| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys stands as a reputable manufacturer of high-quality SS 310 / 310S Round Bars, boasting a myriad of exceptional characteristics. These austenitic stainless steel round bars, composed primarily of chromium and nickel, offer outstanding durability, flexibility, workability, machinability, weldability, ductility, fabricability, high strength, and hardness. Renowned for their anti-corrosion properties, SS310/310S Round Bars/Rods are indispensable in industrial chemistry and nut manufacturing. They excel under extreme temperatures and can be utilized at annealing temperatures without deformation. We proudly offer these stainless steel round bars to our esteemed clients at competitive market prices. Additionally, we provide customization options in various finishes, lengths, and shapes to meet specific client requirements, ensuring versatile application in industrial settings.
For more information on stainless steel rods, please contact Daxun
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rod manufacturing, along with a unique hydroforming process for part fabrication.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods, maintaining the highest material standards.
At Jiangsu Daxun Alloy Co., Ltd., our stainless steel production harnesses the power of the world's most advanced smelting technologies. Our use of state-of-the-art vacuum induction furnaces, vacuum consumable furnaces, and electroslag furnaces ensures the highest purity levels by significantly reducing impurities during the smelting process. This meticulous approach in our production line elevates the overall performance and durability of our ASTM A276 High Temperature Resistance 310S Stainless Steel Rod Hot Rolled products, setting a benchmark in excellence and quality.
Our stainless steel products are not only fully certified and traceable but also of the highest caliber. We proudly supply premium stainless steel to cutting-edge industries including aerospace, industrial sectors, medical fields, marine applications, and military operations.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and Pipes deliver outstanding resistance to both corrosion and heat, thriving even in the harshest environments.
Stainless steel round bars serve a multitude of purposes across various industries, from construction to automotive parts. Recognizing the diverse needs, Daxun Alloy offers stainless steel round bars in a broad array of grades and sizes. Our advanced cutting service ensures precision and accuracy, fulfilling your specifications with excellence every time.
Easily order our premium stainless steel round bars available in an extensive range of sizes tailored to your specific needs. Choose the grade of steel you require, and we will supply bars in lengths spanning from 500mm to an impressive 6 meters, with diameters from a precise 3mm to a robust 500mm. Whether you prefer metric or imperial sizes, we have you covered, ensuring a seamless ordering experience.
Need a custom size? No problem at all! Enjoy unlimited complimentary cuts to length, ensuring you receive exactly what you need. Our precision state-of-the-art bandsaws guarantee accuracy and repeatability with every cut. Simply provide your specifications when placing your order, and we will meticulously fulfill your requirements.
Can you manufacture Stainless Steel (SS) grinding bars & rods?
Absolutely! We specialize in SS grinding bars & rods that excel in precise dimensions, roundness, and straightness, offering superior performance compared to stainless steel polished bars. Please note, the processing cost is higher.
Q1: What products can you offer?
A: We offer a wide range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 and
400 series. Additionally, we provide duplex stainless steels like 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, 600H.
Q2. Can you produce the products according to my drawings?
Yes, we can manufacture products per your drawings to ensure they meet your highest satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We maintain stringent quality control throughout the entire manufacturing process, from start to finish.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can adapt the packaging and transportation methods to suit your specific requests,
though you will need to cover any additional costs and differences incurred.
Q5. How does your factory handle quality control?
Quality is our top priority. We maintain stringent quality control throughout the entire manufacturing process, from start to finish.
Q6. What is your delivery time frame?
A: Delivery typically takes 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite production in our workshop to meet your timelines.
Q7. What are your payment terms?
A: 100% T/T in advance, Western Union (for smaller orders)
B: 30% T/T upfront with 70% balance before shipment
C: 100% Irrevocable LC at sight (for larger orders)
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Share your specific usage, and we will adjust the mechanical properties accordingly.
Q9: How can I obtain a sample?
A: FREE samples are available for inspection and testing. For small pieces, we may cover the courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}