Type: | Titanium Pipes |
---|---|
Application: | Industrial, Medical |
Technique: | Hot Rolled |
Grade: | Gr2 Grade2 |
Shape: | Round |
Standards: | Astmb861 B862 B338 ASME Sb861 Sb862 Sb338 |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Grade 2 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
Grade 2 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 2- TA2- USN 50400 |
Grade 2 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
Grade 2 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
Titanium welded pipe - φ1.0mm to φ1219mm | |
Grade 2 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
Grade 2 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
Titanium pipe Form TA2 | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
Marking TA2 3.7035 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
Grade 2 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
Grade 2 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
Grade 2 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
Grade 2 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
Grade 2 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
Grade 2 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
Grade 2 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
Grade 2 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
Grade 2 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 2 Titanium Welded Tube: Diameter ranges from 6.0mm to 1219mm, wall thickness ranges from 0.3mm to 30mm (depending on diameter), lengths up to 25000mm, made from Gr1 titanium tube. Our welded tubes are meticulously crafted from flat rolled billets (tube blanks) on advanced electric tube welding machines using automatic tungsten inert gas (argon) welding techniques. They are heat treated on the mill line and subjected to rigorous mechanical tests, geometric measurements, and 100% ultrasonic and eddy current testing. Additionally, they undergo pneumatic or hydrostatic testing before being carefully packaged according to customer specifications. Our state-of-the-art manufacturing technology and comprehensive inspection and testing equipment ensure that our thin wall welded tubes consistently meet ASTM B 338 and ASME SB 338 specifications.
Daxun's Grade 2 Titanium Tube is renowned for its medium strength and outstanding cold forming properties. It boasts excellent weldability and exceptional resistance to oxidation and corrosion, making it a top choice for demanding applications.
Purchase Grade 2 Titanium Tubes from Daxun; we offer an extensive range of sizes, starting from a 1.0 mm diameter. Choose from our inventory or request custom-made tubes to meet your specific needs. Our seamless rolled and longitudinally welded tubes are immediately available for a variety of applications, adhering to typical specifications for heat exchangers such as ASTM B 338, ASME SB 338, DIN, and VD TÜV.
Our CP Grade 2 tubes boast a density of 4.51 g/cm3, which is 45% lighter than ferrous alloys. This medium-strength alloy, with a typical yield strength of 352 MPa, offers excellent ductility, formability, and welding properties. The addition of iron and oxygen enhances its strength and formability. CP Grade 2 demonstrates impressive corrosion resistance under oxidizing conditions, making it a stronger alternative to Grade 1 titanium tubes.
Grade 2 Titanium Tubes represent commercially pure titanium with an ideal balance of strength and ductility. This material is celebrated for its toughness and is the most commonly used titanium alloy due to its high strength, weldability, and corrosion resistance. Its superior ductility and formability make it the preferred alloy for piping systems, heat exchangers, reaction and pressure vessels, and flue gas desulfurization systems. Grade 2 titanium alloys are utilized across a range of industries, including chemical processing, petrochemical processing, aerospace, and marine sectors.
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
These premium titanium tubes are meticulously crafted using hot-rolled or hot-extruded processes. They are expertly straightened, with precision machining of inside and outside diameters, and feature a polished finish. Available in both heat-treated and non-heat-treated forms, our tubes undergo rigorous 100% ultrasonic flaw detection to ensure unparalleled quality.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: OD ranging from 19mm to 325mm, wall thickness from 9mm to 30mm, and lengths up to 5000mm (subject to mutual agreement between the manufacturer and customer). - Hot-extruded Titanium Tubes: OD ranging from 50mm to 160mm, wall thickness from 7mm to 35mm, and lengths up to 3000mm (subject to mutual agreement between the manufacturer and customer).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are available in heat-treated forms and feature surface etching. They are subjected to hydrostatic or ultrasonic testing as per manufacturing specifications. Tubes Supplied: OD 6mm to 89mm, wall thickness from 0.5mm to 11mm, lengths up to 6000mm (subject to mutual agreement between the manufacturer and customer).
Titanium Welded Pipes
DaXun excels in producing and supplying high-quality titanium pipes with diameters ranging from 12.7 mm to 38.1 mm (0.47 in to 1.5 in) and wall thicknesses from 0.4 mm to 1.65 mm (0.016 in to 0.065 in, depending on diameter). These pipes can extend up to 25000 mm in length and are available in electrical Gr1, Gr2, and Gr12 titanium alloys, ideal for engineering and chemical industries. Our titanium welded pipes are manufactured from flat rolled raw materials using automatic tungsten inert gas (argon) welding on electric pipe welders and are heat-treated on the production line. Each pipe undergoes extensive mechanical testing, precise geometrical measurements, and 100% ultrasonic and eddy current testing, along with pneumatic or hydrostatic tests. We ensure compliance with ASTM B 338 and ASME SB 338 standards, and our packaging meets customer specifications.
CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.50 g/cc | 0.163 lb/in³ | |
a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
Mechanical Properties | Metric | English | Comments |
Hardness, Brinell | 120 | 120 | annealed |
Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
Hardness, Rockwell B | 70 | 70 | annealed |
Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
Elongation at Break | 24% | 24% | |
25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
Reduction of Area | 35% | 35% | |
Tensile Modulus | 103 GPa | 14900 ksi | |
Compressive Modulus | 110 GPa | 16000 ksi | |
Poissons Ratio | 0.37 | 0.37 | |
Shear Modulus | 45.0 GPa | 6530 ksi | |
Charpy Impact | 310 J | 229 ft-lb | V-notch |
Impact Test | 136 J | 100 ft-lb | Impact Strength |
Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
0.8 | 0.8 | Ti sliding on Ti; 40 m/min |
CP GR2 Titanium tube PHYSICAL PROPERTIES | |
Density | Magnetic Permeability |
0.163 lbs/in-3 | Nonmagnetic |
4.51 g/cm-3 | Electrical Resistivity |
Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
1680°F | 0.53 µΩ/m |
915°C | Elastic Modulus |
Thermal Conductivity | 15.2-17.4 Msi |
12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % | |
Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
Compressive Yield Strength | 970 MPa | 141000 psi | |
Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
Poisson's Ratio | 0.342 | 0.342 | |
Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
Shear Modulus | 44 GPa | 6380 ksi | |
Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
Electrical Properties | |||
Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
Thermal Properties | |||
CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
Solidus | 1604 °C | 2920 °F | |
Liquidus | 1660 °C | 3020 °F | |
Beta Transus | 980 °C | 1800 °F |
Grade 2 Titanium Tube is the gold standard for industrial applications. This exceptional material finds its niche with a balanced combination of moderate strength and notable ductility, all while delivering top-tier corrosion resistance. Whether in highly oxidizing environments or slightly reducing conditions, including exposure to chlorides, this titanium tube shines. Industries such as chemical processing, offshore drilling, and aircraft manufacturing benefit immensely from its robust strength and ease of forming. Additionally, it's a preferred choice for heat exchangers, hypochlorite systems, fire water systems, ballast water systems, components in both industrial and aerospace sectors, CPI equipment, and piping solutions.
Our most frequently utilized titanium tube for industrial applications, the Titanium Seamless Tube Grade 2 offers an exceptional combination of moderate strength and reasonable ductility. It excels in corrosion resistance under both highly oxidizing and mildly reducing conditions, including environments with chlorides. This tube is indispensable in chemical and offshore industries and is a critical component in aircraft manufacturing where strength and formability are paramount. Its versatility extends to heat exchangers, hypochlorite systems, fire water systems, ballast water systems, industrial and aerospace components, CPI equipment, and piping solutions.