| Ti-6Al-4V Grade 5 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 5 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 5-Ti-6Al4V- TC4- USN 56400 |
| Grade 5 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 5 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ6.0mm to φ1219mm | |
| Grade 5 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 5 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form Ti-6Al-4V | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TC4 1.37165 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 5 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 5 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 5 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 5 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 5 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 5 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 5 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 5 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 5 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 5 Titanium Tubes are Integral to Various Industries Operating under Harsh Corrosive Conditions:
At Daxun, we implement rigorous quality assurance tests including flattening, flaring, ultrasonic flaw detection, pitting and resistance, mechanical, hardness, material positive identification, and expansion tests. These ensure that our Grade 1 Titanium Welded Pipe and Grade 1 Titanium Seamless Pipe materials meet the necessary application standards. During production, we meticulously measure the diameter, thickness, and surface quality of our products. Standard delivery time is 5-7 days, while special size products have a delivery time of 15-20 days.
The Ti-6Al4V Grade 5 Titanium Alloy Tube is the Most Commercially Available Titanium Alloy. It Boasts High Strength and Toughness. Grade 5 Titanium Alloy Exhibits Excellent Welding and Processing Characteristics:
We Stock and Sell Grade 5 Titanium Alloy Seamless Tubes, Forged Seamless Tubes, Welded Tubes, etc.
Daxun Alloy, a Premier Titanium Alloy Tube Manufacturer and Supplier in China, Delivers Top-Quality Grade 5 Titanium Pipes Worldwide, Earning Acclaim Across Numerous Projects.
Ti 6Al-4V (Grade 5 Titanium) is the Most Widely Used Titanium Alloy Tube, Representing Over 50% of Total Titanium Usage. Typically Utilized in the Annealed State, it Operates Up to 400°C (750°F). Ti 6Al/4V is Welded with Matching or ELI Filler Wire. It Offers Significantly Higher Strength than Commercial Pure Titanium Tubes, Superior Stiffness, and Enhanced Thermal Properties (excluding thermal conductivity). The Thermal Conductivity of Grade 5 Titanium Tube is Approximately 60% Lower than CP Titanium. Heat Treatable to Achieve Optimal Strength and Performance, its Advantages Include Strong Formability, Low Density, and Outstanding Corrosion Resistance.
This Grade Pairs Strength, Corrosion Resistance, Weldability, and Machinability Perfectly. Hence, It Sees Extensive Use in Military Aircraft, Aviation, Rocket Parts, Precision-Guided Components, Armor Parts, Ship Equipment, Military Vacuum Equipment, and Surgical Implants. Typically Employed in Applications up to 400°C to Enhance Ductility and Toughness in Cold Working Conditions, it Exhibits Excellent Specific Strength. Provided in the Annealed State, it Can Be Heat Treated to Increase Strength for Various Applications. As a Versatile Titanium Alloy, Ti 6Al-4V Titanium Seamless Tube Offers Ideal Properties at Temperatures Ranging from -210°C to 400°C. Grade 5 Titanium Alloy Tube Combines High Strength and Toughness with Excellent Welding and Processing Characteristics.
54c7d639
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
Our state-of-the-art titanium tubes are crafted through hot-rolling or hot-extruding processes. Each tube is meticulously straightened, precision-machined both inside and out, and polished to a flawless finish. Available in both heat-treated and non-heat-treated forms, these tubes undergo rigorous 100% ultrasonic flaw detection to ensure impeccable quality.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: OD ranges from 19mm to 325mm, wall thickness spans 9mm to 30mm, and lengths reach up to 5000mm (negotiable). - Hot-extruded Titanium Tubes: OD from 50mm to 160mm, wall thickness from 7mm to 35mm, lengths up to 3000mm (negotiable).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are offered as heat-treated, surface-etched, and rigorously tested through hydrostatic or ultrasonic means, tailored to precise manufacturing specifications. Tubes Supplied: OD ranges from 6mm to 89mm, wall thickness from 0.5mm to 11mm, and lengths up to 6000mm (negotiable).
Titanium Welded Pipes
DaXun specializes in manufacturing high-quality titanium welded pipes with diameters from 100 mm. Sizes range from 12.7 to 38.1 mm (0.47 in to 1.5 in) in diameter and wall thicknesses from 0.4 to 1.65 mm (0.016 in to 0.065 in), in lengths up to 25000 mm. Our titanium pipes, available in electrical Gr1, Gr2, and Gr12 titanium alloys, are expertly crafted for engineering and chemical industries. Utilizing flat rolled raw material (kelp), these pipes are welded via automatic tungsten inert gas (argon) welding on electric pipe welders and heat-treated on the mill line. Each pipe undergoes stringent mechanical testing, geometrical measurements, and extensive 100% ultrasonic and eddy current testing, including pneumatic or hydrostatic testing. Pipes are meticulously packed according to customer specifications, ensuring compliance with ASTM B 338 and ASME SB 338 standards.
| CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium tube PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
•ASTE B338 - Tubes Titanium tubes standard heat treatable
• AMS 4928 - Forgings and forging stock (annealed)
• AMS 4965 - Forgings (solution treated and aged)
• AMS 4967 - Forgings (annealed, heat treatable)
Typical hardness in the annealed condition is Rockwell C 30-34, and about Rockwell C 35-39 in the solution and aged condition.
Q1: What products can you offer?
A: We offer a comprehensive range of steel types, including general steel like 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, we provide the 300 and 400 series.
Our product line also includes duplex stainless steel such as 2205, 2304, 2101, and 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can produce products precisely as per your drawings, ensuring maximum satisfaction.
Q3. How does your factory manage quality control?
Quality is our top priority. We emphasize stringent quality control from the very beginning to the end of the manufacturing process.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can adapt the packaging and transportation forms to match your requests.
However, any additional costs and the price differences incurred will be your responsibility.
Q5. How does your factory manage quality control?
Quality is our top priority. We emphasize stringent quality control from the very beginning to the end of the manufacturing process.
Q6. How long is the delivery time?
A: Our delivery time ranges from 7 to 20 working days post-payment confirmation.
For urgent orders, we can expedite the process to meet your needs.
Q7. What are your payment terms?
A: For small orders, we accept 100% T/T in advance or Western Union.
B: For standard orders, a 30% T/T advance and 70% balance before shipment.
C: For large orders, we accept 100% Irrevocable LC at sight.
Q8: Can you provide Deep Drawing Quality (DDQ) material?
A: Yes, we offer DDQ material suitable for stainless steel pots, sinks, bowls, etc. Share your specific usage, and we'll adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: We provide FREE samples for your inspection and testing. For small pieces, we may cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: We have exported our stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up.
){kind=link}