| Type: | Titanium Pipes |
|---|---|
| Application: | Industrial, Medical |
| Technique: | Hot Rolled |
| Grade: | Gr5 Grade5 6-4 Ti6al4V |
| Shape: | Round |
| Standards: | Astmb861 B862 B338 ASME Sb861 Sb862 Sb338 |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Ti-6Al-4V Grade 5 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 5 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 5-Ti-6Al4V- TC4- USN 56400 |
| Grade 5 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 5 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ6.0mm to φ1219mm | |
| Grade 5 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 5 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form Ti-6Al-4V | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TC4 1.37165 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 5 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 5 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 5 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 5 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 5 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 5 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 5 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 5 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 5 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 5 titanium tubes are widely used in the following industries under extreme corrosive conditions:
Daxun performs several quality assurance tests, these tests include flattening test, flaring test, ultrasonic flaw detection test, pitting and resistance test, mechanical test, hardness test, material positive identification, expansion test, etc. All these tests ensure that the Grade 1 Titanium Welded Pipe and Grade 1 Titanium Seamless Pipe materials are suitable for the required application. During the production process, we measure the diameter, thickness and surface of the products. Our standard delivery time is 5-7 days and the delivery time for special size products is 15-20 days.
Ti-6Al4V Grade 5 Titanium Alloy Tube is the most commercially available of all Titanium alloys. It combines high strength and toughness. Grade 5 Titanium alloy has good welding and processing characteristics:
We stock and sell Grade 5 Titanium Alloy Seamless Tubes, Forged Seamless Tubes, Welded Tubes, etc.
Daxun Alloy, as a leading titanium alloy tube manufacturer and supplier in China, provides high-quality Grade 5 titanium pipes to the world and has been well received by many projects.
Ti 6Al-4V (Grade 5 Titanium) is the most widely used of all titanium alloy tubes, accounting for more than 50% of the total titanium usage. It is usually used in the annealed state and has an operating temperature of up to 400°C (750°F). Ti 6Al/4V is welded with matching or ELI filler wire. Ti 6Al/4V has significantly higher strength than commercial pure titanium tubes, while having better stiffness and thermal properties (excluding thermal conductivity), and the thermal conductivity of Grade 5 titanium tube is about 60% lower than CP titanium. Among its many advantages, it can be heat treated. Thus, more ideal strength and performance are obtained. The advantages of using Grade 5 titanium seamless tubes include not only strong formability and low density, but also excellent corrosion resistance.
This grade is a perfect combination of strength, corrosion resistance, weldability and machinability. Therefore, it is widely used, such as in military aircraft or aviation industry, rocket parts, precision-guided components, armor parts, ship equipment, military vacuum equipment and other parts. The close version of 6-4, 6-4ELI, is also used in surgical implants. Typically, it is used in applications up to 400°C to improve ductility and toughness in cold working conditions. It also has excellent specific strength. It is usually provided in the annealed state and is easy to heat treat to increase strength for a variety of applications. As a general-purpose titanium alloy, Ti 6Al-4V titanium seamless tube has a wide range of ideal properties at temperatures around -210°C - 400°C. Grade 5 titanium alloy tube is the most commercialized of all titanium alloys. It combines high strength and toughness. Grade 5 titanium alloy tube has good welding and processing characteristics.
f4ec1052
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
These premium hot-finished titanium tubes are meticulously crafted through hot-rolling or hot-extrusion processes, followed by precise straightening, machining of both inside and outside diameters, and a polished surface finish. Available in heat-treated or non-heat-treated forms, our tubes undergo rigorous 100% ultrasonic flaw detection to ensure impeccable quality.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: Outer Diameter (OD) ranges from 19mm to 325mm, wall thickness from 9mm to 30mm, and lengths up to 5000mm, subject to mutual agreement between manufacturer and customer. - Hot-extruded Titanium Tubes: OD varies from 50mm to 160mm, wall thickness from 7mm to 35mm, and lengths up to 3000mm, also subject to mutual customer-manufacturer agreement.
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are offered in heat-treated forms, with surface etching, hydrostatic or ultrasonic testing based on manufacturing specifications. Available in OD ranges from 6mm to 89mm, wall thickness from 0.5mm to 11mm, and lengths up to 6000mm, these tubes are tailored to client specifications through mutual agreement.
Titanium Welded Pipes
DaXun specializes in manufacturing and supplying high-quality titanium pipes with diameters ranging from 12.7 mm to 38.1 mm (0.47 in to 1.5 in), wall thickness from 0.4 mm to 1.65 mm (0.016 in to 0.065 in), and lengths up to a substantial 25000 mm. Suitable for engineering and chemical industries, these pipes are crafted from flat rolled raw material using automatic tungsten inert gas (argon) welding, followed by on-line heat treatment. Each pipe undergoes comprehensive mechanical, geometric, ultrasonic, and eddy current testing, as well as pneumatic or hydrostatic testing, ensuring compliance with ASTM B 338 and ASME SB 338 standards. Pipes are meticulously packed according to client specifications, guaranteeing delivery of superior quality.
| CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium tube PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
• ASTE B338 - Titanium tubes standard, heat treatable
• AMS 4928 - Forgings and forging stock (annealed)
• AMS 4965 - Forgings (solution treated and aged)
• AMS 4967 - Forgings (annealed, heat treatable)
In the annealed state, hardness typically ranges from Rockwell C 30-34. Post solution treatment and aging, it increases to about Rockwell C 35-39.
Q1: What products can you offer?
A: We specialize in general steel types such as 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L. Additionally, we offer high-quality 300 and 400 series steels, as well as duplex stainless steel options including 2205, 2304, 2101, and 2507. For those seeking high-nickel alloys, we provide top-tier 904L, 800H, and 600H alloys.
400 series, and duplex stainless steel like 2205, 2304, 2101, 2507, and more. For high-nickel alloys, we offer exceptional 904L, 800H, and 600H varieties.
Q2. Can you produce the products according to my own drawings?
A: Yes, we can manufacture products based on your drawings to ensure they meet your exact specifications and satisfaction.
Q3. How does your factory handle quality control?
A: Quality is our top priority. We consistently place immense importance on quality control throughout the entire production process, from start to finish.
Q4. Can I request changes to the packaging and transportation methods?
A: Yes, we can adjust the packaging and transportation methods to suit your requirements. However, you will need to cover any additional costs and price differences that may arise during this period.
but you have to bear the costs incurred during this period and any associated spreads.
Q5. How does your factory handle quality control?
A: Quality is our top priority. We consistently place immense importance on quality control throughout the entire production process, from start to finish.
Q6. What is the delivery time?
A: The delivery time typically ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite the process to meet your deadlines.
Q7. What are your payment terms?
A: Our payment options include: A: 100% T/T advance, Western Union (For Small Orders) B: 30% T/T upfront and remaining 70% before shipment C: 100% Irrevocable LC at sight (For Large Orders)
B: 30% T/T and balance 70% before shipment
C: 100% Irrevocable LC at sight (For Big Orders)
Q8: Can you provide Deep Drawing Quality (DDQ) material?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, and more. Please specify your intended use, and we will tailor the mechanical properties to meet your exact requirements.
Q9: How can I obtain a sample?
A: We offer FREE samples for your inspection and testing. For small pieces, we may cover the courier costs depending on the circumstances.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}