310S Stainless Steel Bar ASTM A479 Forged 210-270mm Precision Polished Wear Resistant Engineering Machinery 310S Stainless Steel Rod

• Customization: Available
• Type: Stainless Steel Bars
• Standard: ASTM, AISI, GB, JIS, DIN, EN
• Model NO.: 310S stainless steel rod
• Grade: 310 310S S31008
• Certification: ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS
• Shape: Round
• Technique: Hot Rolled
• Surface Treatment: Bright
• Material: 310 310S S31008
• Manufacturing: Hot Rolling, Cold Rolling, Forging
• Transport Package: Wooden Box or Wooden Pallet
• Specification: φ 3.0mm-350mm
• Trademark: TISCO POSCO Baosteel
• Origin: China
• Production Capacity: 10000ton

Product Description

Product Description

Detailed Photos

 

Product Parameters:   Stainless Steel rod
Material	310 310S S31008
Specifications	ASTM A276, ASME SA276 / ASTM A479  ASME SA479
Dimensions	EN, DIN, JIS, ASTM, BS, ASME, AISI
Round Bars	Outside Diameter in the range of 4mm to 500mm
Bright Bars	Outside Diameter in the range of 4mm to 100mm
Hex Bars	18mm - 57mm (11/16″ to 2-3/4″)
Finish	Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Length	1 to 6 Meters, Custom Cut Lengths
Form	Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc.
Marking & Traceability	Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end.
Test Certificate	Manufacturer Test Certificate according to EN 10204 3.1 B
	Laboratory Test Certificate from Govt. Approved Lab.
	Under Third Party Inspection
Testing & Inspection	Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing

310S: The Global Leader in Stainless Rod and Round Bar Fabrication Services

Daxun Alloys stands as a reputable manufacturer of premium SS 310 / 310S Round Bars, boasting a myriad of superior characteristics. Crafted from austenitic stainless steel rich in chromium and nickel, our SS310/310S Round Bars/Rods offer unparalleled durability, flexibility, and workability. The machinability, weldability, ductility, and fabricability of these rods are first-rate, ensuring high strength and impressive hardness. Highly renowned for their anti-corrosion properties, these rods are indispensable in industrial chemistry and nut manufacturing applications. Built to withstand extreme temperatures, our rods perform flawlessly at annealing temperatures without deformation. Delivered to our esteemed clients at market-leading prices, we offer bespoke solutions in various finishes, lengths, and shapes to tailor-fit specific requirements. Our round bars integrate seamlessly into industrial applications, providing unmatched reliability.

Hot Rolled Stainless Steel Rod
Our Stainless steel rod and bar undergo rigorous heating and multiple passes through a rolling mill. With complete specifications, they meet all established standards and performance benchmarks.

Cold Drawn Bright Stainless Steel Rods
Cold-drawn Stainless steel rods, processed under cold working conditions, sport a smooth surface that can be polished and ground to perfection.

Forged Stainless Steel Rod and Bar
Forged to perfection, our stainless steel rods undergo multiple forging processes to enhance their mechanical properties and overall strength.

 

General Properties
Our extensive network of service centers ensures rapid availability of common stainless steel bar sizes and alloys. We also cater to custom sizes, and for smaller quantities below factory minimums, we offer a stocking program for expedited turnaround. Daxun Alloys stocks a vast range of stainless steel round bars, spanning diameters from 1/16" to 26". Available in nearly every grade, including 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.

 

Additional Services
Our unique processed bar grade of stainless steel round bars is designed for enhanced machinability and reduced overall part costs. With state-of-the-art bar processing machinery, Daxun Alloys delivers precise specifications to meet customer demands.

1. Daxun offers heat treatments based on the specific metal chemistry. 2. Positive Material Identification (PMI): We can complete PMI testing in-house or collaborate with independent laboratories. 3. Ultrasonic Testing (UT): Utilizing high-frequency sound energy, UT inspects and measures stainless steel bar products, aiding in defect detection, evaluation, and dimensional measurement.

For further details on our premium stainless steel rods, contact Daxun today.

310s Stainless Steel Rod: Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	Fe
SS 310	0.015 max	2.0 max	0.15 max	0.020 max	0.015 max	24.00 - 26.00	0.10 max	19.00 - 21.00	54.7 min
SS 310S	0.08 max	2.0 max	1.00 max	0.045 max	0.030 max	24.00 - 26.00	0.75 max	19.00 - 21.00	53.095 min

 

310s Stainless Steel Rod: Mechanical Properties

Density	Melting Point	Tensile Strength	Yield Strength (0.2%Offset)	Elongation
7.9 g/cm3	1402 °C (2555 °F)	Psi - 75000 , MPa - 515	Psi - 30000 , MPa - 205	40%

 

310s Stainless Steel Rod: Physical Properties

Property	At	Value	unit
Density		8,000	kg/m³
Melting Range		1400 - 1450	°C
Modulus of Elasticity	20°C	200	GPa
Shear Modulus	20°C	77	GPa
Poisson's Ratio	20°C	0.3
Thermal Conductivity	100°C	14.2	W / m. °C
Electrical Resistivity	25°C	0.78	micro-ohm . m
Electrical Conductivity	25°C	1.25	% IACS
Specific Heat		500	J/kg. °C
Relative Magnetic Permeability		1.02
Coefficient of Expansion	0 - 100°C	15.9	/°C
	0 - 315°C	16.2	/°C
	0 - 540°C	17	/°C

Daxun's Stainless Steel Rods Manufacturing Capabilities

Our forming capabilities include cutting-edge radial forging machines, advanced heat treatment furnaces, melting furnaces, and rolling mills for titanium rod manufacturing. Additionally, we utilize a unique hydroforming process for part production.

 

Daxun's Heat Treatment Furnace

Our stainless steel rod heat treatment leverages advanced furnace equipment, ensuring the material's stability and superior performance.

 

Daxun's Smelting Ability

a132ad89

Packaging & Shipping

Company Profile

Let us be your trustworthy Stainless Steel Rod supplier

Our stainless steel products are fully certified and meticulously traceable. We proudly supply superior-quality stainless steel to prestigious industries such as aerospace, industrial manufacturing, medical, marine, and military sectors.

Mechanical properties of various grades of stainless steel bars

	Tensile Strength			Yield Strength
Alloy	UNS Designation	Spec.	psi	MPa	ksi	psi	MPa	ksi	Elongation in 2 inches (min.) %	Grain Size Req.	Max. Hardness	Modulus of Elasticity (x106 psi)
304	S30400	A249, A312	75,000	515	75	30,000	205	30	35	-	90 Rb	28
304L	S30403	A270 A312	70,000	485	70	25,000	170	25	35	-	90 Rb	28
304LN	S30453	A249, A688	75,000	515	75	30,000	205	30	35	-	90 Rb	28
304H	A30409	A249, A312	75,000	515	75	30,000	205	30	35	7 or coarser	90 Rb	28

 

The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table.
Grade	Tensile Str	Yield Str	Elong	Hardness
	(MPa) min	0.2% Proof	(% in 50mm) min
		(MPa) min		Rockwell B (HR B) max	Brinell (HB) max
316	515	205	40	95	217
316L	485	170	40	95	217
316H	515	205	40	95	217

 

	Tensile Strength			Yield Strength
Alloy	UNS Designation	Spec.	psi	MPa	ksi	psi	MPa	ksi	Elongation in 2 inches (min.) %
321	S32100	-	75,000	515	-	30,000	205	-	35
321H	S32109	-	75,000	515	-	30,000	205	-	35

 

Grade	Density	Melting Point	Tensile Strength	Yield Strength (0.2%Offset)	Elongation
310S	7.9 g/cm3	1402 °C (2555 °F)	Psi - 75000 , MPa - 515	Psi - 30000 , MPa - 205	40%

 

Grade	Tensile Strength	Yield Strength	Elongation	Hardness
	(MPa) min	0.2% Proof	(% in 50mm) min
		(MPa) min		Rockwell C (HR C)	Brinell (HB)
UNS S31803 / 2205	621	448	25	31 max	293 max
UNS S32205 / 2205	621	448	25	31 max	293 max

 

Grade	Property	Value
2507/ S32750	Density (g/cm3)	7.8
	0.2% Offset Yield Strength	80 ksi
	Ultimate Tensile Strength	116 ksi
	0.1% Offset Yield Strength 0.2%	91 ksi
	Elongation in 2 inches, %	15%
	Hardness Rockwell C	32
	Impact Energy	74 ft.-lbs
	Density	0.28 lb per inch3
	Modulus of elasticity	28 x 10(6) psi
	Coefficient of thermal expansion	7.2 x 10(-6) per of at 68 to 212 of
	Thermal conductivity	8.7 Btu/hr ftoF
	Heat capacity	0.12 Btu/ lb oF
	Electrical resistivity	31.5 x10(-6) ohm-inch

 

For comprehensive information on stainless steel rods, please contact Daxun

Certifications

GENERAL PROPERTIES

• 310S alloy is an austenitic stainless steel bar renowned for its remarkable high temperature resistance, combined with impressive ductility and weldability. Owing to its elevated chromium and nickel content, this alloy excels in high-temperature applications, delivering robust corrosion resistance, outstanding oxidation resistance, and unparalleled strength at temperatures soaring up to 2100°F. Its superior composition allows 310S to surpass 304 or 309 stainless steel bars in most scenarios.

APPLICATIONS

• Higher alloyed stainless steels exhibit remarkable strength at elevated temperatures and exceptional resistance to creep deformation and environmental damage. Consequently, Alloy 310 is extensively utilized in heat treatment and chemical processing industries. Noteworthy applications include:
• Furnace Parts
• Oil Burner Parts
• Heat Exchangers
• Welding Filler Wire and Electrodes
• Annealing Covers
• Combustion Tubes
• Fire Box Sheets

RESISTANCE

Stainless Steel Alloy 310 offers unparalleled resistance to both corrosion and heat, thriving in the most demanding environments.

CORROSION RESISTANCE

• Provides stellar corrosion resistance.
• High chromium content ensures excellent aqueous corrosion resistance.
• Exceptional resistance at standard temperatures, along with impressive performance in oxidizing and carburizing atmospheres.

HEAT RESISTANCE

• Displays strong resistance to oxidation during intermittent service in air at temperatures up to 1040°C and continuous service up to 1150°C.
• Excellent resistance to thermal fatigue and cyclic heating.
• Ideal for environments with *** dioxide gas at elevated temperatures.
• Continuous use in the 425-860°C range is not recommended if subsequent aqueous corrosion resistance is needed, due to carbide precipitation.
• Primarily utilized at temperatures starting from around 800 or 900°C, which are above the effective range of 304H and 321.

FABRICATION

• Ideal for use in heat treatment and process industries due to its resilience in high-temperature and corrosive environments.
• Frequently fabricated into complex structures.
• Readily roller-formed, stamped, and drawn.
• Since 310 Stainless Steel rods work harden, severe forming operations should be followed by annealing.

WELDABILITY

• Austenitic stainless steel is generally considered weldable.
• Boasts weldability on par with 304 and 304L.
• Special care is imperative to accommodate a higher coefficient of thermal expansion to prevent warping and distortion.
• Standard welding processes for this grade include:
  • TIG-Welding
  • MAG-Welding Solid Wire
  • Arc Welding (E)
  • Laser Beam Welding

310-310S-31008 grade stainless steel round bars

Stainless steel round bars hold broad utility, spanning industries from construction to automotive parts. To accommodate diverse applications, Daxun Alloys offers these bars in various grades and sizes. Our complimentary advanced cutting service guarantees precision to meet your specific requirements every time.

Wide Range of Sizes to Choose From

Experience seamless ordering with our versatile stainless steel round bars, available in an extensive range of sizes. Simply select your desired steel grade, and we will supply bars in lengths from 500mm to 6 meters and diameters from 3mm to 500mm. Whether you prefer metric or imperial measurements, we've got you covered.

Need a custom size? No problem! Enjoy unlimited free custom cuts tailored to your specifications. Utilizing advanced bandsaw technology, we guarantee precision and consistency with every cut. Just specify your requirements when placing your order, and we'll take care of the rest.

FAQ

 

Can you do SS grinding bar & rod?

Yes, we specialize in SS grinding bar & rod with unmatched precision in dimension, roundness, and straightness. These exceed the quality of standard polished stainless steel bars, though the processing cost is higher.

Q1: What products can you offer?

A: We provide a diverse range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and 300 series.
Additionally, we offer 400 series, duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.

Q2. Can you produce the products according to my own drawings?

A: Yes, we can manufacture products based on your drawings to meet your highest satisfaction.

Q3. How does your factory do regarding quality control?

A: Quality is our top priority. We enforce stringent quality control measures from start to finish.

Q4. Can I request to change the form of packaging and transportation?

A: Yes, we can adapt the packaging and transportation to your requests,
though you will need to cover any additional costs and price differences that arise.

Q5. How does your factory do regarding quality control?

A: Quality is our top priority. We enforce stringent quality control measures from start to finish.

Q6. How long is the delivery time?

A: Delivery time is typically 7-20 working days after payment confirmation.
For urgent orders, we expedite the process to complete it ahead of schedule.

Q7. What is your payment policy?

A: 100% T/T in advance, Western Union (for small orders)

B: 30% T/T upfront and 70% balance before shipment

C: 100% Irrevocable LC at sight (for large orders)

Q8: Can you make DDQ (Deep Drawing Quality)?

A: Yes, we can. Our material is suitable for stainless steel pots, sinks, and bowls. Specify your usage, and we will tailor the mechanical properties to meet your requirements.

Q9: How can I get a sample?

A: Free samples are available for your review and testing. For small pieces, we may cover the courier cost, subject to conditions.

Q10: Which countries have you exported to?

A: We have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, among others.