| Type: | Stainless Steel Bars |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | 310 310S S31008 |
| Certification: | ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS |
| Shape: | Round |
| Technique: | Hot Rolled |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys is a distinguished manufacturer of premium-quality SS 310/310S Round Bars, known for their remarkable characteristics. These austenitic stainless steel bars, based on chromium and nickel, exhibit exceptional durability, flexibility, workability, machinability, weldability, ductility, fabricability, high strength, and hardness. SS 310/310S Round Bars are particularly useful in industrial chemistry and nut manufacturing. Their anti-corrosion properties make them highly popular in the market. They can withstand extreme temperatures and are suitable for use at annealing temperatures without deforming. We supply these superior stainless steel round bars to our esteemed clients at competitive market prices. Furthermore, we offer customization in various finishes, lengths, and shapes to meet specific client requirements, ensuring their seamless integration in industrial applications.
For more information on stainless steel rods, please contact Daxun.
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our advanced forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods, along with a unique hydroforming process for fabricating parts.
Our sophisticated heat treatment furnace equipment ensures the stability and high performance of stainless steel rods.
At Jiangsu Daxun Alloy Co., Ltd., our stainless steel production harnesses the unparalleled capabilities of cutting-edge smelting technology. Utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, we meticulously eliminate impurities during the smelting process. This rigorous approach not only enhances the purity but also significantly boosts the performance and quality of our ASTM A276 High Temperature 310S Stainless Steel Round Rods, ensuring superior reliability and durability in every application.
Our premium stainless steel offerings are not only fully certified but also meticulously traceable, ensuring top-notch quality. We proudly supply our superior stainless steel products to leading industries such as aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and pipes offer unparalleled resistance to both corrosion and heat, even in the most stringent environments.
Stainless steel round bars are extensively employed across various industries, from construction to automotive parts. Given the diverse applications, Daxun Alloys offers a range of stainless steel round bars in multiple grades and sizes. Our advanced cutting service ensures precise customization to meet your specific requirements every time.
Discover the ease of ordering our premium stainless steel round bars, available in an extensive range of sizes to suit your every need. Choose the exact grade of steel you desire, and we'll supply bars in lengths ranging from 500mm to 6 meters, with diameters from 3mm to an impressive 500mm. Whether you prefer metric or imperial measurements, our flexible ordering process ensures you get precisely what you need.
For those unique, non-standard size requirements, Jiangsu Daxun Alloy Co., Ltd. has got you covered. We offer unlimited complimentary cuts to length, utilizing advanced bandsaw technology to guarantee precision and consistency with every order. Just specify your custom dimensions when placing your order, and experience unmatched accuracy and satisfaction.
Can you produce SS grinding bars and rods?
Yes, we specialize in crafting SS grinding bars and rods with impeccable precision in dimensions, roundness, and straightness. These are superior to traditional polished bars, though the advanced processing incurs higher costs.
Q1: What products can you offer?
A: We offer an extensive range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 300 series.
Additionally, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2: Can you produce products according to my own drawings?
A: Absolutely, we can manufacture products tailored to your specific drawings, ensuring they meet your exact requirements.
Q3: How does your factory manage quality control?
A: Quality is our top priority. We maintain stringent quality control processes from the initial stages to final production.
Q4: Can I request changes to packaging and transportation?
A: Yes, we can modify packaging and transportation methods to meet your needs.
Please note, you will need to cover any additional costs and differences incurred during this process.
Q5: How does your factory manage quality control?
A: Quality is our top priority. We maintain stringent quality control processes from the initial stages to final production.
Q6: How long is the delivery time?
A: Delivery takes between 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite production to meet your timeline.
Q7: What are your payment terms?
A: 100% T/T in advance or Western Union for small orders.
B: 30% T/T deposit with the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) material?
A: Yes, we can. Our materials are ideal for stainless steel pots, sinks, bowls, etc. Provide your usage requirements, and we'll adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: We offer FREE samples for inspection and testing. For small pieces, we may cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and beyond.