| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | GR1 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a preeminent global producer and supplier of superior Grade 1 titanium plates.
Pure Grade 1 titanium plate boasts unparalleled ductility and cold formability, perfect for deep drawing applications. With exceptional general and seawater corrosion resistance, Grade 1 titanium stands resilient against oxidizing, neutral, and mildly reducing media, including chlorides. This low-density metal (about half that of nickel-based alloys) offers a high strength-to-weight ratio and robust corrosion resistance, making it an optimal choice for challenging chemical environments. As the softest and most ductile commercially pure titanium, Grade 1 also excels in cold formability, corrosion resistance, weldability, and impact hardness.
Leading the market as ASTM B265 Titanium Gr 1 Plate Producers, we offer Titanium Gr 1 Sheets, Finished Plates, Coils, and more. From Hot Rolled to Cold Rolled Plates, we provide a comprehensive range of Titanium Gr 1 Sheets and Plates, including Patterned and Perforated options, all manufactured to the highest standards in China.
We pride ourselves on delivering Grade 1 titanium plate products with prompt efficiency. Our seamless system integrates production capacity, information flow, logistics, and capital flow to ensure timely delivery. Real-time data pushes order information directly to our logistics system, enabling flawless coordination. Strategically located processing centers near highways, rivers, and seas ensure quick responses, streamlined scheduling, and efficient storage and transportation, guaranteeing timely completion of tasks.
With its lower density and high ductility, Grade 1 titanium plate is ideal for weight-sensitive industries and deep drawing processes. Key sectors include medical, chemical equipment, and aerospace. Its strength and corrosion resistance also make it suitable for marine, chemical processing, and desalination applications. Typical uses for Grade 1 titanium encompass oil and gas components, reaction and pressure vessels, piping systems, power generation, heat exchangers, linings, and flue gas desulfurization systems. Adhering to standards such as ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, and AMS4972, ensures the highest quality and reliability.
Our precision cold-rolled Grade 1 Titanium Plates range from 0.3 mm to 6.0 mm in thickness, while hot-rolled plates span 4.76 mm to 155 mm. Produced through longitudinal and transverse rolling, these plates can be supplied hot-rolled or heat-treated. When necessary, creep flattening is employed as a heat treatment to alleviate internal stresses and meet special flatness requirements. Plates are available as cut blanks or complex shapes, tailored to customer specifications with further mechanical or chemical processing as needed.
Comprehensive Information about the Chemical Composition of (Ti 6AL-4V) Grade 5 Titanium Sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
Insights into the Chemical Composition of Grade 2 TitaniumSheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Examination of the Mechanical Properties of Grade 2 Titanium Sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is a leading authority in the realm of metal, specializing in both small and large-scale titanium plate projects. As your trusted reference point and dedicated long-term partner, DAXUN stands ready to cater to all your business needs with premium titanium plates and comprehensive technical assistance. Position DAXUN not just as your supplier of industrial pure titanium and titanium alloy plates, but as a strategic ally committed to overcoming any challenges and requirements you may face, ensuring the successful realization of your project ambitions.
Our state-of-the-art service center in China maintains an extensive inventory of titanium plate products, enabling swift order fulfillment. Leveraging basic processing, advanced water jet cutting, and efficient plate nesting, we deliver exceptional value to our clients, significantly reducing both time and costs.
DAXUN's relentless investment in cutting-edge production facilities and strategic capacity agreements with our partners ensure we remain at the pinnacle of titanium plate quality-both now and in the future.
Reach out to DAXUN today to receive the most up-to-date pricing and technical details on our titanium plates.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is your premier manufacturer and supplier of Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plates from China! Our mission is to craft the world's highest-performing titanium alloy plates. We offer rapid global delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. DAXUN specializes in producing and stocking Grade 5 (UNS R56400) alloy titanium plates, available in thicknesses from 0.5mm to 300mm. Cold rolled options range from 0.5mm-6.0mm, hot rolled from 6.0-50mm, and forged for 50mm and above. Grade 5 titanium plate (Ti-6Al-4V) is celebrated as the 'workhorse' of titanium alloys, known for its high strength, ductility, superb corrosion resistance, and high temperature tolerance, making it highly sought after in both general and military industries. Compliance standards include: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
Ti-6Al-4V Grade 5 Titanium Plate: Essential for Aerospace, Military, Power Industry, Vehicle Armor, Rocket Precision Guidance Parts, Marine Industry, and Beyond
Grade 1
DAXUN Alloys: Your Leading Global Producer and Supplier of High-Quality Grade 1 Titanium Plates
Pure Grade 1 Titanium Plate: Unmatched in Ductility and Cold Formability, Perfect for Deep Drawing. Renowned for its excellent resistance to general and seawater corrosion, as well as resistance to oxidizing, neutral, and mildly reducing solutions, including chlorides. With a low density (about half that of nickel-based alloys), high strength-to-weight ratio, and outstanding corrosion resistance, it is the material of choice for a variety of challenging chemical environments. Commercially pure Grade 1 titanium is the softest and most ductile of titanium grades, offering excellent cold formability, corrosion resistance, weldability, and impact hardness.
Your Trusted Source in China for ASTM B265 Titanium Gr 1 Plates: Producers, Suppliers, and Dealers of Titanium Gr 1 Sheets, Finished Plates, Coils, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, Perforated Plates, and More.
Grade 2
DAXUN: Proud Producers and Stockists of Commercially Pure Grade 2 (UNS R50400) Titanium Plates in Thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is known as the 'workhorse' of commercially pure titanium, boasting high strength, ductility, and excellent corrosion resistance, making it ideal for numerous industrial applications.
Grade 2 Titanium Plate: The Perfect Balance of Strength and Ductility. Its superior impact strength and weldability, combined with excellent corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, wet ***, and seawater, make it the material of choice for a multitude of demanding applications.
With its low density, high strength-to-weight ratio, and exceptional corrosion resistance, titanium is ideal for a diverse array of applications. Grade 2 Titanium Plate resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. Its melting point of 1660°C further establishes it as the preferred alloy for most industrial applications requiring superior ductility and corrosion resistance.
DAXUN: Your Titanium Plate Specialist for Both Small and Large Projects. As your trusted reference point and long-term partner, DAXUN is committed to providing you with top-quality titanium plates and comprehensive technical assistance. Consider DAXUN not just as a supplier, but as a strategic ally dedicated to helping you overcome any challenges and achieve your project goals.
At DAXUN's state-of-the-art service center in China, we maintain a robust stock of titanium plate products, ensuring rapid order fulfillment. Our advanced services, including basic processing, precision water jet cutting, and meticulous plate nesting, deliver exceptional added value, significantly reducing both time and costs for our esteemed customers.
DAXUN's unwavering commitment to continuous investment in our cutting-edge production facilities, coupled with strategic capacity agreements with our esteemed partners, guarantees that we remain pioneers in delivering unparalleled titanium plate quality, both now and well into the future.
Reach out to DAXUN today for the most competitive titanium plate prices and comprehensive technical information available.
Q1: What products can you offer?
A: We provide a diverse range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, our selection encompasses high-performance alloys such as 316L 300, 400 series, duplex stainless steels like 2205, 2304, 2101, 2507, 904L, and high-nickel alloys such as 800H and 600H.
Q2. Can you produce the products according to my own drawings?
Absolutely! We can manufacture products precisely according to your drawings, ensuring the utmost satisfaction and adherence to your specifications.
Q3. How does your factory do regarding quality control?
Quality is our top priority. We consistently emphasize rigorous quality control from the very beginning of the production process to the final stages, ensuring top-notch products.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation methods to suit your preferences and requirements.
However, please note that any additional costs and differentials incurred during this period will be your responsibility.
Q5. How does your factory do regarding quality control?
Quality is our top priority. We consistently emphasize rigorous quality control from the very beginning of the production process to the final stages, ensuring top-notch products.
Q6. How long is the delivery time?
A: The delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we expedite the process to ensure timely delivery.
Q7. What is your Payment?
A: 100% T/T advance, Western Union (For Small Orders)
B: 30% T/T upfront and the balance 70% before shipment
C: 100% Irrevocable LC at sight (For Large Orders)
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we specialize in DDQ. Our materials are perfect for producing stainless steel pots, sinks, bowls, and more. Just let us know your specific needs, and we will tailor the mechanical properties to meet your requirements.
Q9: How to get a sample?
A: We offer FREE samples for your evaluation. If you need a small piece, we can cover the courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to numerous countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, where we will be delighted to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}