| Customization: | Available |
|---|---|
| Material: | TA2 Titanium Alloy |
| Color: | Silver |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Ti-6Al-4V Grade 5 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 5 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 5-Ti-6Al4V- TC4- USN 56400 |
| Grade 5 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 5 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ6.0mm to φ1219mm | |
| Grade 5 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 5 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form Ti-6Al-4V | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TC4 1.37165 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 5 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 5 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 5 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 5 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 5 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 5 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 5 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 5 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 5 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 5 titanium tubes are renowned for their exceptional performance in the following industries, even under extreme corrosive conditions:
At Daxun, we conduct rigorous quality assurance tests including flattening, flaring, ultrasonic flaw detection, pitting and resistance, mechanical, hardness, material verification, and expansion tests. These procedures ensure the suitability of our Grade 1 Titanium Welded and Seamless Pipes for their intended applications. Throughout production, we meticulously measure the diameter, thickness, and surface quality of our products. Our standard delivery time is 5-7 days, extending to 15-20 days for special sizes.
Ti-6Al4V Grade 5 Titanium Alloy Tube is the most commercially sought-after titanium alloy, renowned for its exceptional strength and toughness. It offers outstanding welding and processing characteristics:
We stock and sell a variety of Grade 5 Titanium Alloy Tubes, including Seamless, Forged Seamless, and Welded Tubes.
As a leading manufacturer and supplier of titanium alloy tubes in China, Daxun Alloy provides top-tier Grade 5 titanium pipes that have garnered acclaim from numerous high-profile projects worldwide.
Ti 6Al-4V (Grade 5 Titanium) stands as the most widely used titanium alloy, representing over 50% of total titanium usage. Typically utilized in an annealed state, it operates efficiently up to 400°C (750°F). It is welded using matching or ELI filler wire, boasting greater strength compared to commercial pure titanium tubes along with enhanced stiffness and thermal properties (excluding thermal conductivity). Although its thermal conductivity is about 60% lower than CP titanium, Grade 5 titanium's other advantages-such as heat treatability, strong formability, low density, and excellent corrosion resistance-make it a superior choice for seamless tubes.
This extraordinary Grade 5 titanium alloy seamlessly blends exceptional strength, outstanding corrosion resistance, superb weldability, and remarkable machinability. As a result, it is extensively utilized across various high-demand sectors. Within the military and aerospace industries, it is an indispensable material for crafting military aircraft, aviation components, rocket parts, precision-guided elements, armor parts, ship equipment, and military vacuum equipment. Notably, the closely related 6-4ELI variant finds critical applications in surgical implants. Operating efficiently up to 400°C, it enhances ductility and toughness in cold working conditions, while maintaining an impressive specific strength. Typically supplied in an annealed state, it can be easily heat-treated to bolster its strength for diverse applications. As a versatile titanium alloy, the Ti 6Al-4V seamless tube showcases an array of ideal properties over a temperature range of -210°C to 400°C. Recognized as the most commercialized titanium alloy, Grade 5 titanium alloy tube offers a perfect amalgamation of high strength and toughness, along with excellent welding and processing characteristics.
Discover our Titanium Alloy Grade 5 Seamless Pipe, renowned for its unparalleled performance in high-stress environments. This includes the Titanium Gr 5 High Pressure Pipe and the ASTM B338 Titanium Alloy Gr 5 Seamless Pipe, known for their reliability and strength. We also provide the Titanium Gr 5 Thick Wall Pipe, a testament to robust engineering. As a premier China Titanium Grade 5 ERW Pipe Supplier, we offer Titanium Alloy Gr 5 Pipe, Titanium Gr 5 Electropolished Pipe, and anti-corrosion solutions. Our range includes the ASTM B338 Titanium Grade 5 Welded Pipe and the ASTM B861 / ASME SB861 Titanium Grade 5 Seamless Pipe, perfected by our expertise as a leading China Titanium Gr-5 Seamless Pipe Manufacturer. Our catalog features the Ti-6al-4v Pipe, available in various specifications such as the ASTM B338 Titanium Grade 5 Pipe, Titanium Gr 5 Bright Annealed Pipe, and Titanium WERKSTOFF NR 3.7165 Pipe. Trust us as your reliable Ti-6al-4v Pipe Dealer, offering excellence in every Titanium Gr 5 product.
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
These premium titanium tubes are meticulously crafted using advanced hot-rolling or hot-extrusion processes. They come straightened with both inner and outer diameters precisely machined and surface-polished to perfection. Available in both heat-treated and non-heat-treated forms, our tubes undergo rigorous 100% ultrasonic flaw detection to ensure impeccable quality.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: Outer Diameter (OD) ranging from 19mm to 325mm, wall thickness from 9mm to 30mm, and lengths up to 5000mm (customizable based on manufacturer and customer agreements). - Hot-extruded Titanium Tubes: OD ranging from 50mm to 160mm, wall thickness from 7mm to 35mm, and lengths up to 3000mm (customizable based on manufacturer and customer agreements).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are expertly supplied in heat-treated forms with surface-etched finishes, and are hydrostatically or ultrasonically tested to meet precise manufacturing specifications. Tubes Supplied: Outer Diameter (OD) from 6mm to 89mm, wall thickness from 0.5mm to 11mm, and lengths up to 6000mm (customizable based on manufacturer and customer agreements).
Titanium Welded Pipes
DaXun specializes in the production and supply of titanium pipes with diameters ranging from 100 mm. 12.7 to 38.1 mm (0.47 in to 1.5 in), wall thickness from 0.4 to 1.65 mm (0.016 in to 0.065 in, depending on diameter), and lengths up to 25000 mm. We offer electrical Gr1, Gr2, and Gr12 titanium alloy pipes designed for engineering and chemical industries. Our titanium welded pipes are crafted from flat rolled raw material (kelp) using state-of-the-art automatic tungsten inert gas (argon) welding on electric pipe welders, and are heat-treated on the mill line. Each pipe undergoes comprehensive mechanical testing, geometrical measurements, 100% ultrasonic and eddy current testing, as well as pneumatic or hydrostatic testing. Pipes are meticulously packed according to customer specifications. Our manufacturing processes and inspection test equipment ensure that our thin-wall welded pipes conform to ASTM B 338 and ASME SB 338 standards.
| CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium tube PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
• ASTM B338 - Standard for heat-treatable titanium tubes
• AMS 4928 - Specifications for annealed forgings and forging stock
• AMS 4965 - Standards for solution-treated and aged forgings
• AMS 4967 - Specifications for annealed, heat-treatable forgings
In the annealed condition, typical hardness ranges from Rockwell C 30-34, while in the solution and aged condition, it ranges from Rockwell C 35-39.
Q1: What products can you offer?
A: We offer a diverse range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and the 300 series.
Additionally, our offerings include 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can customize our products based on your drawings to ensure they meet your exact specifications and satisfaction.
Q3: How does your factory ensure quality control?
Quality is our top priority. We maintain rigorous quality control measures from the beginning to the end of the production process.
Q4: Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation methods as per your request.
However, you will need to cover any additional costs and differences incurred during this process.
Q5: How does your factory ensure quality control?
Quality is our top priority. We maintain rigorous quality control measures from the beginning to the end of the production process.
Q6: How long is the delivery time?
A: Standard delivery time ranges from 7 to 20 working days after payment confirmation.
If the order is urgent, we will prioritize and expedite the production process accordingly.
Q7: What are your payment terms?
A: We accept 100% T/T in advance and Western Union for small orders.
B: We also accept 30% T/T with the remaining 70% due before shipment.
C: For large orders, we accept 100% irrevocable LC at sight.
Q8: Can you produce DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Share your usage requirements, and we will adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: We offer FREE samples for your evaluation and testing. For small pieces, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
){kind=link}