| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition of 201 Stainless Steel Rod
Chemical Composition (wt%) Limits as Specified in ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties of 201 Stainless Steel Rod
Mechanical property requirements for the annealed product as specified in ASTM A240 and ASME SA240
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
The mechanical property requirements for our cold worked flat rolled products are meticulously defined and rigorously upheld to ensure superior quality and performance. Introducing the 201 Stainless Steel Rod - engineered for precision and durability.
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Exemplary Physical Properties
Outstanding physical properties define our Type 201 stainless steel rod, making it ideal for various structural applications.
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Our forming capabilities encompass state-of-the-art radial forging machines, advanced heat treatment furnaces, high-efficiency melting furnaces, and cutting-edge rolling mills designed for manufacturing titanium rods. Additionally, we employ a unique hydroforming process to produce high-precision parts.
Our stainless steel rod heat treatment process utilizes advanced furnace equipment, ensuring the material's stability and exceptional performance.
Jiangsu Daxun Alloy Co., Ltd. employs the world's most advanced smelting technologies, including vacuum induction furnaces, vacuum consumable furnaces, and electroslag furnaces. These technologies significantly reduce impurities during the smelting process, enhancing the performance and quality of our stainless steel rods.
Our stainless steel products are fully certified and traceable. We supply the highest quality stainless steel to leading industries including aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you do SS grinding bar & rod?
Yes, we can produce SS grinding bars & rods with exceptional precision in dimension, roundness, and straightness. These are superior to standard stainless steel polished bars, although the processing costs are higher.
Q1: What products can you offer?
A: We offer a comprehensive range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series.
Additionally, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, and 2507. We also offer high-nickel alloys like 904L, 800H, and 600H.
Q2: Can you produce the products according to my own drawings?
Absolutely, we can manufacture products based on your drawings to ensure they meet your exact specifications and satisfaction.
Q3: How does your factory manage quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures from the beginning of the process to the end to ensure superior standards.
Q4: Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation forms according to your requirements.
However, you will be responsible for any additional costs and differences incurred during this period.
Q5: How does your factory manage quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures from the beginning of the process to the end to ensure superior standards.
Q6: How long is the delivery time?
A: Delivery typically takes 7-20 working days after payment confirmation.
For urgent orders, we can expedite the process and prioritize completion in our workshop.
Q7: What are your payment terms?
A: 100% T/T in advance, Western Union (for small orders).
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you produce DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, and more. Inform us of your specific usage, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I get a sample?
A: FREE samples are available for your inspection and testing. If a small piece is required, we may cover the courier cost, depending on the specifics.
Q10: Which countries have you exported to?
A: We have exported our stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}