| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys is a premier global producer and supplier of superior Grade 1 titanium plates, synonymous with quality and reliability in the market.
Pure Grade 1 titanium plate boasts exceptional ductility and cold formability, perfect for deep drawing applications. This grade is renowned for its outstanding resistance to general and seawater corrosion, as well as its resilience against oxidizing, neutral, and mildly reducing solutions, including chlorides. With a low density-approximately half that of nickel-based alloys-and a high strength-to-weight ratio, Grade 1 titanium is ideal for challenging chemical environments. It is the softest and most ductile of commercially pure titanium grades, offering excellent cold formability, corrosion resistance, weldability, and impact hardness.
As leading producers of ASTM B265 Titanium Grade 1 plates, Jiangsu Daxun Alloy Co., Ltd. supplies a variety of products including Titanium Gr 1 Sheets, Finished Plates, Coils, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, and Perforated Plates. We serve as a trusted manufacturer and dealer of Grade 1 Titanium Sheets and Plates, meeting the highest standards in China.
We ensure customers receive their Grade 1 titanium plate products promptly with our streamlined delivery process. Daxun's integrated system supports production capacity, information flow, logistics, and capital flow. Order data is pushed to the logistics system in real-time, ensuring seamless data connection. Strategically located processing centers near highways, rivers, and seas enable efficient scheduling, rapid response, and effective storage and transportation linkage, guaranteeing timely task completion.
Grade 1 titanium plate, distinguished by its lower density and high ductility, is ideal for industries focused on weight and deep drawing processes. Key sectors include medical, chemical equipment, and aerospace. The plate's strength and corrosion resistance make it suitable for marine, chemical processing, and desalination industries. Typical applications encompass oil and gas components, reaction and pressure vessels, piping systems, power generation, heat exchangers, linings, flue gas desulfurization systems, and numerous other industrial components. Common standards include ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, and AMS4972.
The cold rolled thickness range for Grade 1 Titanium Plates spans 0.3 mm to 6.0 mm, while hot rolled plates range from 4.76 mm to 155 mm. These plates are available in hot rolled or heat treated conditions, produced through longitudinal and transverse rolling. If needed, creep flattening can be employed as a heat treatment to relieve internal stresses and meet specific flatness requirements. Plates can also be supplied as cut blanks, tailored to complex shapes from a parent plate, with further processing-mechanical or chemical-dependent on customer requirements.
About the chemical composition of (Ti 6AL-4V) Grade 5 Titanium Sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of Grade 2 TitaniumSheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of Grade 2 Titanium Sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is a distinguished metal expert, specializing in both small and large-scale titanium plate projects. DAXUN is your definitive reference point and committed long-term partner, poised to supply your business with premium titanium plates and comprehensive technical assistance. More than just a supplier of industrial pure titanium plates and titanium alloy plates, DAXUN serves as your strategic ally, equipped to help you navigate any challenges and meet your needs, ensuring the successful realization of your project goals.
DAXUN's service center in China boasts a ready stock of titanium plate products for swift order fulfillment. By offering basic processing, precision water jet cutting, and efficient plate nesting products, we add significant value for our customers, optimizing both their time and costs.
Our relentless investment in production facilities and capacity agreements with our partners guarantee that DAXUN remains at the forefront of titanium plate quality, both now and in the future.
Contact DAXUN today to receive the most competitive titanium plate prices and up-to-date technical information.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! With the goal of creating the world's high-performance titanium alloy plates. We deliver quickly worldwide - ASTM B265 Grade 2, Grade 5 Titanium Plates. DAXUN produces and stocks alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled. 6.0-50mm is hot rolled, and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is the "workhorse" of titanium alloy materials. It combines high strength, ductility and excellent corrosion resistance, high temperature resistance, thus being favored by many general and military industries. Compliant with: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, etc.
Ti-6Al-4V grade 5 titanium plate is mainly used in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, marine industry, etc.
Grade 1
Today, DAXUN Alloys is a leading global producer and supplier of high-quality Grade 1 titanium plate.
Pure Grade 1 titanium plate has excellent ductility and cold formability, making it ideal for deep drawing. Grade 1 titanium is known for its excellent general and seawater corrosion resistance, as well as its resistance to oxidizing, neutral and mildly reducing media (solutions), including chlorides. Titanium's low density (about half that of nickel-based alloys), high strength-to-weight ratio and corrosion resistance make it an excellent choice for a wide range of harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile. It has good cold formability and excellent corrosion resistance. It also has excellent weldability and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the "workhorse" of the commercially pure titanium family. It combines high strength, ductility, and excellent corrosion resistance for many industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate. It offers an excellent balance between strength and ductility. It has good impact strength and is easily weldable. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. It also has excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an ideal material for a wide range of applications, and it effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is a metal expert focused on small and large titanium plate projects. DAXUN is your reference point and long-term partner, ready to provide you and your business with titanium plates and any technical assistance you may need. You can consider DAXUN not only as your supplier of industrial pure titanium plates and titanium alloy plates, but also as your strategic partner to help you meet any challenges and needs you may encounter, ultimately allowing you to achieve your project goals.
At Jiangsu Daxun Alloy Co., Ltd., our China-based DAXUN service center maintains a robust inventory of titanium plate products, ensuring swift and efficient order processing. By leveraging advanced services such as basic processing, water jet cutting, and precise plate nesting, we deliver unparalleled value to our customers, significantly reducing both time and costs.
Through relentless investment in cutting-edge production facilities and strategic capacity agreements with our esteemed partners, DAXUN remains a leader in titanium plate quality. This commitment ensures that our products set the benchmark for excellence both now and in the future.
Reach out to DAXUN today to access the latest pricing and comprehensive technical details on our superior titanium plates. Your journey towards premium quality starts with us.
Q1: What products can you offer?
A: We proudly offer a wide range of premium steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, our selection features high-quality duplex stainless steel like 2205, 2304, 2101, 2507, and high-nickel alloys such as 904L, 800H, and 600H.
A: Furthermore, we specialize in an extensive variety of 400 series stainless steels, ensuring we meet diverse industry needs and applications.
Q2. Can you produce the products according to my own drawings?
Yes, we can craft customized products precisely to your specifications, ensuring complete satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We meticulously oversee quality control processes from start to finish, ensuring exceptional product standards.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify packaging and transportation methods to meet your specific requirements,
but please note that any additional costs and price differences incurred during this period will be your responsibility.
Q5. How does your factory handle quality control?
Quality is our utmost priority. We implement rigorous quality control measures from the beginning to the end to ensure superior product quality.
Q6. How long is the delivery time?
A: Standard delivery time ranges from 7 to 20 working days after payment confirmation.
If your order is urgent, we can expedite the process to prioritize your needs.
Q7. What are your payment terms?
A: 100% T/T advance, Western Union (For Small Orders)
B: 30% T/T upfront, with the balance of 70% paid before shipment
C: 100% Irrevocable LC at sight (For Large Orders)
Q8: Can you produce Deep Drawing Quality (DDQ)?
A: Yes, we can. Our materials are suitable for a variety of stainless steel products such as pots, sinks, and bowls. Provide us with your specific usage requirements, and we will tailor the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: FREE samples are available for your inspection and testing. For small pieces, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: To date, our stainless steel materials have been exported to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
){kind=link}