| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition of 201 Stainless Steel Rod
Chemical composition (wt%) limits conforming to ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties of 201 Stainless Steel Rod
Mechanical properties for the annealed product as per ASTM A240 and ASME SA240 specifications
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
Mechanical property requirements for cold worked flat rolled products align with the rigorous standards set forth in 201 Stainless Steel Rod
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Physical Properties
Physical properties of Type 201 stainless steel rod showcase its superior durability and versatility.
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
With cutting-edge radial forging machines, sophisticated heat treatment furnaces, high-efficiency melting furnaces, and advanced rolling mills, Daxun excels in manufacturing titanium rods. Our unique hydroforming process further ensures precision in manufacturing intricate parts.
Our advanced heat treatment furnace technology ensures the stainless steel rods achieve optimal stability and high performance.
Utilizing the world's leading vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun Stainless Steel significantly reduces impurities, thereby enhancing the overall performance and quality of our stainless steel rods.
Our stainless steel products are fully certified and traceable. We supply the highest quality stainless steel, including the renowned 201 Stainless Steel Round Rod TISCO POSCO Baosteel φ 3.0mm-350mm Corrosion Resistant, to leading industries such as aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you do SS grinding bar & rod?
Yes, we specialize in producing SS grinding bars and rods. These products boast precise dimensions, impeccable roundness, and exceptional straightness, setting them apart from standard stainless steel polished bars. However, please note that the enhanced processing incurs higher costs.
Q1: What products can you offer?
A: We provide a diverse range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and the entire 300 series.
Additionally, we offer the 400 series and duplex stainless steels like 2205, 2304, 2101, and 2507. High-nickel alloys such as 904L, 800H, and 600H are also available.
Q2. Can you produce the products according to my own drawings?
Yes, we can custom-produce products based on your drawings, ensuring they meet your highest satisfaction.
Q3. How does your factory do regarding quality control?
Quality is our top priority. We maintain stringent quality control measures throughout the entire production process, from inception to completion.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can accommodate requests to alter packaging and transportation forms to suit your needs.
However, please note that any additional costs incurred during this period will be borne by you.
Q5. How does your factory do regarding quality control?
Quality is our top priority. We maintain stringent quality control measures throughout the entire production process, from inception to completion.
Q6. How long is the delivery time?
A: Delivery is typically within 7 to 20 working days after payment confirmation.
If the order is urgent, we can expedite processing in our workshop to meet your timeline.
Q7. What is your Payment?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront, with the remaining 70% due before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, etc. Provide us your specific use case, and we will adjust the mechanical properties accordingly.
Q9: How to get a sample?
A: FREE samples are available for your evaluation. For small sample pieces, we may cover courier costs, depending on the situation.
Q10: Which country have you exported to?
A: To date, we have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and several other countries.
){kind=link}