| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Explore our extensive range of stainless steel products, including ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, and Stainless Steel 410 Rod. As premier manufacturers of SS 410 Round Bar and SS DIN 1.4006 Round Bar, we also offer the finest 410 Stainless Steel Bright Bar, 410 SS Polished Bar, and SS 410 Rods. Purchase from leading China-based producers of AISI SS 410 Round Bar.
For more information on our premium stainless steel rods, please contact Daxun.
410 Stainless Steel Rod: Chemical Composition
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our state-of-the-art forming capabilities include advanced radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods. We also employ a unique hydroforming process to produce intricate parts.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods through precise heat treatment processes.
Daxun Stainless Steel utilizes the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These state-of-the-art technologies reduce impurities during the smelting process, significantly enhancing the overall performance of our stainless steel rods.
At Jiangsu Daxun Alloy Co., Ltd., our stainless steel products are not only fully certified but also meticulously traceable. We pride ourselves on delivering the highest caliber of stainless steel, catering to a diverse array of industries such as aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
Visit specific product pages for detailed size information, or contact us for quotes on custom size orders.
Our 410 stainless steel round bars are extensively utilized, spanning sectors from construction to automotive. Given their versatility, Jiangsu Daxun Alloy Co., Ltd. offers these bars in various grades and sizes. Leverage our complimentary advanced cutting service to meet your precise specifications every single time.
Can you do SS grinding bar & rod?
Yes, we can manufacture SS grinding bars & rods with impeccable precision in dimension, roundness, and straightness. These qualities exceed those of standard stainless steel polished bars, though the processing cost is somewhat higher.
Q1: What products can you offer?
A: We provide a wide range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L.
400 series as well as duplex stainless steel like 2205, 2304, 2101, 2507, and more. We also offer high-nickel alloys such as 904L, 800H, and 600H.
Q2. Can you produce products according to my own drawings?
Yes, we can manufacture products based on your drawings to ensure they meet your exact specifications and satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. From start to finish, we implement rigorous quality control measures to ensure the highest standards.
Q4. Can I request changes to packaging and transportation?
Yes, we can modify the packaging and transportation methods according to your specific requests.
However, you will be responsible for any additional costs incurred during this process.
Q5. How does your factory handle quality control?
Quality is our top priority. From start to finish, we implement rigorous quality control measures to ensure the highest standards.
Q6. What is the delivery time?
A: Our standard delivery time is 7-20 working days after payment confirmation.
For urgent orders, we can expedite the process to meet your timeline.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and 70% balance before shipment.
C: 100% Irrevocable LC at sight, suitable for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality)?
A: Absolutely. Our materials are perfect for applications like stainless steel pots, sinks, and bowls. Just let us know your requirements, and we will adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: We offer FREE samples for your evaluation and testing. For small pieces, we can cover the courier cost, subject to our discretion.
Q10: Which countries have you exported to?
A: So far, our stainless steel materials have been exported to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}