| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, Stainless Steel 410 Rod, Extensive Range of Stainless Steel 410 Round Bar, SS 410 Round Bar, SS DIN 1.4006 Round Bar Manufacturers - Buy Stainless Steel 410 Bright Bar, 410 SS Polished Bar, SS 410 Rod Suppliers, China AISI SS 410 Round Bar Producers.
For more information on stainless steel rods, please contact Daxun.
410 Stainless Steel Rod Chemical Composition
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our forming capabilities include cutting-edge radial forging machines, advanced heat treatment and melting furnaces, and high-precision rolling mills. We also utilize a unique hydroforming process for the manufacturing of titanium rods and specialized parts.
Our stainless steel rod heat treatment employs advanced furnace technology to guarantee the stability and superior performance of the material.
Daxun Stainless Steel incorporates the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, significantly reducing impurities during the smelting process and enhancing the performance of the finished stainless steel rods.
Our stainless steel products at Jiangsu Daxun Alloy Co., Ltd. are fully certified and traceable. We supply the highest-quality stainless steel to leading industries including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
Explore our product pages for specific sizes or contact us for a quote on custom-sized orders.
410 Stainless steel round bars are incredibly versatile, finding use from construction to automotive parts. Daxun Alloys offers a wide variety of grades and sizes to meet diverse needs. Our advanced cutting service ensures precise customization to meet your exact requirements.
Can you manufacture stainless steel grinding bars and rods?
Absolutely! We specialize in stainless steel grinding bars and rods, offering precision in dimension, impeccable roundness, and superior straightness. Though they surpass polished bars in quality, the processing costs are higher.
Q1: What range of products do you offer?
A: We offer an extensive range of steel types, including general grades like 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Our collection also features:
400 series, duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you manufacture products based on my drawings?
Yes, we can produce products according to your drawings, ensuring they meet your utmost satisfaction.
Q3. How does your factory ensure quality control?
Quality is our top priority. We maintain stringent quality control measures from the beginning to the end of production.
Q4. Can I request changes to the packaging and transportation methods?
Yes, we can modify the packaging and transportation methods according to your requirements.
However, you must bear any additional costs and the price differences that may arise during this period.
Q5. How does your factory ensure quality control?
Quality is our top priority. We maintain stringent quality control measures from the beginning to the end of production.
Q6. What is your delivery time?
A: Delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite the production process in our workshop.
Q7. What are your payment terms?
A: 100% T/T in advance or Western Union (for small orders).
B: 30% T/T in advance and 70% balance before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you produce Deep Drawing Quality (DDQ) material?
A: Yes, we can. Our DDQ materials are perfect for stainless steel pots, sinks, bowls, etc. Provide your specific usage, and we'll adjust the mechanical properties accordingly.
Q9: How can I obtain a sample?
A: Free samples are available for your evaluation. For small pieces, we may cover the courier cost, depending on the circumstances.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}