| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | GR1 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys proudly holds the position of a leading global producer and supplier of premium Grade 1 titanium plates, known for their superior quality and performance.
Pure Grade 1 titanium plate boasts exceptional ductility and cold formability, making it perfect for deep drawing applications. Its outstanding general and seawater corrosion resistance, combined with its ability to withstand oxidizing, neutral, and mildly reducing environments-including chlorides-makes it indispensable for a myriad of industrial uses. With a low density of about half that of nickel-based alloys, it offers a high strength-to-weight ratio. Its excellent corrosion resistance, weldability, and good impact hardness further enhance its appeal for severe chemical conditions.
Producers of ASTM B265 Titanium Gr 1 Plates, Titanium Gr 1 Sheets, and Finished Plates. Suppliers of ASTM B265 Titanium Grade 1 Coils and Pure Titanium Gr 1 Hot and Cold Rolled Plates. Dealers in Titanium ASTM B265 Gr 1 Sheets, Patterned and Perforated Plates, and Sheets and Plates Manufacturers in China.
We ensure prompt and reliable delivery of Grade 1 titanium plate products. This speed is backed by an integrated system that encompasses production capacity, information flow, logistics, and financial flow. For instance, Daxun's order data is instantly transmitted to the logistics system, ensuring seamless data integration. Our processing center, strategically located near highways, rivers, and seas, enables efficient scheduling, rapid response, and coordinated storage and transportation, guaranteeing timely task completion.
Grade 1 titanium plate, with its lower density and increased ductility, is ideal for industries focused on weight reduction and deep drawing processes. Key industries include medical, chemical equipment, and aerospace. Its strength and corrosion resistance also make it suitable for marine, chemical processing, and desalination applications. Typical uses for Grade 1 titanium alloys include oil and gas components, reaction and pressure vessels, piping systems, power, heat exchangers, linings, and flue gas desulfurization systems. Adhering to standards such as ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, and AMS4972.
The cold rolled thickness range for Grade 1 Titanium Plates spans from 0.3 mm to 6.0 mm, while hot rolled thickness ranges from 4.76 mm to 155 mm. These plates are manufactured via longitudinal and transverse rolling and may be supplied in hot rolled or heat treated conditions. Creep flattening can be employed as a heat treatment to alleviate internal stresses and meet specific flatness requirements. Additionally, plates can be provided as cut blanks, with further processing tailored to customer specifications through either mechanical or chemical methods.
About the chemical composition of (Ti 6AL-4V) Grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of Grade 2 titaniumsheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of Grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is a renowned metal expert specializing in both small and large-scale titanium plate projects. As a trusted reference point and long-term partner, DAXUN is committed to supplying your business with premium titanium plates and comprehensive technical support. Beyond being a mere supplier of industrial pure titanium plates and titanium alloy plates, DAXUN serves as a strategic partner, dedicated to helping you overcome any challenges and fulfilling your unique requirements, ensuring the successful achievement of your project goals.
The DAXUN service center in China boasts an extensive inventory of titanium plate products, enabling swift order processing. We elevate customer value through essential processing, water jet cutting, and efficient plate nesting services, significantly reducing time and costs for our clients.
Continuous investment in DAXUN's state-of-the-art production facilities and strategic capacity agreements with our partners secure our leading position in delivering top-tier titanium plate quality, both now and in the future.
Reach out to DAXUN today to receive the most up-to-date titanium plate prices and essential technical information.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN, a premier Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China, is committed to creating the world's highest-performance titanium alloy plates. We ensure rapid worldwide delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. DAXUN specializes in alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm. Plates from 0.5mm-6.0mm are cold rolled, 6.0-50mm are hot rolled, and those 50mm and above are forged. Grade 5 titanium plate (Ti-6Al-4V) is the quintessential titanium alloy, offering a combination of high strength, ductility, and superior resistance to corrosion and high temperatures. This makes it highly sought after by both general and military industries. Our products comply with various standards including ASTE, ASME, AMS, GB, GJB, MIL, JIS, and EN.
Ti-6Al-4V Grade 5 titanium plate finds its primary applications in aerospace, military industries, power sectors, vehicle armor, precision rocket guidance parts, and the marine industry.
Grade 1
Today, DAXUN Alloys is recognized as a leading global producer and supplier of premium Grade 1 titanium plate, known for its unmatched quality.
Pure Grade 1 titanium plate is celebrated for its exceptional ductility and cold formability, making it perfect for deep drawing processes. Grade 1 titanium offers excellent resistance to general and seawater corrosion, as well as resistance to oxidizing, neutral, and mildly reducing media (solutions), including chlorides. With a low density (about half that of nickel-based alloys), high strength-to-weight ratio, and remarkable corrosion resistance, it is ideal for various harsh chemical environments. Commercially pure Grade 1 titanium is the softest and most ductile titanium grade, providing excellent cold formability, corrosion resistance, weldability, and impact hardness.
We are renowned ASTM B265 Titanium Gr 1 Plate Producers, offering Titanium Gr 1 Sheets, Finished Plates, Coils, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, Perforated Plates, and more. Our comprehensive portfolio makes us the top choice for Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade 2
DAXUN specializes in producing and stocking commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the cornerstone of the commercially pure titanium family, offering a perfect blend of high strength, ductility, and exceptional corrosion resistance for diverse industrial applications.
Grade 2 Titanium Plate is known for its excellent balance between strength and ductility. It provides good impact strength, easy weldability, and outstanding corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, it demonstrates superior resistance to seawater and salt solutions.
With low density, high strength-to-weight ratio, and impressive corrosion resistance, titanium is ideal for numerous applications. It effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. Featuring a melting point of 1660°C, Grade 2 Titanium Plate is the preferred choice for industrial applications requiring good ductility and corrosion resistance.
DAXUN is your go-to metal expert for both small and large titanium plate projects. As a steadfast partner, we are ready to provide you and your business with top-quality titanium plates and unparalleled technical assistance. Consider DAXUN not just as your supplier of industrial pure titanium plates and titanium alloy plates but as your strategic partner, committed to helping you overcome any challenges and achieve your project goals.
At the heart of China, DAXUN's premier service center boasts an impressive inventory of titanium plate products, ensuring rapid order fulfillment. Our suite of value-added services, including fundamental processing, precise water jet cutting, and tailored plate nesting, empowers our clientele by significantly reducing both time and expenditure.
DAXUN's unwavering commitment to excellence is evident through relentless investments in cutting-edge production facilities and strategic capacity agreements with esteemed partners. This dedication propels DAXUN to the pinnacle of titanium plate quality, ensuring we lead the industry both now and into the future.
Reach out to DAXUN today for the most competitive titanium plate prices and up-to-date technical information, and experience the pinnacle of quality and service.
Q1: What products can you offer?
A: We offer an extensive range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300 series.
Additionally, we have the 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, etc., along with high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Yes, we can manufacture products to your specific drawings, ensuring they meet your highest satisfaction.
Q3. How does your factory ensure quality control?
A: Quality is our top priority. We consistently emphasize rigorous quality control from start to finish.
Q4. Can the form of packaging and transportation be changed upon request?
A: Yes, we can accommodate changes to packaging and transportation based on your request.
However, any additional costs incurred during this process will be borne by you.
Q5. How does your factory do regarding quality control?
A: Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q6. How long is the delivery time?
A: Delivery takes 7-20 working days after payment confirmation.
For urgent orders, we can expedite production to meet your timeline.
Q7. What are your payment terms?
A: 100% T/T in advance, Western Union (for small orders).
B: 30% T/T in advance with a 70% balance before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you provide Deep Drawing Quality (DDQ) material?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Let us know your requirements, and we will adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: FREE samples are available for inspection and testing. If you need a small piece, we might cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}