| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys, a reputable manufacturer, offers high-quality SS 310 / 310S Round Bars renowned for their exceptional characteristics. These austenitic stainless steels, based on chromium and nickel, exhibit unparalleled durability, flexibility, workability, machinability, weldability, ductility, fabricability, high strength, and hardness. Ideal for industrial chemistry and nut manufacturing, these rods are market favorites due to their superior anti-corrosion properties, enduring extreme temperatures effortlessly. Unaffected by annealing temperatures, they resist deformation, ensuring reliability. We provide tailored round bars in diverse finishes, lengths, and shapes, all at competitive prices, catering to specific client needs. Our versatile circular bars seamlessly integrate into various industrial applications.
For More Information on Stainless Steel Rods, Please Contact Daxun
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rods production, alongside a unique hydroforming process for parts manufacturing.
Utilizing advanced heat treatment furnace equipment, our stainless steel rod heat treatment guarantees material stability and high performance.
Jiangsu Daxun Alloy Co., Ltd. leverages cutting-edge technology to deliver unparalleled quality in stainless steel production. Utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun Stainless Steel minimizes impurities during the smelting process. This meticulous approach ensures that the high-temperature 310S stainless steel rods meet ASTM A276 standards, providing superior performance and reliability in every application.
Discover our range of top-tier, fully certified stainless steel products. At Jiangsu Daxun Alloy Co., Ltd., we proudly supply the highest quality stainless steel to a diverse array of industries. Leading sectors such as aerospace, industrial manufacturing, medical fields, marine applications, and even the military trust our products for their critical operations.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and pipes present excellent resistance to both corrosion and heat, even under the most demanding conditions.
Stainless steel round bars are extensively used, spanning a wide range of applications from construction to automotive parts. Given their diverse uses, Daxun Alloys offers stainless steel round bars in various grades and sizes. Our advanced cutting service ensures precise fulfillment of your requirements every time.
Discover the convenience of easily ordering our premium stainless steel round bars in a versatile array of sizes tailored to your specific needs. Choose from a variety of grades and receive bars ranging in lengths from 500mm to an impressive 6 meters, and diameters from a delicate 3mm to a robust 500mm. To cater to all your preferences, we provide options for both metric and imperial sizes, ensuring seamless integration into your projects.
For those unique requirements that go beyond standard sizes, we've got you covered. At Jiangsu Daxun Alloy Co., Ltd., we offer unlimited free cuts to length, utilizing advanced bandsaws that guarantee precision and consistency every time. Just specify your exact needs when placing your order, and we will deliver with impeccable accuracy.
Can you manufacture stainless steel grinding bars and rods?
Yes, we specialize in producing stainless steel grinding bars and rods with unparalleled precision in dimension, roundness, and straightness. These attributes surpass those of standard polished stainless steel bars, although they do entail higher processing costs.
Q1: What products do you offer?
A: We offer a wide range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L. Additionally, we provide 300 series, duplex stainless steels such as 2205, 2304, 2101, and 2507, as well as high-nickel alloys like 800H and 600H.
400 series, duplex stainless steels such as 2205, 2304, 2101, 2507, and high-nickel alloys including 904L, 800H, and 600H.
Q2: Can you manufacture products based on my drawings?
Absolutely, we can produce products tailored to your specific drawings, ensuring they meet your utmost satisfaction.
Q3: How does your factory ensure quality control?
Quality is our top priority. We maintain rigorous quality control processes from the beginning to the end of production.
Q4: Can the form of packaging and transportation be modified upon request?
Yes, we can accommodate changes in packaging and transportation as per your request,
although you will need to cover any additional costs incurred during this period and any price differences.
Q5: How does your factory handle quality control?
Quality is our top priority. We maintain rigorous quality control processes from the beginning to the end of production.
Q6: What is the delivery time?
A: Our delivery time ranges from 7 to 20 working days following payment confirmation.
For urgent orders, we expedite processing to ensure timely completion.
Q7: What are your payment terms?
A: 100% T/T in advance, Western Union (for small orders)
B: 30% T/T in advance and 70% balance before shipment
C: 100% Irrevocable LC at sight (for large orders)
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, etc. Let us know your specific usage, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: FREE samples are available for your evaluation and testing. If you need a small piece, we can cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and others.
){kind=link}