| Type: | Stainless Steel Sheets |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | 201 304 316 321 310S 2205 2507 410 430 |
| Certification: | ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS |
| Shape: | Flat |
| Technique: | Cold Rolled |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Grade | 201 304 316 321 309 310S 2205 2507 410 420 430 440 409 630 17-4 |
| Stainless Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Standard | ASTM A240 / ASME SA240 ASTM/ASME 240/480,JIS 4305,DIN EN 10088-2JIS, AISI, ASTM, GB, DIN, EN, etc |
| Stainless Steel Plate and sheet Length | 1000mm-13000mm or as required |
| Stainless steel Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| Stainless steel Plate Thickness | 0.3 to 120mm or as required |
| ASTM A240 Stainless Steel 304 Plate Process | Hot/ Cold Rolled/forging |
| Stainless steel Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM A240Stainless steel sheet, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| Stainless steel Sheet ASTM | ASTM A240 |
| Stainless steelSheet AMS | AMS 240 |
| Tolerances of width and thickness | ASTM-ASME-GB-EN-DIN-JIS |
| Stainless steel Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Stainless steel Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm,1500*6000,Cold rolled 304 Stainless Plate 0.5-6.4 mm,Hot rolled 304 Stainless Plate 3.0-60.0 mm |
| Stainless steel Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM A240Stainless Steel Sheet suppliers |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including:Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting |
| Plasma profiles | As per customer's drawings |
| Value added services for 304 Stainless Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| Manufacturer | POSCO, Aperam, ATI, Baosteel, TISCO, ArcelorMittal, VDM, Nippon Metal, Tsingshan, Delong. |
| China Stainless steel sheet Manufacturer | ASTM A240Stainless Steel Stainless steel sheet: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Stainless Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Steel Stainless Stainless steel sheet: Steel Stainless Clad plate is a composite steel plate made by bonding Stainless Plate, etc.ASTM A240Stainless SteelStrip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| Stainless steel sheet Origin | CHINA |
| Packing of Stainless steel sheet | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy Stainless steel sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment,NABL Approved Lab Reports,Any third party inspection is accepted,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count TestGrade: AISI 304/S30400 |
| Manufacturing: cold-rolled plate, hot-rolled plate, forged plate | |
| Standard: ASTM, ASME, GB, DIN, JIS, ISO, EN, BS | |
| Type: cold-rolled thin plate, hot-rolled thick plate | |
| Surface: 2B, NO.1, NO.4, HL, BA, 8K, etc. | |
| Length: 2438mm3048mm6000mm can be customized | |
| Origin: TISCO, Baosteel, Posco, Tsingshan, Delong |
At Daxun, we cut and finish high-quality stainless steel sheets to meet your exact size requirements, ensuring full certification. As a proud BSSA member and ISO 9001 certified company, all our stainless steel sheets are sourced from trusted factories and must pass our rigorous quality control procedures before delivery. We meticulously monitor each product from start to finish, guaranteeing your utmost satisfaction upon receipt.
Stainless Steel Plate Surface Description
| Finish Designation | Method and degree of finish |
| No.1 | After hot rolling, heat treatment, pickling or other equivalent treatment is applied. |
| No.2D | Annealing and pickling are performed after cold rolling; material is soft with surface of silver-white luster; used for general applications and deep drawing. |
| No.2B | After 2D finish, skin pass rolling is performed to obtain a more suitable luster; the surface becomes very exquisite; used for general applications. |
| No.3 | Intermediate 100-120 grit finish; used for applications in which surface polishing is performed after shaping. |
| No.4 | General 150-180 grit finish; used for restaurants and kitchen equipment and tools. |
| #240 | 240 grit finish; used when a finer finish than No. 4 is required; typically for restaurants and kitchen equipment and tools. |
| #320 | 320 grit finish polished product. |
| HL | This finish is performed by continuous linear polishing using an abrasive of appropriate grain size; mainly used for architectural applications. |
| BA | Achieved by performing bright annealing after cold rolling and then skin pass rolling to obtain even greater reflectance; provides excellent corrosion resistance; used for household appliances, kitchen equipment, and automobiles. |
| 8K | Through multiple grinding, it achieves very high brightness and smoothness, like a mirror. |
| 304/304L/304LN/304H stainless steel Shhet/plate composition | ||||
| Grade | 304 | 304L | 304LN | 304H |
| UNS Designation | S30400 | S30403 | S30453 | S30409 |
| Carbon (C) Max. | 0.08 | 0.030* | 0.03 | 0.04 - 0.10 |
| Manganese (Mn) Max. | 2 | 2 | 2 | 2 |
| Phosphorous (P) Max. | 0.045 | 0.045 | 0.045 | 0.045 |
| *** (S) Max. | 0.03 | 0.03 | 0.03 | 0.03 |
| Silicon (Si) Max. | 1 | 1 | 1 | 1 |
| Chromium (Cr) | 18.0-20.0 | 18.0-20.0 | 18.0-20.0 | 18.0-20.0 |
| Nickel (Ni) | 8.0-11.0 | 8.0-11.0 | 8.0-11.0 | 8.0-11.0 |
| Molybdenum (Mo) | - | - | - | - |
| Nitrogen (N) | - | - | 0.10-0.15 | - |
| Iron (Fe) | Bal. | Bal. | Bal. | Bal. |
| Other Elements | - | - | - | - |
| 316/316L316H stainless steel Shhet/plate composition | ||||||||||
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 316 | Min | - | - | - | 0 | - | 16 | 2 | 10 | - |
| Max | 0.08 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
| 316L | Min | - | - | - | - | - | 16 | 2 | 10 | - |
| Max | 0.03 | 2 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | 0.1 | |
| 316H | Min | 0.04 | 0.04 | 0 | - | - | 16 | 2 | 10 | - |
| max | 0.1 | 0.1 | 0.75 | 0.045 | 0.03 | 18 | 3 | 14 | - | |
| 321/321H stainless steel Shhet/plate composition | ||
| Grade | 321 | 321H |
| UNS Designation | S32100 | S32109 |
| Carbon (C) Max. | 0.08 | 0.04-0.10 |
| Manganese (Mn) Max. | 2 | 2 |
| Phosphorous (P) Max. | 0.04 | 0.04 |
| *** (S) Max. | 0.03 | 0.03 |
| Silicon (Si) Max. | 0.75 | 0.75 |
| Chromium (Cr) | 17.0-20.0 | 17.0-20.0 |
| Nickel (Ni) | 9.0-12.0 | 9.0-12.0 |
| Molybdenum (Mo) | - | - |
| Nitrogen (N) | 0.1 Max. | 0.1 Max. |
| Iron (Fe) | Bal. | Bal. |
| Other Elements | Ti=5(C) to 0.70% | Ti=4(C) to 0.60% |
| 310/310S stainless steel Shhet/plate composition | |||||||||
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |