| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Discover the unparalleled quality of our ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, Stainless Steel 410 Rod, and a comprehensive array of Stainless Steel 410 Round Bars. We are esteemed manufacturers of SS 410 Round Bars, SS DIN 1.4006 Round Bars, and renowned suppliers of Stainless Steel 410 Bright Bars, 410 SS Polished Bars, and SS 410 Rods. Entrust your needs to China's leading AISI SS 410 Round Bar producers.
For further information on our premium stainless steel rods, please reach out to Daxun.
Comprehensive Chemical Composition of 410 Stainless Steel Rod
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our forming capabilities are bolstered by advanced radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills. We also utilize a unique hydroforming process to manufacture parts with precision.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods, elevating their material quality.
Utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun Stainless Steel minimizes impurities during the smelting process, delivering superior performance in our finished stainless steel rods.
Our stainless steel products come with full certification and traceability, ensuring the highest quality. We proudly supply top-grade stainless steel to a range of leading industries, such as aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
Please refer to specific product pages for unique sizes. Feel free to contact us for a quote on any custom size orders.
SS 410 stainless steel round bars are highly versatile and widely utilized, from construction to automotive components. Given their diverse applications, Daxun Alloys provides these round bars in an array of grades and sizes. Our advanced cutting service ensures precise adherence to your specifications each time.
Can you provide SS grinding bars and rods?
Yes, we specialize in producing SS grinding bars and rods with unparalleled precision in dimension, roundness, and straightness. These products surpass the quality of standard stainless steel polished bars, though they do come with a higher processing cost.
Q1: What types of products can you offer?
A: We offer a comprehensive range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L.
Additionally, we provide 400 series stainless steel, duplex stainless steels like 2205, 2304, 2101, 2507, and high-nickel alloys such as 904L, 800H, 600H.
Q2: Can you manufacture products based on my custom drawings?
Yes, we can tailor our production processes to meet your specific drawings and requirements, ensuring your utmost satisfaction.
Q3: How does your factory ensure quality control?
Quality is our top priority. We implement stringent quality control measures throughout the entire production process, from start to finish.
Q4: Can I request changes in packaging and transportation?
Yes, we can modify the packaging and transportation methods according to your specifications,
but please note that you will need to cover any additional costs and differences incurred during this period.
Q5: How does your factory handle quality control?
Quality is our top priority. We maintain rigorous quality control procedures from the beginning to the end of the production process.
Q6: What is your delivery time?
A: Our standard delivery time is 7-20 working days after payment confirmation.
For urgent orders, we can expedite production to meet your needs.
Q7: What are your payment terms?
A: 100% T/T in advance or Western Union for small orders.
B: 30% T/T deposit with the remaining 70% due before shipment.
C: 100% Irrevocable Letter of Credit (LC) at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for applications such as stainless steel pots, sinks, and bowls. Please inform us of your specific usage, and we will adjust the mechanical properties accordingly to meet your requirements.
Q9: How can I obtain a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we may cover the courier cost depending on the situation.
Q10: To which countries have you exported?
A: We have successfully exported our stainless steel materials to numerous countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, and Ukraine, among others.
){kind=link}