| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition 201 Stainless Steel Rod
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties 201 Stainless Steel Rod
Mechanical property requirements for the annealed product as specified in ASTM A240 and ASME SA240
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
Mechanical property requirements for cold worked flat rolled products as specified in 201 Stainless Steel Rod: A high-quality, versatile solution for various industrial applications.
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Physical Properties
Physical properties for Type 201 stainless steel rod, ensuring durability and performance in demanding environments.
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Our forming capabilities include state-of-the-art radial forging machines, advanced heat treatment furnaces, high-efficiency melting furnaces, and sophisticated rolling mills for manufacturing titanium rods. Additionally, we utilize a unique hydroforming process to produce high-quality parts.
Our stainless steel rod heat treatment employs cutting-edge furnace equipment to ensure material stability and superior performance.
At Jiangsu Daxun Alloy Co., Ltd., we use the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. This top-tier equipment minimizes impurities during the smelting process, enhancing the performance of our finished stainless steel rods.
Our stainless steel products are meticulously certified and fully traceable, ensuring the highest standards of quality. We proudly supply elite stainless steel to leading industries such as aerospace, industrial manufacturing, medical technology, marine engineering, and military applications.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you produce SS grinding bar & rod?
Yes, we specialize in producing SS grinding bars & rods with unparalleled precision in dimension, roundness, and straightness. These are superior to stainless steel polished bars, though the processing cost is higher.
Q1: What products can you offer?
A: We offer a wide range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300 series.
Additionally, we provide 400 series and duplex stainless steel like 2205, 2304, 2101, 2507, as well as high-nickel alloys such as 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Absolutely, we can manufacture products precisely according to your drawings to ensure complete satisfaction.
Q3. How does your factory manage quality control?
Quality is our utmost priority. We are committed to stringent quality control from the start to finish of the production process.
Q4. Can I request changes in packaging and transportation?
Yes, we can customize the packaging and transportation forms based on your requirements.
However, any additional costs and price differences during this period will be your responsibility.
Q5. How does your factory manage quality control?
Quality remains our top priority. We adhere to stringent quality control procedures throughout the entire production process.
Q6. What is the delivery time?
A: The typical delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite production to meet your timeline.
Q7. What are your payment terms?
A: 100% T/T in advance or Western Union for small orders.
B: 30% T/T as a deposit and 70% balance before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality)?
A: Yes, our materials are suitable for creating products like stainless steel pots, sinks, and bowls. Let us know your specific usage, and we'll adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: FREE samples are available for inspection and testing. For small pieces, we may cover the courier cost depending on the circumstances.
Q10: Which countries have you exported to?
A: We have successfully exported our stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}