| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For further details on stainless steel rods, please reach out to Daxun.
304 Stainless Steel Rod Chemical Composition
Chemical Composition (wt%) as per ASTM A240 and ASME SA240*
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod Mechanical Properties
Mechanical property specifications for annealed products as defined in ASTM A240 and ASME SA240.
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod Physical Properties
Physical properties for Type 304/304L stainless steel.
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our forming capabilities feature cutting-edge radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods, complemented by a unique hydroforming process for parts production.
Our state-of-the-art heat treatment furnace ensures the stability and superior performance of stainless steel rods through precise and controlled thermal processes.
Jiangsu Daxun Alloy Co., Ltd. takes pride in utilizing the world's most cutting-edge technology in stainless steel production. By employing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun Stainless Steel significantly reduces impurities during the smelting process. This meticulous attention to detail not only enhances the purity but also substantially improves the overall performance and durability of our superior Baosteel 304 Stainless Steel Round Rods, available in 5-30mm sizes and renowned for their exceptional corrosion resistance.
Our premium stainless steel products are fully certified and traceable, ensuring you receive only the highest quality materials. We proudly serve leading industries such as aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
DAUXN 304/304L Stainless Steel RODS are indispensable across a myriad of residential and commercial sectors, including:
Can you manufacture SS grinding bars and rods?
Absolutely! We specialize in producing SS grinding bars and rods with precise dimensions, exceptional roundness, and straightness, surpassing standard stainless steel polished bars in quality. However, please note that the processing costs are higher.
Q1: What products can you offer?
A: We offer a wide range of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300 series.
Additionally, we provide 400 series and duplex stainless steel such as 2205, 2304, 2101, and 2507. We also supply high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products tailored to your drawings, ensuring complete satisfaction with the outcome.
Q3. How does your factory manage quality control?
Quality is our top priority. We rigorously control quality throughout every stage of the production process.
Q4. Can I request changes to packaging and transportation?
Yes, we can modify the packaging and transportation methods according to your requests.
However, you will be responsible for any additional costs and differences incurred during this period.
Q5. How does your factory manage quality control?
Quality is paramount. We place a strong emphasis on quality control from start to finish.
Q6. What is the delivery time?
A: Delivery takes 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite the process in our workshop to meet your timeline.
Q7. What payment methods do you accept?
A: 100% T/T in advance, Western Union (for small orders)
B: 30% T/T with the balance 70% before shipment
C: 100% Irrevocable L/C at sight (for large orders)
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, and more. Share your requirements, and we will adjust the mechanical properties to meet them.
Q9: How can I obtain a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we may cover the courier costs, depending on the situation.
Q10: To which countries have you exported?
A: We have exported stainless steel materials to several countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}