| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | GR1 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a premier global producer and supplier of superior Grade 1 titanium plates.
Pure Grade 1 titanium plate boasts exceptional ductility and cold formability, making it ideal for deep drawing. Renowned for its superb general and seawater corrosion resistance, this titanium grade excels against oxidizing, neutral, and mildly reducing media, including chlorides. With half the density of nickel-based alloys, a high strength-to-weight ratio, and impressive corrosion resistance, titanium is the top choice for severe chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile, featuring excellent cold formability, superb corrosion resistance, remarkable weldability, and good impact hardness.
Producers of ASTM B265 Titanium Grade 1 Plates, Sheets, and Finished Plates. Suppliers of Titanium Grade 1 Coils, Pure Titanium Gr 1 Hot Rolled and Cold Rolled Plates, Gr 1 Titanium Patterned and Perforated Plates. Manufacturers of ASTM B265 Gr 1 Sheets and Plates in China.
We ensure timely and rapid delivery of Grade 1 titanium plate products. This speed is backed by a seamless system encompassing production, information flow, logistics, and capital. For instance, Daxun's order data integrates directly with the logistics system in real-time, ensuring smooth data flow. Our logistics infrastructure, situated near highways and waterways, is designed for optimal scheduling, quick response, interconnected storage and transport, and efficient loading, guaranteeing on-time completion of every task.
Grade 1 titanium plate, with its lower density and higher ductility, is perfect for weight-sensitive industries and deep drawing processes. Key sectors include medical, chemical equipment, and aerospace. Its strength and corrosion resistance also make it ideal for marine, chemical processing, and desalination applications. Typical uses of Grade 1 titanium alloys extend to oil and gas components, reaction and pressure vessels, piping systems, power setups, heat exchangers, linings, flue gas desulfurization systems, and a myriad of industrial components. Common standards include ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, and AMS4972.
The cold rolled thickness range for Grade 1 Titanium Plates varies from 0.3 mm to 6.0 mm, supplied in hot rolled or heat-treated conditions. The hot rolled thickness range spans 4.76 mm to 155 mm. These plates are produced using longitudinal and transverse rolling techniques. Creep flattening can be applied as a heat treatment to relieve internal stresses and meet specific flatness requirements. Plates can be provided as cut blanks, with further mechanical or chemical processing based on customer needs.
Chemical composition of (Ti 6Al-4V) Grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
Chemical composition of Grade 2 titanium sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Mechanical properties of Grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is your ultimate metal expert, dedicated to both small and large titanium plate projects. As your premier reference point and long-term partner, DAXUN is poised to supply your business with top-tier titanium plates and comprehensive technical support. Think of DAXUN not just as a supplier of industrial pure titanium plates and titanium alloy plates, but as a strategic ally committed to overcoming challenges and meeting all your needs, ensuring you achieve your project goals with unparalleled efficiency.
DAXUN's state-of-the-art service center in China boasts a vast inventory of titanium plate products, primed for expedited order processing. By offering fundamental processing, precise water jet cutting, and efficient plate nesting services, we deliver added value to our customers, significantly reducing their time and costs.
With steadfast investment in DAXUN's cutting-edge production facilities and strategic capacity agreements with partners, DAXUN ensures it remains at the pinnacle of titanium plate quality, both now and in the future.
Reach out to DAXUN today to secure the latest titanium plate prices and comprehensive technical information tailored to your needs.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a renowned Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! Our mission is to produce the world's finest high-performance titanium alloy plates. We offer swift worldwide delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. DAXUN maintains a robust inventory of Grade 5 (UNS R56400) titanium plates with thicknesses ranging from 0.5mm to 300mm (cold rolled for 0.5mm-6.0mm, hot rolled for 6.0-50mm, and forged for 50mm and above). Grade 5 titanium plate (Ti-6Al-4V) is the backbone of titanium alloy materials. It boasts high strength, ductility, superb corrosion and high temperature resistance, making it highly sought after in both general and military industries. Compliance assured: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, among others.
Ti-6Al-4V Grade 5 Titanium Plate: The Preferred Choice for Aerospace, Military, Power Industry, Vehicle Armor, Rocket Precision Guidance Systems, Marine Industry, and Beyond.
Exclusive Grade 1 Titanium
Today, DAXUN Alloys stands as a leading global producer and supplier of premium Grade 1 titanium plates.
Pure Grade 1 titanium plate features remarkable ductility and cold formability, making it perfect for deep drawing. Renowned for its outstanding general and seawater corrosion resistance, it also excels in oxidizing, neutral, and mildly reducing media, including chlorides. Grade 1 titanium's low density (about half that of nickel-based alloys), high strength-to-weight ratio, and exceptional corrosion resistance make it a stellar option for challenging chemical environments. Commercially pure Grade 1 titanium is the most malleable and ductile. It offers excellent cold formability, exceptional corrosion resistance, and superior weldability with notable impact toughness.
Premier Producers of ASTM B265 Titanium Gr 1 Plates, Sheets, and Coils: Hot Rolled and Cold Rolled Plates, Patterned and Perforated Plates, and more. Trusted Titanium Gr 1 Suppliers and Manufacturers in China.
Renowned Grade 2 Titanium
DAXUN manufactures and stocks commercially pure Grade 2 titanium plates (UNS R50400) in thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the cornerstone of the commercially pure titanium range, blending high strength, ductility, and exceptional corrosion resistance for diverse industrial applications.
Grade 2 Titanium Plate: A commercially pure titanium solution offering an optimal balance of strength and ductility. It boasts impressive impact strength, easy weldability, and superior corrosion resistance in highly oxidizing, alkaline, brine, weakly reducing, and wet *** environments. Furthermore, it provides excellent resistance to seawater and salt solutions.
Titanium's intrinsic low density, high strength-to-weight ratio, and corrosion resistance render it an exceptional material for numerous applications. It effectively withstands stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the go-to alloy for most industrial applications demanding excellent ductility and corrosion resistance.
At DAXUN, we are experts in both small and large titanium plate projects. As your strategic partner, DAXUN is ready to supply titanium plates and offer any necessary technical support. Beyond being your industrial pure titanium and titanium alloy plates supplier, we aim to be your strategic ally, helping you overcome any challenges and fulfill your project goals efficiently.
DAXUN's premier service center in China boasts an extensive stock of titanium plate products, ensuring rapid order processing for your convenience. By utilizing advanced basic processing methods, precision water jet cutting, and expert plate nesting, we deliver exceptional added value to our customers. This not only enhances efficiency but also significantly reduces both time and costs for you.
At DAXUN, continuous investment in state-of-the-art production facilities and strategic capacity agreements with our esteemed partners place us at the zenith of titanium plate quality. This commitment guarantees that DAXUN remains a leader in the industry, delivering unparalleled titanium plate products now and well into the future.
Reach out to DAXUN today to receive comprehensive information on the latest titanium plate prices and in-depth technical specifications. Our team is ready to assist you with any inquiries and provide the best solutions tailored to your needs.
Q1: What products can you offer?
A: We proudly offer a comprehensive range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and 300.
Additionally, we provide high-quality 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Absolutely! We can manufacture products precisely according to your drawings, ensuring your utmost satisfaction.
Q3. How does your factory ensure quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures throughout the entire production process.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can customize the packaging and transportation methods to meet your specific requirements.
However, you will be responsible for any additional costs and price differences incurred during this period.
Q5. How does your factory ensure quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures throughout the entire production process.
Q6. How long is the delivery time?
A: Our standard delivery time is 7-20 working days after payment confirmation.
For urgent orders, we expedite the process to complete the delivery ahead of schedule.
Q7. What are your payment terms?
A: We accept 100% T/T advance payments and Western Union for small orders.
Additionally, we offer 30% T/T upfront with the remaining 70% due before shipment.
For large orders, we accept 100% Irrevocable LC at sight.
Q8: Can you provide Deep Drawing Quality (DDQ) materials?
A: Yes, we specialize in DDQ materials suitable for stainless steel pots, sinks, bowls, and more. Share your usage requirements, and we will tailor the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: We offer FREE samples for inspection and testing. For small pieces, we may cover the courier costs depending on the situation.
Q10: Which countries have you exported to?
A: We have successfully exported our stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and beyond.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}