| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition 201 Stainless Steel Rod
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties 201 Stainless Steel Rod
Mechanical property requirements for the annealed product as specified in ASTM A240 and ASME SA240
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
Mechanical property requirements for cold-worked flat-rolled products as specified in industry standards ensure exceptional quality and reliability. 201 Stainless Steel Rod: Engineered for Precision and Durability
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Physical Properties: Unmatched Strength and Resilience
Physical Properties for Type 201 Stainless Steel Rod: Optimized for Superior Performance
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Our forming capabilities include state-of-the-art radial forging machines, advanced heat treatment furnaces, high-efficiency melting furnaces, and precision rolling mills for manufacturing titanium rods, complemented by a unique hydroforming process to create complex parts with unmatched precision.
Stainless steel rod heat treatment utilizes cutting-edge furnace technology to guarantee the stability and high performance of each material, making every rod a pinnacle of quality.
Daxun Stainless Steel employs the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace to meticulously reduce impurities and significantly enhance the performance of our high-quality stainless steel rods.
Our high-caliber stainless steel products are not only fully certified but also entirely traceable. We pride ourselves on supplying the utmost quality stainless steel to a diverse range of top-tier industries, including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you manufacture Stainless Steel grinding bars & rods?
Yes, we specialize in producing Stainless Steel grinding bars & rods that offer outstanding precision in dimension, roundness, and straightness. These qualities surpass those of standard polished bars, though the processing costs are correspondingly higher.
Q1: What range of products do you offer?
A: We provide a comprehensive selection of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series,
400 series, as well as duplex stainless steels like 2205, 2304, 2101, 2507, and high-nickel alloys such as 904L, 800H, and 600H.
Q2: Can you produce items based on my custom drawings?
Yes, we can manufacture products precisely according to your drawings to ensure they meet your exact specifications and satisfaction.
Q3: How does your factory ensure quality control?
Quality is our top priority. We implement rigorous quality control processes from the initial stage through to the final product to ensure superior quality.
Q4: Can I request changes to the packaging and transportation methods?
Yes, we can modify packaging and transportation methods to meet your specific requirements,
though you will need to cover any additional costs incurred during this process.
Q5: How does your factory manage quality control?
Quality is paramount to us. From start to finish, we maintain stringent quality control measures to ensure the highest standards.
Q6: What is your lead time for deliveries?
A: Our delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite the production process to meet your deadlines.
Q7: What are your payment terms?
A: 100% T/T advance, or Western Union for smaller orders.
B: 30% T/T upfront, with the remaining 70% due before shipment.
C: 100% Irrevocable LC at sight for larger orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we offer DDQ materials suitable for manufacturing stainless steel pots, sinks, bowls, etc. Let us know your specific applications, and we will tailor the mechanical properties to your needs.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation. For small pieces, we may also cover courier costs, depending on the situation.
Q10: To which countries have you exported your products?
A: So far, we have shipped our stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}