Product Parameters: Stainless Steel rod |
Material |
904L 1.4539 N08904 Super Austenite Round Bar |
Specifications |
ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
Dimensions |
EN, DIN, JIS, ASTM, BS, ASME, AISI |
Round Bars |
Outside Diameter in the range of 4mm to 500mm |
Bright Bars |
Outside Diameter in the range of 4mm to 100mm |
Hex Bars |
18mm - 57mm (11/16″ to 2-3/4″) |
Finish |
Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
Length |
1 to 6 Meters, Custom Cut Lengths |
Form |
Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
Marking & Traceability |
Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
Test Certificate |
Manufacturer Test Certificate according to EN 10204 3.1 B |
Laboratory Test Certificate from Govt. Approved Lab. |
Under Third Party Inspection |
Testing & Inspection |
Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Hot Rolled Stainless Steel Rods
Our stainless steel rods and bars undergo meticulous heating and rolling through multiple passes in a state-of-the-art rolling mill. Boasting comprehensive specifications, their performance adheres strictly to industry standards and requirements.
Cold Drawn Bright Stainless Steel Rods
Our cold-drawn stainless steel rods are crafted under precise cold working conditions. They feature an impeccably smooth surface, with options for additional polishing and grinding for enhanced finish.
Forged Stainless Steel Rods and Bars
Forged stainless steel rods undergo repeated forging processes to significantly enhance their mechanical properties and strength, ensuring superior performance and durability.
Distinguished General Properties
Daxun Alloys offers a comprehensive network of service centers stocking an extensive range of stainless steel bar products for immediate supply. We specialize in custom-sized stainless steel bars and can establish a stocking program for orders below the factory minimum to ensure rapid turnaround. Our inventory includes round bars from 1/16" to 26" in diameter, available in a wide array of grades such as 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.
Premier Additional Services
Our vast inventory includes our proprietary processed bar grade: stainless steel round bars treated to consistent standards for enhanced machinability, ultimately reducing the total cost per part. With cutting-edge stainless steel bar processing machinery, Daxun Alloys meets precise customer specifications with unmatched precision.
1. Heat Treatments: Daxun can perform specialized heat treatments on our stainless steel bars, contingent on the metal's chemistry. 2. Positive Material Identification (PMI): Additional PMI testing may be conducted in-house or via an independent laboratory to ensure material integrity. 3. Ultrasonic Testing (UT): Utilizing high-frequency sound energy, UT aids in defect detection, evaluation, and dimensional measurement, ensuring the utmost quality of our products.
![904L Stainless Steel Bar En 1.4539 φ 80-200mm High Chemical Resistance Chemical Parts 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
For comprehensive information on our premium stainless steel rods, please reach out to Daxun.
904L Stainless Steel Rod Chemical Composition
Element |
% Present (in product form) |
Carbon (C) |
0.02 |
Silicon (Si) |
0.7 |
Manganese (Mn) |
2 |
Phosphorous (P) |
0.03 |
Sulfur (S) |
0.01 |
Chromium (Cr) |
19.00 - 21.00 |
Nickel (Ni) |
24.00 - 26.00 |
Nitrogen (N) |
0.15 |
Molybdenum (Mo) |
4.00 - 5.00 |
Copper (Cu) |
1.20 - 2.00 |
Iron (Fe) |
Balance |
904L Stainless Steel Rod Mechanical Properties
Product Form |
|
|
|
|
C |
H |
P |
L |
L |
TW/TS |
Thickness (mm) Max. |
8 |
13.5 |
75 |
160 |
2502) |
60 |
Yield Strength |
Rp0.2N/mm2 |
2403) |
2203) |
2203) |
2304) |
2305) |
2306) |
Rp1.0N/mm2 |
2703) |
2603) |
2603) |
2603) |
2603) |
2503) |
Tensile Strength |
RmN/mm2 |
530 - 7303) |
530 - 7303) |
520 - 7203) |
530 - 7304) |
530 - 7305) |
520 - 7206) |
Elongation min. in % |
Jmin(Longitudinal) |
- |
100 |
100 |
100 |
- |
120 |
Jmin(Transverse) |
- |
60 |
60 |
- |
60 |
90 |
904L Stainless Steel Rod Physical Properties
Density at 20°C kg/m3 |
8 |
Thermal Conductivity W/m K at |
20°C |
12 |
Modulus of Elasticity kN/mm2 at |
20°C |
195 |
200°C |
182 |
400°C |
166 |
500°C |
158 |
Specific Thermal Capacity at 20°C J/kg K |
450 |
Electrical Resistivity at 20°C mm2/m |
1 |
Daxun's Premier Stainless Steel Rod Manufacturing Capabilities
Our forming capabilities are unparalleled, featuring cutting-edge radial forging machines, advanced heat treatment furnaces, high-efficiency melting furnaces, and precision rolling mills for manufacturing titanium rods. We also employ a unique hydroforming process for crafting specialized parts.
Daxun's Advanced Heat Treatment Furnaces
Our state-of-the-art heat treatment furnaces ensure the stability and high performance of stainless steel rods through advanced thermal processing techniques.
Daxun's Superior Smelting Abilities
Daxun Stainless Steel leverages the world's most advanced vacuum induction furnaces, vacuum consumable furnaces, and electroslag furnaces to minimize impurities during smelting, significantly enhancing the performance and quality of our stainless steel rods.
![904L Stainless Steel Bar En 1.4539 φ 80-200mm High Chemical Resistance Chemical Parts 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
Allow us to be your reliable and trusted stainless steel rod supplier
Our premium stainless steel products come with full certification and traceability. We are proud suppliers of top-tier stainless steel to key industries such as aerospace, industrial, medical, marine, and military sectors.
![904L Stainless Steel Bar En 1.4539 φ 80-200mm High Chemical Resistance Chemical Parts 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
Discover the mechanical properties of various grades of our high-quality stainless steel bars.
|
Tensile Strength |
Yield Strength |
|
|
|
|
|
|
Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
Grain Size Req. |
Max. Hardness |
Modulus of Elasticity (x106 psi) |
304 |
S30400 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
304L |
S30403 |
A270 A312 |
70,000 |
485 |
70 |
25,000 |
170 |
25 |
35 |
- |
90 Rb |
28 |
304LN |
S30453 |
A249, A688 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
304H |
A30409 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
7 or coarser |
90 Rb |
28 |
The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. |
Grade |
Tensile Str |
Yield Str |
Elong |
Hardness |
(MPa) min |
0.2% Proof |
(% in 50mm) min |
|
(MPa) min |
|
Rockwell B (HR B) max |
Brinell (HB) max |
316 |
515 |
205 |
40 |
95 |
217 |
316L |
485 |
170 |
40 |
95 |
217 |
316H |
515 |
205 |
40 |
95 |
217 |
|
Tensile Strength |
Yield Strength |
|
|
|
Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
321 |
S32100 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
321H |
S32109 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
Grade |
Density |
Melting Point |
Tensile Strength |
Yield Strength (0.2%Offset) |
Elongation |
310S |
7.9 g/cm3 |
1402 °C (2555 °F) |
Psi - 75000 , MPa - 515 |
Psi - 30000 , MPa - 205 |
40% |
Grade |
Tensile Strength |
Yield Strength |
Elongation |
Hardness |
(MPa) min |
0.2% Proof |
(% in 50mm) min |
|
(MPa) min |
|
Rockwell C (HR C) |
Brinell (HB) |
UNS S31803 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
UNS S32205 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
Grade |
Property |
Value |
2507/
S32750 |
Density (g/cm3) |
7.8 |
0.2% Offset Yield Strength |
80 ksi |
Ultimate Tensile Strength |
116 ksi |
0.1% Offset Yield Strength 0.2% |
91 ksi |
Elongation in 2 inches, % |
15% |
Hardness Rockwell C |
32 |
Impact Energy |
74 ft.-lbs |
Density |
0.28 lb per inch3 |
Modulus of elasticity |
28 x 10(6) psi |
Coefficient of thermal expansion |
7.2 x 10(-6) per of at 68 to 212 of |
Thermal conductivity |
8.7 Btu/hr ftoF |
Heat capacity |
0.12 Btu/ lb oF |
Electrical resistivity |
31.5 x10(-6) ohm-inch |
For comprehensive information on our stainless steel rods, please reach out to Daxun today.
![904L Stainless Steel Bar En 1.4539 φ 80-200mm High Chemical Resistance Chemical Parts 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
![904L Stainless Steel Bar En 1.4539 φ 80-200mm High Chemical Resistance Chemical Parts 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
![904L Stainless Steel Bar En 1.4539 φ 80-200mm High Chemical Resistance Chemical Parts 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)