| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Discover the unparalleled quality of our ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, and more. As top manufacturers and suppliers in China, we offer an extensive range of Stainless Steel 410 products including Round Bars, Bright Bars, Polished Bars, and Rods. Partner with us and access superior Stainless Steel 410 materials that meet your specifications.
For further details on our premium stainless steel rods, please contact Daxun.
410 Stainless Steel Rod Chemical Composition
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our forming capabilities include cutting-edge radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills. We also employ a unique hydroforming process for manufacturing high-quality titanium rods and parts.
Utilizing advanced heat treatment furnace equipment, we ensure the stability and high performance of our stainless steel rods.
Equipped with the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun reduces impurities during smelting, enhancing the performance of our stainless steel rods.
Our premium stainless steel products come with full certification and traceability, ensuring the highest standards of quality. We proudly serve leading industries such as aerospace, industrial, medical, marine, and military sectors with our top-tier stainless steel.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
Explore our specific product pages for detailed size options, and feel free to reach out for a quote on any custom size orders.
The 410 Stainless Steel Round Bars from Jiangsu Daxun Alloy Co., Ltd. are extensively utilized across various sectors ranging from construction to automotive manufacturing. Due to their versatile applications, Daxun Alloys provides these round bars in diverse grades and dimensions. Our complimentary advanced cutting service ensures that your specifications are met with precision every time.
Q: Can you produce SS grinding bars and rods?
A: Yes, we specialize in producing SS grinding bars and rods that feature precise dimension, roundness, and straightness, superior to regular stainless steel polished bars. Please note that the processing cost is higher.
Q1: What products can you offer?
A: We offer a wide range of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L.
Additionally, we provide 400 series and duplex stainless steel like 2205, 2304, 2101, 2507, and high-nickel alloys such as 904L, 800H, and 600H.
Q2. Can you produce products according to my drawings?
A: Absolutely, we can manufacture products tailored to your drawings to ensure your utmost satisfaction.
Q3. How does your factory handle quality control?
A: Quality is our top priority. We are committed to stringent quality control practices from start to finish.
Q4. Can I request changes to the packaging and transportation form?
A: Yes, we can adjust the packaging and transportation form according to your requirements.
However, any additional costs incurred during this period will be borne by you.
Q5. How does your factory handle quality control?
A: Quality is our top priority. We are committed to stringent quality control practices from start to finish.
Q6. What is your delivery time?
A: Our delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite production in our workshop to complete ahead of schedule.
Q7. What are your payment terms?
A: We offer the following payment options:
B: 30% T/T in advance and 70% balance before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you produce Deep Drawing Quality (DDQ) material?
A: Yes, we produce DDQ material suitable for stainless steel pots, sinks, bowls, etc. Let us know your application, and we will adjust the mechanical properties to meet your specific requirements.
Q9: How can I get a sample?
A: We provide FREE samples for your evaluation and testing. If you only need a small piece, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}