| Product Parameters: Stainless Steel rod | |
| Material | 2507 S32750 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Our product range includes the ASTM A276 Super Duplex Steel S32750 Round Bar, Super Duplex Steel Bar Supplier, Super Duplex Steel UNS S32760 Bright Bar, Super Duplex Steel 2507 Bar, Super Duplex Steel UNS S32950 Flat Bar, Austenitic Super Duplex Steel S32760 Round Bar, Hot Rolled Super Duplex Steel S32760 Round Bar, Super Duplex Steel S32760 Round Bar, and the Super Duplex Steel UNS S32750-proudly manufactured in China.
For more comprehensive information on our stainless steel rods, please contact Daxun.
2507 Stainless Steel Rod Chemical Composition
| Grade | Super Duplex 2507 |
| UNS Designation | S32750 |
| Carbon (C) Max. | 0.03 |
| Manganese (Mn) Max. | 1.2 |
| Phosphorous (P) Max. | 0.035 |
| *** (S) Max. | 0.02 |
| Silicon (Si) Max. | 0.8 |
| Chromium (Cr) | 24.0-26.0 |
| Nickel (Ni) | 6.0-8.0 |
| Molybdenum (Mo) | 3.0-5.0 |
| Nitrogen (N) | 0.24-0.32 |
| Iron (Fe) | Bal. |
| Copper (Cu) | 0.5 |
| Other Elements | - |
| Physical Properties of Super Duplex 2507 Alloys in the Annealed Condition at -20°F to +100°F | ||||||||||||||
| Tensile Strength | Yield Strength | |||||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
| Super Duplex 2507 | S32950 | A789, A790 | 100,000 | 690 | 100 | 70,000 | 485 | 70 | 20 | - | 30.5 Rc | - | - | - |
| Super Duplex 2507 | S32750 | A789, A790 | 116,000 | 800 | 116 | 80,000 | 550 | 80 | 15 | - | 32 Rc | 27.5 | 7.2 | 98 |
| Density, lb/in3 | 0.28 |
| Modulus of Elasticity, psi | 29.0x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 7.5 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 8 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microhm-in | 31.5 |
Our state-of-the-art forming capabilities include radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods, complemented by a unique hydroforming process for producing intricate parts.
We utilize cutting-edge heat treatment furnace equipment to ensure the stability and high performance of our stainless steel rods.
Daxun Stainless Steel employs the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace to minimize impurities during the smelting process, thereby enhancing the performance of our finished stainless steel rods.
Our stainless steel products are meticulously certified and fully traceable. We pride ourselves on supplying the highest quality stainless steel to premier industries such as aerospace, industrial sectors, medical fields, marine applications, and military operations.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you manufacture SS grinding bars and rods?
Yes, we specialize in producing SS grinding bars and rods that boast precise dimensions, impeccable roundness, and exceptional straightness. While superior to stainless steel polished bars, please note that the processing costs are higher.
Q1: What range of products can you provide?
A: We offer a diverse array of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 and
400 series stainless steel. Our selection also includes duplex stainless steels like 2205, 2304, 2101, 2507, and high-nickel alloys such as 904L, 800H, and 600H.
Q2: Can you manufacture products according to my custom drawings?
Absolutely. We are adept at producing products tailored to your specific drawings to ensure complete satisfaction.
Q3: How does your factory ensure quality control?
Quality is our top priority. We rigorously maintain quality control measures from the initial stages to the final product.
Q4: Can the packaging and transportation method be altered upon request?
Yes, we can customize packaging and transportation methods to suit your needs,
although any additional costs incurred during this modification will be your responsibility.
Q5: How does your factory handle quality control?
Ensuring top-notch quality is our highest priority. We consistently enforce stringent quality control processes from start to finish.
Q6: What is your typical delivery time?
A: The standard delivery time is 7-20 working days post-payment confirmation.
For urgent orders, we expedite the process to complete your order ahead of schedule.
Q7: What are your payment terms?
A: 100% T/T in advance, or Western Union (suitable for small orders).
B: 30% T/T upfront, with the remaining 70% due before shipment.
C: 100% Irrevocable Letter of Credit (LC) at sight (ideal for large orders).
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Certainly. Our materials are perfect for manufacturing stainless steel pots, sinks, bowls, and more. Share your specific usage requirements with us, and we will adjust the mechanical properties to meet them.
Q9: How can I obtain a sample?
A: We provide FREE samples for your evaluation and testing. For small sample pieces, we may cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}