| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For more information on our premium stainless steel rods, please get in touch with Daxun.
304 Stainless Steel Rod - Chemical Composition
Chemical Composition (wt%) limits as per ASTM A240 and ASME SA240* standards.
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod - Mechanical Properties
Mechanical property requirements for annealed products as specified in ASTM A240 and ASME SA240.
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod - Physical Properties
Physical properties for Type 304/304L stainless steel.
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our advanced forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods. Additionally, we employ a unique hydroforming process for creating intricate parts.
Our stainless steel rod heat treatment employs advanced furnace equipment, ensuring material stability and superior performance.
At Daxun Stainless Steel, we employ the world's most advanced smelting technology. Utilizing state-of-the-art vacuum induction furnaces, vacuum consumable furnaces, and electroslag furnaces, we meticulously minimize impurities during the smelting process. This rigorous approach significantly enhances the purity and performance of our finished 304L Stainless Steel Round Rods, ensuring they meet the highest standards for food processing and other critical applications.
Our stainless steel products are meticulously certified and fully traceable, ensuring unparalleled quality. We proudly supply top-tier stainless steel to the most demanding industries, including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
The DAUXN 304/304L Stainless Steel RODS find their place in a myriad of home and commercial settings, such as:
Can you provide stainless steel grinding bars and rods?
Absolutely! We specialize in producing stainless steel grinding bars and rods that boast precise dimensions, impeccable roundness, and exceptional straightness. These qualities surpass those of standard stainless steel polished bars, though they come with a higher processing cost.
Q1: What products are available from Jiangsu Daxun Alloy Co., Ltd.?
A: We provide a diverse range of steel types including general grades like 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series,
as well as 400 series, and duplex stainless steels such as 2205, 2304, 2101, 2507, 904L, 800H, and 600H high-nickel alloys.
Q2. Can you manufacture products based on my custom drawings?
Yes, we can manufacture products tailored to your drawings, ensuring they meet your highest satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We consistently emphasize rigorous quality control from start to finish.
Q4. Can I request changes in packaging and transportation methods?
Yes, we can modify the packaging and transportation methods according to your specifications,
though you will need to cover any additional costs incurred during this process.
Q5. How does your factory manage quality control?
Quality is paramount. We always maintain strict quality control measures throughout the entire production process.
Q6. What is the estimated delivery time?
A: Delivery typically takes 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite the production process to meet your requirements.
Q7. What are your payment terms?
A: 100% T/T in advance, Western Union (for small orders)
B: 30% T/T upfront and the remaining 70% before shipment
C: 100% Irrevocable Letter of Credit (LC) at sight (for large orders)
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, and more. You can inform us of your specific application, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation and testing. For small pieces, we can cover the courier cost, depending on the situation.
Q10: Which countries have you exported your products to?
A: To date, we have exported our stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and numerous other countries.
){kind=link}