depends.
Q10:Which country have you exported to?
A:Until now,we have exported stainless steel material to following countries: Vietnam,Thailand,Turkey,Russia,Maroc,Korea,India,Pakistan,UAE,Ukraine and so on.