| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a premier global producer and supplier of top-tier Grade 1 titanium plates.
Pure Grade 1 titanium plate boasts exceptional ductility and cold formability, making it perfect for deep drawing applications. This titanium grade is celebrated for its outstanding resistance to general and seawater corrosion, as well as its resilience against oxidizing, neutral, and mildly reducing environments, including chlorides. With a low density-approximately half that of nickel-based alloys-a high strength-to-weight ratio, and remarkable corrosion resistance, Titanium Grade 1 is an ideal choice for various harsh chemical conditions. Known for being the softest and most ductile among commercially pure titanium grades, it offers superb cold formability, excellent weldability, and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
We excel in providing customers with quick and reliable delivery of Grade 1 titanium plate products. This speed is enabled by a comprehensive system encompassing production capacity, information flow, logistics, and capital flow. For instance, Daxun's order data is instantly integrated into the logistics system, ensuring seamless data connectivity. Logistically, our processing center's strategic proximity to highways, rivers, and seas ensures efficient scheduling, rapid responses, synchronized storage and transportation, and efficient loading-guaranteeing timely task completion.
Grade 1 titanium plate's lower density and increased ductility make it ideal for industries requiring weight sensitivity and deep drawing processes. Key sectors include medical, chemical equipment, and aerospace. The strength and corrosion resistance of Grade 1 titanium plates also make them perfect for marine, chemical processing, and desalination applications. Typical uses encompass oil and gas components, reaction and pressure vessels, piping systems, power generation, heat exchangers, linings, flue gas desulfurization systems, and many other industrial elements. Common standards include ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, AMS4972.
The cold-rolled thickness range for Grade 1 Titanium Plates spans from 0.3 mm to 6.0 mm, available in hot rolled or heat-treated conditions. The hot rolled thickness range extends from 4.76 mm to 155 mm, produced via longitudinal and transverse rolling. These plates can also undergo creep flattening to relieve internal stresses and meet specific flatness requirements. Additionally, plates can be supplied as cut blanks, which are complex shapes cut from the parent plate, with further mechanical or chemical processing tailored to customer specifications.
About the chemical composition of (Ti 6AL-4V) Grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of Grade 2 titanium sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of Grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN stands as a distinguished authority in metal fabrication, specializing in both small and large-scale titanium plate projects. Serving as your pivotal reference point and enduring partner, DAXUN is poised to deliver top-tier titanium plates along with comprehensive technical support tailored for your business. Beyond being a mere supplier of industrial pure titanium plates and titanium alloy plates, DAXUN positions itself as your strategic ally, ready to navigate any challenges and fulfill all your requirements, ensuring the triumphant realization of your project ambitions.
Strategically located in China, DAXUN's service center boasts a robust inventory of titanium plate products, guaranteeing prompt order fulfillment. Leveraging foundational processing, precision water jet cutting, and efficient plate nesting services, we offer unparalleled added value, substantially reducing both time and costs for our esteemed customers.
DAXUN's unwavering commitment to excellence is reflected in our continuous investment in state-of-the-art production facilities and strategic capacity agreements with our partners. This ensures that DAXUN remains at the pinnacle of titanium plate quality, both now and in the foreseeable future.
Reach out to DAXUN today to access the most competitive titanium plate prices and cutting-edge technical insights.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN proudly stands as a premier manufacturer and supplier of Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plates from China. Our mission is to produce the world's highest-performance titanium alloy plates and ensure swift global delivery. We offer ASTM B265 Grade 2 and Grade 5 Titanium Plates with thicknesses ranging from 0.5mm to 300mm-cold rolled for 0.5mm-6.0mm, hot rolled for 6.0mm-50mm, and forged for thicknesses above 50mm. Grade 5 titanium plate (Ti-6Al-4V) is renowned as the 'workhorse' of titanium alloys, combining exceptional strength, ductility, and resistance to corrosion and high temperatures. This makes it a preferred choice for both general and military industries. Our products comply with numerous standards including ASTE, ASME, AMS, GB, GJB, MIL, JIS, and EN.
The Ti-6Al-4V grade 5 titanium plate is extensively utilized in industries such as aerospace, military, power, vehicle armor, rocket precision guidance, and marine applications.
Grade 1
Today, Jiangsu Daxun Alloys is celebrated as a leading global producer and supplier of premium Grade 1 titanium plates.
Pure Grade 1 titanium plates from DAXUN offer exceptional ductility and cold formability, making them perfect for deep drawing applications. Grade 1 titanium is distinguished by its outstanding general and seawater corrosion resistance, as well as its resilience against oxidizing, neutral, and mildly reducing environments, including chloride solutions. With a low density (approximately half that of nickel-based alloys), high strength-to-weight ratio, and superior corrosion resistance, Grade 1 titanium is ideal for a variety of harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile, providing good cold formability, excellent weldability, and impressive impact hardness.
We produce ASTM B265 Titanium Gr 1 Plates, Titanium Gr 1 Sheets, Finished Plates, Coils, Pure Titanium Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, Perforated Plates, and more. As a leading manufacturer in China, we ensure our products meet the highest quality standards and diverse application needs.
Grade 2
DAXUN manufactures and stocks commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the 'workhorse' of the commercially pure titanium family, recognized for its superior strength, ductility, and excellent corrosion resistance in various industrial applications.
Grade 2 Titanium Plates offer a remarkable balance between strength and ductility. They possess good impact strength, are easily weldable, and demonstrate excellent corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, they exhibit outstanding resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and resistance to corrosion make Grade 2 Titanium Plates an excellent choice for numerous applications. These plates effectively combat stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C, making them ideal for industrial applications requiring high ductility and corrosion resistance. With a melting point of 1660°C, Grade 2 Titanium Plates are the preferred material for various demanding environments.
DAXUN is a titanium plate specialist dedicated to both small and large-scale projects. Beyond being just a supplier, DAXUN is your strategic partner, ready to provide technical assistance and high-quality titanium plates to help you overcome challenges and achieve your project goals. Trust DAXUN to support your business with premium titanium solutions and unparalleled service.
Located in the heart of China, DAXUN's state-of-the-art service center boasts an extensive inventory of premium titanium plate products, ensuring swift and efficient order processing. By offering essential processing services, precision water jet cutting, and optimized plate nesting solutions, we deliver unparalleled added value to our customers-saving them both time and money.
DAXUN continually propels itself to the pinnacle of titanium plate excellence through relentless investment in cutting-edge production facilities and strategic capacity agreements with trusted partners. Our unwavering commitment guarantees that DAXUN remains a leading authority in titanium plate quality, both today and in the foreseeable future.
Reach out to DAXUN today to secure the most competitive titanium plate prices and obtain comprehensive technical information. Let us provide the expertise and materials you need to succeed.
Q1: What products can you offer?
A: We offer a wide range of high-quality steel types including general steels like 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and 300 series. In addition, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
400 series, and duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Absolutely, we can manufacture products according to your drawings to ensure they meet your exact specifications and satisfaction.
Q3. How does your factory do regarding quality control?
A: Quality is our top priority. We maintain stringent quality control measures from the initial stages to the final product to ensure excellence.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can modify the packaging and transportation form to meet your requirements.
However, you will need to cover any additional costs incurred during this period.
Q5. How does your factory do regarding quality control?
A: Quality is our top priority. We maintain stringent quality control measures from the initial stages to the final product to ensure excellence.
Q6. How long is the delivery time?
A: Delivery is typically within 7 to 20 working days after payment confirmation. For urgent orders, we will expedite the process to meet your deadlines.
If the order is urgent, we will push our workshop to finish in advance.
Q7. What is your Payment?
A: We offer several payment options: 100% T/T advance, Western Union for small orders, and 30% T/T with the balance of 70% before shipment.
B: 30% T/T in advance, with the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for deep drawing applications such as stainless steel pots, sinks, and bowls. Provide us with your specific use case, and we will tailor the mechanical properties to meet your needs.
Q9: How to get a sample?
A: We offer FREE samples for your evaluation and testing. If you require a small piece, we can cover the courier costs depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have successfully exported our stainless steel materials to a wide range of countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will be there to pick you up.
){kind=link}