Product Parameters: Stainless Steel rod |
Material |
904L 1.4539 N08904 Super Austenite Round Bar |
Specifications |
ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
Dimensions |
EN, DIN, JIS, ASTM, BS, ASME, AISI |
Round Bars |
Outside Diameter in the range of 4mm to 500mm |
Bright Bars |
Outside Diameter in the range of 4mm to 100mm |
Hex Bars |
18mm - 57mm (11/16″ to 2-3/4″) |
Finish |
Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
Length |
1 to 6 Meters, Custom Cut Lengths |
Form |
Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
Marking & Traceability |
Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
Test Certificate |
Manufacturer Test Certificate according to EN 10204 3.1 B |
Laboratory Test Certificate from Govt. Approved Lab. |
Under Third Party Inspection |
Testing & Inspection |
Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
High-Quality Hot Rolled Stainless Steel Rod
Our stainless steel rod and bar are meticulously heated and expertly rolled through multiple passes in a state-of-the-art rolling mill. Featuring a comprehensive range of specifications, our products meet and exceed performance standards and requirements.
Impeccably Finished Cold Drawn Bright Stainless Steel Rods
Our cold-drawn stainless steel rods, drawn under precise cold working conditions, boast a smooth, flawless surface. These rods can also be further polished and ground to perfection.
Premium Forged Stainless Steel Rod and Bar
Our forged stainless steel rods undergo multiple forging processes to significantly enhance their mechanical properties and strengthen the stainless steel rods to unmatched levels.
Exceptional General Properties
Our extensive network of service centers stocks a vast array of stainless steel bar products, ensuring a fast and ready supply of common bar sizes and alloys. We also offer custom-sized stainless steel bars. For orders below factory minimums, we can arrange a stocking program for swift turnaround. Daxun Alloys stocks stainless steel round bars ranging from 1/16" to 26" in diameter, available in nearly every stainless steel grade, including but not limited to 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.
Comprehensive Additional Services
The majority of our inventory features our exclusive processed bar grade: stainless steel round bars, meticulously melted to consistent standards to enhance machinability and minimize the total cost of each part. Our state-of-the-art stainless steel bar processing machinery enables Daxun Alloys to manufacture according to our customers' precise specifications.
1. Daxun offers specialized heat treatments for our stainless steel bars, contingent on the metal's chemistry. 2. Positive Material Identification (PMI) When required, additional PMI testing can be conducted in-house or through an independent laboratory to ensure material integrity. 3. Ultrasonic Testing (UT) Utilizing high-frequency sound energy, our UT inspections and measurements detect and evaluate defects, dimensionally measure products, and more.
![904L Stainless Steel Rod, Hot Forged, Acid Resistant, Chemical Processing, Posco Trademark](//www.micstatic.com/athena/img/transparent.png)
For further details about our premium stainless steel rods, please reach out to Daxun.
904L Stainless Steel Rod: Chemical Composition
Element |
% Present (in product form) |
Carbon (C) |
0.02 |
Silicon (Si) |
0.7 |
Manganese (Mn) |
2 |
Phosphorous (P) |
0.03 |
Sulfur (S) |
0.01 |
Chromium (Cr) |
19.00 - 21.00 |
Nickel (Ni) |
24.00 - 26.00 |
Nitrogen (N) |
0.15 |
Molybdenum (Mo) |
4.00 - 5.00 |
Copper (Cu) |
1.20 - 2.00 |
Iron (Fe) |
Balance |
904L Stainless Steel Rod: Mechanical Properties
Product Form |
|
|
|
|
C |
H |
P |
L |
L |
TW/TS |
Thickness (mm) Max. |
8 |
13.5 |
75 |
160 |
2502) |
60 |
Yield Strength |
Rp0.2N/mm2 |
2403) |
2203) |
2203) |
2304) |
2305) |
2306) |
Rp1.0N/mm2 |
2703) |
2603) |
2603) |
2603) |
2603) |
2503) |
Tensile Strength |
RmN/mm2 |
530 - 7303) |
530 - 7303) |
520 - 7203) |
530 - 7304) |
530 - 7305) |
520 - 7206) |
Elongation min. in % |
Jmin(Longitudinal) |
- |
100 |
100 |
100 |
- |
120 |
Jmin(Transverse) |
- |
60 |
60 |
- |
60 |
90 |
904L Stainless Steel Rod: Physical Properties
Density at 20°C kg/m3 |
8 |
Thermal Conductivity W/m K at |
20°C |
12 |
Modulus of Elasticity kN/mm2 at |
20°C |
195 |
200°C |
182 |
400°C |
166 |
500°C |
158 |
Specific Thermal Capacity at 20°C J/kg K |
450 |
Electrical Resistivity at 20°C mm2/m |
1 |
Daxun's Cutting-Edge Stainless Steel Rod Manufacturing Capabilities
Our forming capabilities include advanced radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for top-tier titanium rod manufacturing. Additionally, we employ a unique hydroforming process for creating precision parts.
Daxun's Advanced Heat Treatment Furnace
Our stainless steel rod heat treatment utilizes advanced furnace equipment, ensuring the material's stability and superior performance.
Daxun's Superior Smelting Ability
At Daxun Stainless Steel, we leverage the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace to minimize impurities during smelting, thereby significantly enhancing the performance of our finished stainless steel rods.
![904L Stainless Steel Rod, Hot Forged, Acid Resistant, Chemical Processing, Posco Trademark](//www.micstatic.com/athena/img/transparent.png)
Experience unparalleled reliability with Jiangsu Daxun Alloy Co., Ltd., your premier supplier of 904L Stainless Steel Rods.
Our stainless steel products are meticulously certified and fully traceable, ensuring you receive the highest quality material. We proudly serve leading industries such as aerospace, industrial, medical, marine, and military, meeting their exacting standards for excellence.
![904L Stainless Steel Rod, Hot Forged, Acid Resistant, Chemical Processing, Posco Trademark](//www.micstatic.com/athena/img/transparent.png)
Detailed Mechanical Properties of Various Grades of Stainless Steel Bars
|
Tensile Strength |
Yield Strength |
|
|
|
|
|
|
Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
Grain Size Req. |
Max. Hardness |
Modulus of Elasticity (x106 psi) |
304 |
S30400 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
304L |
S30403 |
A270 A312 |
70,000 |
485 |
70 |
25,000 |
170 |
25 |
35 |
- |
90 Rb |
28 |
304LN |
S30453 |
A249, A688 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
304H |
A30409 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
7 or coarser |
90 Rb |
28 |
The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. |
Grade |
Tensile Str |
Yield Str |
Elong |
Hardness |
(MPa) min |
0.2% Proof |
(% in 50mm) min |
|
(MPa) min |
|
Rockwell B (HR B) max |
Brinell (HB) max |
316 |
515 |
205 |
40 |
95 |
217 |
316L |
485 |
170 |
40 |
95 |
217 |
316H |
515 |
205 |
40 |
95 |
217 |
|
Tensile Strength |
Yield Strength |
|
|
|
Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
321 |
S32100 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
321H |
S32109 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
Grade |
Density |
Melting Point |
Tensile Strength |
Yield Strength (0.2%Offset) |
Elongation |
310S |
7.9 g/cm3 |
1402 °C (2555 °F) |
Psi - 75000 , MPa - 515 |
Psi - 30000 , MPa - 205 |
40% |
Grade |
Tensile Strength |
Yield Strength |
Elongation |
Hardness |
(MPa) min |
0.2% Proof |
(% in 50mm) min |
|
(MPa) min |
|
Rockwell C (HR C) |
Brinell (HB) |
UNS S31803 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
UNS S32205 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
Grade |
Property |
Value |
2507/
S32750 |
Density (g/cm3) |
7.8 |
0.2% Offset Yield Strength |
80 ksi |
Ultimate Tensile Strength |
116 ksi |
0.1% Offset Yield Strength 0.2% |
91 ksi |
Elongation in 2 inches, % |
15% |
Hardness Rockwell C |
32 |
Impact Energy |
74 ft.-lbs |
Density |
0.28 lb per inch3 |
Modulus of elasticity |
28 x 10(6) psi |
Coefficient of thermal expansion |
7.2 x 10(-6) per of at 68 to 212 of |
Thermal conductivity |
8.7 Btu/hr ftoF |
Heat capacity |
0.12 Btu/ lb oF |
Electrical resistivity |
31.5 x10(-6) ohm-inch |
For comprehensive information on our top-tier stainless steel rods, reach out to Jiangsu Daxun Alloy Co., Ltd. today.
![904L Stainless Steel Rod, Hot Forged, Acid Resistant, Chemical Processing, Posco Trademark](//www.micstatic.com/athena/img/transparent.png)
![904L Stainless Steel Rod, Hot Forged, Acid Resistant, Chemical Processing, Posco Trademark](//www.micstatic.com/athena/img/transparent.png)
![904L Stainless Steel Rod, Hot Forged, Acid Resistant, Chemical Processing, Posco Trademark](//www.micstatic.com/athena/img/transparent.png)