Product Parameters: Stainless Steel rod |
Material |
904L 1.4539 N08904 Super Austenite Round Bar |
Specifications |
ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
Dimensions |
EN, DIN, JIS, ASTM, BS, ASME, AISI |
Round Bars |
Outside Diameter in the range of 4mm to 500mm |
Bright Bars |
Outside Diameter in the range of 4mm to 100mm |
Hex Bars |
18mm - 57mm (11/16″ to 2-3/4″) |
Finish |
Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
Length |
1 to 6 Meters, Custom Cut Lengths |
Form |
Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
Marking & Traceability |
Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
Test Certificate |
Manufacturer Test Certificate according to EN 10204 3.1 B |
Laboratory Test Certificate from Govt. Approved Lab. |
Under Third Party Inspection |
Testing & Inspection |
Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Premium Hot Rolled Stainless Steel Rod
Our Stainless Steel Rod and Bar is meticulously heated and rolled through multiple passes in a state-of-the-art rolling mill. With comprehensive specifications, they meet and exceed all performance standards and requirements.
Cold Drawn Bright Stainless Steel Rods
Our Cold-Drawn Stainless Steel Rods are precision-drawn under stringent cold working conditions. Boasting a smooth and refined surface, these rods can also be expertly polished and ground for enhanced finish.
Superior Forged Stainless Steel Rod and Bar
Forged Stainless Steel Rods undergo multiple forging processes to significantly enhance mechanical properties and ensure superior strength.
Outstanding General Properties
Our extensive network of service centers ensures quick and reliable supply of stainless steel bar products in common sizes and alloys. We also specialize in custom-sized stainless steel bars. For orders below factory minimum, our stocking program ensures prompt and fast turnaround. Daxun Alloys offers stainless steel round bars ranging from 1/16" to 26" in diameter, available in nearly every grade of stainless steel, including 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.
Comprehensive Additional Services
Our inventory predominantly features our unique processed bar grade: stainless steel round bars, melted to exacting standards to improve machinability and minimize part costs. Equipped with advanced machinery, Daxun Alloys consistently produces bars to our customers' precise specifications.
1. Heat Treatments: Daxun performs precise heat treatments on our stainless steel bars, tailored to the metal's specific chemistry. 2. Positive Material Identification (PMI): When required, additional PMI testing is conducted, either in-house or through independent labs. 3. Ultrasonic Testing (UT): Using high-frequency sound energy, UT inspects and measures stainless steel bar products for defect detection/evaluation, dimensional measurement, and more.
![904L Stainless Steel Bar ASTM B625 φ 65-140mm Strong Acid Resistance Metallurgical Equipment 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
For detailed information on our stainless steel rods, please contact Daxun.
904L Stainless Steel Rod Chemical Composition
Element |
% Present (in product form) |
Carbon (C) |
0.02 |
Silicon (Si) |
0.7 |
Manganese (Mn) |
2 |
Phosphorous (P) |
0.03 |
Sulfur (S) |
0.01 |
Chromium (Cr) |
19.00 - 21.00 |
Nickel (Ni) |
24.00 - 26.00 |
Nitrogen (N) |
0.15 |
Molybdenum (Mo) |
4.00 - 5.00 |
Copper (Cu) |
1.20 - 2.00 |
Iron (Fe) |
Balance |
904L Stainless Steel Rod Mechanical Properties
Product Form |
|
|
|
|
C |
H |
P |
L |
L |
TW/TS |
Thickness (mm) Max. |
8 |
13.5 |
75 |
160 |
2502) |
60 |
Yield Strength |
Rp0.2N/mm2 |
2403) |
2203) |
2203) |
2304) |
2305) |
2306) |
Rp1.0N/mm2 |
2703) |
2603) |
2603) |
2603) |
2603) |
2503) |
Tensile Strength |
RmN/mm2 |
530 - 7303) |
530 - 7303) |
520 - 7203) |
530 - 7304) |
530 - 7305) |
520 - 7206) |
Elongation min. in % |
Jmin(Longitudinal) |
- |
100 |
100 |
100 |
- |
120 |
Jmin(Transverse) |
- |
60 |
60 |
- |
60 |
90 |
904L Stainless Steel Rod Physical Properties
Density at 20°C kg/m3 |
8 |
Thermal Conductivity W/m K at |
20°C |
12 |
Modulus of Elasticity kN/mm2 at |
20°C |
195 |
200°C |
182 |
400°C |
166 |
500°C |
158 |
Specific Thermal Capacity at 20°C J/kg K |
450 |
Electrical Resistivity at 20°C mm2/m |
1 |
Daxun's Cutting-Edge Stainless Steel Rod Manufacturing Capabilities
Our forming capabilities feature state-of-the-art radial forging machines, advanced heat treatment furnaces, high-performance melting furnaces, and modern rolling mills for producing titanium rods. Additionally, we utilize a unique hydroforming process for manufacturing complex parts.
Advanced Heat Treatment Furnace at Daxun
Daxun's stainless steel rod heat treatment employs cutting-edge furnace technology to ensure material stability and top-tier performance.
Unparalleled Smelting Ability at Daxun
Daxun utilizes the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace to minimize impurities during the smelting process, thereby enhancing the performance of the finished stainless steel rods.
![904L Stainless Steel Bar ASTM B625 φ 65-140mm Strong Acid Resistance Metallurgical Equipment 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
Choose Jiangsu Daxun Alloy Co., Ltd. as Your Reliable Stainless Steel Rod Supplier
Our stainless steel products are meticulously certified and fully traceable, ensuring the utmost quality and reliability. We proudly supply top-tier stainless steel to a myriad of leading industries, including aerospace, industrial, medical, marine, and military sectors.
![904L Stainless Steel Bar ASTM B625 φ 65-140mm Strong Acid Resistance Metallurgical Equipment 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
Detailed Mechanical Properties of Various Grades of Stainless Steel Bars
|
Tensile Strength |
Yield Strength |
|
|
|
|
|
|
Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
Grain Size Req. |
Max. Hardness |
Modulus of Elasticity (x106 psi) |
304 |
S30400 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
304L |
S30403 |
A270 A312 |
70,000 |
485 |
70 |
25,000 |
170 |
25 |
35 |
- |
90 Rb |
28 |
304LN |
S30453 |
A249, A688 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
304H |
A30409 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
7 or coarser |
90 Rb |
28 |
The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. |
Grade |
Tensile Str |
Yield Str |
Elong |
Hardness |
(MPa) min |
0.2% Proof |
(% in 50mm) min |
|
(MPa) min |
|
Rockwell B (HR B) max |
Brinell (HB) max |
316 |
515 |
205 |
40 |
95 |
217 |
316L |
485 |
170 |
40 |
95 |
217 |
316H |
515 |
205 |
40 |
95 |
217 |
|
Tensile Strength |
Yield Strength |
|
|
|
Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
321 |
S32100 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
321H |
S32109 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
Grade |
Density |
Melting Point |
Tensile Strength |
Yield Strength (0.2%Offset) |
Elongation |
310S |
7.9 g/cm3 |
1402 °C (2555 °F) |
Psi - 75000 , MPa - 515 |
Psi - 30000 , MPa - 205 |
40% |
Grade |
Tensile Strength |
Yield Strength |
Elongation |
Hardness |
(MPa) min |
0.2% Proof |
(% in 50mm) min |
|
(MPa) min |
|
Rockwell C (HR C) |
Brinell (HB) |
UNS S31803 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
UNS S32205 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
Grade |
Property |
Value |
2507/
S32750 |
Density (g/cm3) |
7.8 |
0.2% Offset Yield Strength |
80 ksi |
Ultimate Tensile Strength |
116 ksi |
0.1% Offset Yield Strength 0.2% |
91 ksi |
Elongation in 2 inches, % |
15% |
Hardness Rockwell C |
32 |
Impact Energy |
74 ft.-lbs |
Density |
0.28 lb per inch3 |
Modulus of elasticity |
28 x 10(6) psi |
Coefficient of thermal expansion |
7.2 x 10(-6) per of at 68 to 212 of |
Thermal conductivity |
8.7 Btu/hr ftoF |
Heat capacity |
0.12 Btu/ lb oF |
Electrical resistivity |
31.5 x10(-6) ohm-inch |
For comprehensive information and expert advice on stainless steel rods, please reach out to Jiangsu Daxun Alloy Co., Ltd.
![904L Stainless Steel Bar ASTM B625 φ 65-140mm Strong Acid Resistance Metallurgical Equipment 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
![904L Stainless Steel Bar ASTM B625 φ 65-140mm Strong Acid Resistance Metallurgical Equipment 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)
![904L Stainless Steel Bar ASTM B625 φ 65-140mm Strong Acid Resistance Metallurgical Equipment 904L Stainless Steel Rod](//www.micstatic.com/athena/img/transparent.png)