| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition of 201 Stainless Steel Rod
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties of 201 Stainless Steel Rod
Mechanical property requirements for annealed product as specified in ASTM A240 and ASME SA240
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
Mechanical property requirements for cold worked flat rolled products as specified in ASTM A276 ensure superior performance and durability, making them ideal for high-stress applications. 201 Stainless Steel Rod: High-quality, versatile, and reliable, perfect for a wide range of applications in various industries.
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Physical Properties: Comprehensive details on the robustness and durability of our stainless steel rods.
Physical Properties for Type 201 Stainless Steel Rod: Detailed insights into the strength, flexibility, and corrosion resistance of our premium product.
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Forming Capabilities: State-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium and stainless steel rods. Our unique hydroforming process ensures precision in part manufacturing.
Stainless Steel Rod Heat Treatment: Utilizing advanced furnace equipment to ensure material stability and high performance, perfect for demanding applications.
Daxun Stainless Steel: Leading the industry with state-of-the-art vacuum induction furnace, vacuum consumable furnace, and electroslag furnace technology. We ensure the highest quality and performance by reducing impurities during the smelting process.
Our stainless steel products are meticulously certified and entirely traceable. We proudly provide the finest stainless steel to elite industries such as aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you provide stainless steel grinding bars and rods?
Absolutely! We specialize in SS grinding bars and rods that boast precise dimensions, optimal roundness, and unrivaled straightness. These features surpass those of standard stainless steel polished bars. However, please note that the processing costs are comparatively higher.
Q1: What range of products do you offer?
A: We offer a comprehensive selection of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series,
as well as 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, etc. Additionally, we provide high-nickel alloy types like 904L, 800H, and 600H.
Q2: Can you manufacture products according to custom drawings?
Yes, we can manufacture products tailored to your drawings, ensuring they meet your highest satisfaction.
Q3: How does your factory ensure quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures from start to finish.
Q4: Can I request changes in packaging and transportation?
Yes, we can accommodate changes in packaging and transportation forms per your requirements.
However, you will need to cover any additional costs and the price differences incurred during this process.
Q5: How does your factory manage quality control?
Quality remains our utmost priority. We always place significant importance on maintaining high-quality standards from the beginning to the end of the production process.
Q6: What is the typical delivery time?
A: Delivery usually takes 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite the process to ensure timely completion.
Q7: What payment methods do you accept?
A: 100% T/T in advance, Western Union (for small orders)
B: 30% T/T in advance and the remaining 70% before shipment
C: 100% Irrevocable LC at sight (for large orders)
Q8: Can you produce Deep Drawing Quality (DDQ) products?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, etc. Inform us of your specific application, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: FREE samples are available for your evaluation. For small pieces, we may cover the courier costs, depending on the situation.
Q10: To which countries have you exported your products?
A: We have successfully exported stainless steel materials to countries such as Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many others.
){kind=link}