| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Discover our extensive range: ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, and Stainless Steel 410 Rod. We are leading manufacturers of SS 410 Round Bar, SS DIN 1.4006 Round Bar, offering a variety of options including Stainless Steel 410 Bright Bar and 410 SS Polished Bar. Your trusted suppliers in China for AISI SS 410 Round Bar.
For more information on our premium stainless steel rods, please contact Daxun.
Detailed Composition of 410 Stainless Steel Rod
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our forming capabilities include cutting-edge radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills. We also employ a unique hydroforming process for manufacturing titanium rods and specialized parts.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods.
At Daxun Stainless Steel, we utilize the world's most advanced vacuum induction furnaces, vacuum consumable furnaces, and electroslag furnaces to minimize impurities and enhance the performance of our finished stainless steel rods.
Our stainless steel products come with full certification and traceability. We proudly supply premium quality stainless steel to prominent sectors such as aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
Refer to specific product pages for unique sizes, and contact us for quotes on custom size orders.
410 Stainless steel round bars possess extensive applications, ranging from construction to automotive components. Given their versatility, Daxun Alloys provides these bars in various grades and dimensions, ensuring we meet your precise needs with our advanced cutting services every time.
Can you manufacture SS grinding bar & rod?
Absolutely, we specialize in producing SS grinding bar & rod with unparalleled precision in dimension, roundness, and straightness. These attributes ensure superior performance compared to polished bars, although they come with a higher processing cost.
Q1: What products can you offer?
A: We offer a broad range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, we provide
400 series and duplex stainless steel options such as 2205, 2304, 2101, 2507, among others. We also supply high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce products according to my own drawings?
Yes, we can meticulously craft products based on your drawings, ensuring that the final output fully meets your satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We implement rigorous quality control measures from the very start of the production process to the final stages.
Q4. Can I request changes in packaging and transportation?
Yes, we can accommodate changes in packaging and transportation as per your requirements.
However, you will be responsible for any additional costs and differences incurred during this period.
Q5. How does your factory ensure quality control?
Quality remains our utmost priority. We constantly emphasize stringent quality control throughout the entire production cycle.
Q6. What is the typical delivery time?
A: Our delivery time ranges from 7 to 20 working days upon payment confirmation.
For urgent orders, we expedite production to meet your deadlines.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront with the remaining 70% due before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are suitable for applications like stainless steel pots, sinks, and bowls. Let us know your specific use case, and we will adjust the mechanical properties to fit your needs.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation. If you need a small piece, we may cover the courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to numerous countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many others.
){kind=link}