| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys, a beacon of excellence in the manufacturing realm, proudly presents its high-quality SS 310 / 310S Round Bars. Crafted with precision, these austenitic stainless steel bars showcase a robust blend of chromium and nickel, ensuring exceptional durability and flexibility. Not only do they boast superb workability, machinability, weldability, and ductility, but they also stand out for their high strength and hardness. Renowned for their anti-corrosion properties and ability to withstand extreme temperatures, these bars are perfect for industrial chemistry and nut manufacturing applications. Our commitment to quality and customization allows us to deliver Stainless Steel Round Bars tailored to your unique specifications, all at market-leading prices. Choose Daxun for dependable, high-performance round bars that excel in industrial applications.
For more detailed information on our stainless steel rods, please contact Daxun.
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our state-of-the-art forming capabilities include advanced radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills. Additionally, our unique hydroforming process is ideal for manufacturing complex titanium parts.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods. Experience the excellence of Daxun's heat-treated products.
At Jiangsu Daxun Alloy Co., Ltd., we pride ourselves on utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. By employing these state-of-the-art technologies, we significantly reduce impurities during the smelting process, thereby enhancing the overall performance and quality of our 310S Stainless Steel Round Rod ASTM A276 Hot Rolled Polished High Temperature. This precision ensures that our stainless steel rods meet the highest industry standards and deliver superior durability and reliability in high-temperature applications.
Our stainless steel products are fully certified and meticulously traceable. We proudly supply top-tier stainless steel to leading industries such as aerospace, industrial, medical, marine, and military sectors, ensuring unmatched quality and performance.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and pipes deliver outstanding resistance to both corrosion and heat, even in the most challenging environments.
Stainless steel round bars are highly versatile, finding applications across various sectors from construction to automotive parts. To cater to this diverse usage, Daxun Alloys offers stainless steel round bars in multiple grades and sizes. Our complimentary advanced cutting service ensures precision to meet your specific requirements every time.
Our premium stainless steel round bars are available for easy ordering in a diverse array of sizes to suit all your needs. Choose the specific grade of steel you require, and we will deliver bars that span lengths from 500mm to an impressive 6 meters with diameters ranging from a delicate 3mm to a robust 500mm. We even provide the flexibility of ordering in both metric and imperial sizes, ensuring you get exactly what you need.
Need a custom size? No problem! We offer complimentary unlimited cuts to length. Utilizing advanced bandsaw technology for matchless accuracy and consistency, we can flawlessly meet your exact specifications each and every time. Just inform us of your requirements when placing your order, and we'll handle the rest.
Can you provide SS grinding bars and rods?
Yes, we specialize in producing SS grinding bars and rods with exceptional precision in dimension, roundness, and straightness. These are superior to standard stainless steel polished bars, though the processing cost is correspondingly higher.
Q1: What products can you offer?
A: We offer a wide range of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and 300 series.
Additionally, we provide 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, etc., as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you manufacture products based on my custom drawings?
Yes, we can manufacture products according to your custom drawings to ensure they meet your exact specifications.
Q3. How does your factory ensure quality control?
Quality is our top priority. We consistently emphasize rigorous quality control measures from start to finish.
Q4. Can I request changes to the packaging and transportation methods?
Yes, we can modify the packaging and transportation methods according to your requests.
However, you will need to cover any additional costs and price differences incurred during this process.
Q5. How does your factory ensure quality control?
Quality is our top priority. We consistently emphasize rigorous quality control measures from start to finish.
Q6. What is the delivery time?
A: The delivery timeframe is 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite production in our workshop to ensure timely delivery.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T deposit and the remaining 70% before shipment.
C: 100% Irrevocable Letter of Credit at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, and more. Provide us with your usage details, and we will tailor the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: We offer FREE samples for your inspection and testing. For small pieces, we may cover the courier cost, depending on the circumstances.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and others.
){kind=link}